Method for preparing composite quartz stone slab by using arsenic-containing waste residues and flotation tailings

A technology for flotation of tailings and quartz slate, which is used in the field of solidification and safe disposal of hazardous solid waste and artificial building materials. Good fire performance

Active Publication Date: 2019-06-07
BEIJING GEOENVIRON ENG & TECH
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the use of natural stone to prepare composite quartz slabs consumes a lot of stone, which is also one of the reasons for the high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment provides a method for preparing composite quartz slabs with arsenic-containing waste residue and flotation tailings, including the following steps:

[0047] (1) Select the flotation tailings of a certain molybdenum ore as the raw material, and the main element composition of the tailings is shown in Table 1-1:

[0048] Table 1-1 Element composition of flotation tailings of a certain molybdenum mine

[0049] element name

WO 3

SiO 2

al 2 o 3

CaO

MgO

Cu

P

Fe

content(%)

0.1

76.98

13.58

0.91

0.078

0.011

0.0038

0.55

[0050] Flotation desulfurization and iron removal are carried out on the above-mentioned tailings raw materials, and the iron content of the new tailings raw materials obtained is 0.27% (the raw materials do not contain sulfur, and the sulfur content has not been detected after pretreatment). The number of particles is 15-60 mesh; the tailings after desulfurization...

Embodiment 2

[0064] This embodiment provides a method for preparing composite quartz slabs with arsenic-containing waste residue and flotation tailings, including the following steps:

[0065] (1) Select the flotation tailings of a spodumene ore as raw material, and the main element composition of the tailings is shown in Table 1-4:

[0066] Table 1-4 Element composition of spodumene flotation tailings

[0067] element name

Li 2 o

f e2 o 3

S n

al 2 o 3

Nb 2 o 5

B e o

C a o

m g o

m n o

K 2 o

N a2 o

P 2 o 5

SiO 2

content(%)

0.12

1.12

0.02

14.31

0.011

0.006

0.54

0.11

0.06

0.10

0.67

0.05

71.76

[0068] Flotation desulfurization and iron removal are carried out on the above-mentioned tailings raw materials, and the iron content of the obtained new tailings raw materials is 0.34% (the raw materials do not contain sulfur, and the sulfur content has not be...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a composite quartz stone slab by using arsenic-containing waste residues and flotation tailings. The method is characterized in that the flotation tailings, the arsenic-containing waste residues, an unsaturated polyester, a coupling agent and a curing agent are used as raw materials, the materials are mixed, pressing is performed, solidification is performed, and therefore the composite quartz stone slab is prepared, wherein the flotation tailings are molybdenite flotation tailings or spodumene flotation tailings, the arsenic-containing waste residues are arsenic-containing waste residues obtained after flue dust treatment or arsenic-containing waste residues obtained after water treatment, and the amounts of the added raw materials are as follows: 26-55 parts by weight of the flotation tailings, 11-45 parts by weight of the arsenic-containing waste residues, 8-10 parts by weight of the unsaturated polyester, 0.001-0.0046 parts by weight of the coupling agent, and 0.001-0.005 part by weight of the curing agent. The method provided by the invention realizes solidification stabilization and recycling of arsenic in the preparation processof the composite quartz stone slab; and raw materials used in the method have a wide source and low price, the technical route is simple, leaching toxicity is qualified, and the method is convenientfor industrial implementation.

Description

technical field [0001] The invention relates to the technical field of solidification and safety treatment of hazardous solid waste and the technical field of artificial building materials. Arsenic solidification and recycling. Background technique [0002] In the non-ferrous metal smelting process, arsenic is an unavoidable major pollutant, mainly because most non-ferrous metal minerals exist in the form of sulfide, and arsenic is mainly associated or symbiotic in the form of sulfide. During the smelting process, arsenic is mainly opened from the system in the form of smoke and dust, and the process of treating arsenic-containing smoke and dust will produce a large amount of arsenic-containing precipitates and tailings. In addition, these arsenic-containing tailings generally also contain heavy metal ions such as copper, lead, chromium, and mercury, which are hazardous solid wastes and must be properly disposed of in strict accordance with hazardous waste treatment and dis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18C04B111/54
Inventor 刘文莉熊辉刘力奇甄胜利孙伟韩海生马强贺真常晓然董旭龙
Owner BEIJING GEOENVIRON ENG & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap