Preparation method of two-dimensional crystal Nb2CTx nano material
A nanomaterial, two-dimensional crystal technology, applied in nanotechnology, chemical instruments and methods, inorganic chemistry, etc., can solve the problems of high risk, difficult to store, strong irritation of hydrofluoric acid, etc. Gentle process, environmentally friendly results
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0021] Example 1:
[0022] Weigh 1gLiF into the corroded bottle, measure 10mL of 12mol / L hydrochloric acid, pour it into the corroded bottle, and add 1g of Nb 2 AlC raw material was slowly added to it. After the reaction stabilizes, it is placed under 50℃ and magnetically stirred for 72 hours. The product is washed repeatedly with deionized water and centrifuged until the PH value is greater than or equal to 5, ultrasonically dispersed for 1 hour, and 5mL~100mL of water is added to obtain a concentration of 1. ~30mg / mL Nb 2 CT x The solution is centrifuged and filtered to obtain a single layer of Nb 2 CT x Thin film material, take the bottom solid and dry to obtain the multilayer two-dimensional crystal Nb 2 C nanomaterials, measuring Nb in two-dimensional crystals 2 CT x The conductivity is 500~3000S / cm.
Example Embodiment
[0023] Example 2:
[0024] Weigh 0.99g LiF into the corroded bottle, measure 10mL of 9mol / L hydrochloric acid, pour it into the corroded bottle, and add 1g Nb 2 AlC raw material is slowly added to it. After the reaction is stable, it is placed under 50℃ and magnetically stirred for 72 hours. The product is repeatedly washed with deionized water and centrifuged until the pH value is greater than or equal to 5, ultrasonically dispersed for 1 hour, and 5mL~100mL of water is added to obtain a concentration of 0.1 ~30mg / mL Nb 2 CT x The solution is centrifuged and filtered to obtain a single layer of Nb 2 CT x Thin film material, take the bottom solid and dry to obtain the multilayer two-dimensional crystal Nb 2 CT x Nanomaterials, measuring Nb in two-dimensional crystals 2 CT x The conductivity is 2000~4000S / cm.
[0025] figure 1 Two-dimensional crystal Nb 2 CT x Nanomaterial aqueous solution and Tyndall phenomenon;
[0026] figure 2 For through the two-dimensional nano-layered crysta...
PUM
Property | Measurement | Unit |
---|---|---|
Conductivity | aaaaa | aaaaa |
Conductivity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap