Loofah complex oil absorb material

An oil-absorbing material and porous composite material technology, applied in the field of loofah composite oil-absorbing materials, can solve the problems of poor binding force and easy blockage of graphene oil-absorbing materials, and achieve the effect of high reuse effect, large pore structure, and high oil absorption.

Active Publication Date: 2019-06-07
ZHEJIANG UNIV OF TECH +1
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a practical and efficient loofah composite oil-absorbing material in order to solve the defects of poor binding force and easy clogging of current graphene oil-absorbing materials, which can absorb grease more quickly and efficiently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Loofah complex oil absorb material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] (1) slice the loofah, at 200 ℃, N 2 Carbonization under atmosphere for 4h to obtain carbonized loofah;

[0037] (2) Weigh 0.05g cetyltrimethylammonium bromide, add it to 100ml water and stir to mix, weigh 0.5g carbonized loofah, add carbonized loofah to the solution, stir at 80°C to change After curing for 2 hours, take out the loofah solid and wash it, dry the loofah solid at 100°C for 1 hour to obtain the modified loofah;

[0038] (3) Take 50mg of graphene and add it to 50ml of water, stir and mix for 10min under ultrasonic to obtain graphene suspension;

[0039] (4) Mix the graphene suspension with the modified loofah, put it in a hydrothermal reaction at 140°C for 10 hours to obtain a porous solid, and then dry the obtained porous solid at 90°C for 4 hours to obtain a loofah composite Oil absorbent material. The SEM photo of the loofah composite oil-absorbing material is shown in figure 1 .

Embodiment 2

[0041] (1) Slice the loofah, at 450°C, N 2 Carbonization under atmosphere for 2h to obtain carbonized loofah;

[0042] (2) Weigh 0.05g of cetyltrimethylammonium bromide, add it to 300ml of water and stir to mix, weigh 1g of carbonized loofah, add carbonized loofah into the solution, and stir at 100°C for modification 1.5h, take out the loofah solid and wash it, dry the loofah solid at 105°C for 2h to obtain the modified loofah;

[0043] (3) Take 300mg graphene and join in 75ml water, stir and mix 35min under ultrasonic, obtain graphene suspension;

[0044] (4) Mix the graphene suspension with the modified loofah, put it in a hydrothermal reaction at 160°C for 18 hours to obtain a porous solid, and then dry the obtained porous solid at 40°C for 48 hours to obtain a loofah composite Oil absorbent material.

Embodiment 3

[0046] (1) Slice the loofah and carbonize it under vacuum at 280°C for 6 hours to obtain carbonized loofah;

[0047] (2) Weigh 0.1g of cetyltrimethylammonium bromide, add it to 400ml of water and stir to mix, weigh 2g of carbonized loofah, add the carbonized loofah into the solution, stir and modify at 95°C 2.5h, take out the loofah solid and wash it, dry the loofah solid at 95°C for 1 hour to obtain the modified loofah;

[0048] (3) Take by weighing 330mg graphene and join in 105ml water, stir and mix 30min under ultrasonic, obtain graphene suspension;

[0049] (4) Mix the graphene suspension with the modified loofah and place it in a hydrothermal reaction at 180°C for 12 hours to obtain a porous solid, then dry the obtained porous solid at 50°C for 30 hours to obtain a loofah compound Oil absorbent material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a loofah complex oil absorb material. The preparation process is free from harmful and toxic pollutant and has the advantages of simple operation and high efficiency. Loofah is combined with grapheme, so as to obtain the complex oil absorb material with large pore structure and good air permeability, and can be reused for many times. The loofah complex oil absorb materialprepared by the invention has high oil absorbing property and reuse effect, and can be applied to marine oil pollution treatment and oil fume exhaust gas purification.

Description

technical field [0001] The invention relates to a loofah composite oil-absorbing material, which belongs to the technical field of preparation and application of environmental purification materials. Background technique [0002] The oil extraction and transportation process and the discharge of oily sewage from factories and cities are likely to cause oil pollution in water bodies and endanger the health of organisms, which has become a major environmental issue of concern to the world. [0003] In addition, cooking oil will be emitted into the air in the form of oil mist to form oil fume during cooking, and its harm should not be underestimated. Various toxic components in oil fume not only directly threaten human health, but also increase the content of urban fine particles and cause air pollution. Exacerbate the occurrence of smog weather. [0004] Therefore, a practical and efficient porous oil-absorbing material has been developed. In addition to its high oil-absorbin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/24B01J20/30B01D53/02B01D17/022
Inventor 孙青徐新建高绪元盛嘉伟赵有谱张俭楼向狄
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap