Bacteriostasis nylon sock and preparation method thereof

A nylon and modified technology, which is applied in the manufacture of rayon, single-component polyamide rayon, fiber chemical characteristics, etc., can solve the problems of endangering human health, growing many bacteria, and easy to breed bacteria, etc., to improve mechanical properties Intensity, improved antibacterial performance, and good synergistic antibacterial effect

Inactive Publication Date: 2019-06-11
安徽倍发来纺织科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, most of the socks that people wear have not been treated with antibacterial, and a lot of bacteria will grow when worn for a long time, especially for people who are prone to sweating, which will not only cause a lot of inconvenience to people's lives, but also endanger human health. At present, many companies will post-process socks, such as microwave sterilization, etc., but these have not solved the antibacterial problem from the source of the material, and bacteria are still easy to breed after wearing for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bacteriostasis nylon sock and preparation method thereof
  • Bacteriostasis nylon sock and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of antibacterial nylon socks, it is made up of the raw material of following weight portion:

[0026] Cotton fiber 10, modified monomer solution 150, initiator 4, trimethylhydroxyethylethylenediamine 2, octylisothiazolinone 1, calcium propionate 2, beeswax 3, dithiosalicylic acid 4, Pentaerythritol3.

[0027] Described initiator is dicumyl peroxide.

[0028] Described modified monomer solution is made up of the raw material of following parts by weight:

[0029] Caprolactam 80, hydroxyethyl cellulose 10, diatomaceous earth 10, benzyltriphenylphosphine chloride 2, polyvinylpyrrolidone 1, fatty acid polyethylene glycol ester 0.3, saturated octadecylamide 0.7.

[0030] The preparation method of described modified monomer solution, comprises the following steps:

[0031] (1) Take diatomite, calcinate at 650°C for 1 hour, cool to room temperature, grind into fine powder, blend with benzyltriphenylphosphine chloride, and add to thionyl chloride 0.8 times the weight ...

Embodiment 2

[0049] A kind of antibacterial nylon socks, it is made up of the raw material of following weight portion:

[0050] Cotton fiber 17, modified monomer solution 180, initiator 7, trimethylhydroxyethylethylenediamine 3, octylisothiazolinone 2, calcium propionate 4, beeswax 5, dithiosalicylic acid 6, Pentaerythritol 5.

[0051] Described initiator is dicumyl peroxide.

[0052] Described modified monomer solution is made up of the raw material of following parts by weight:

[0053] Caprolactam 100, hydroxyethyl cellulose 12, diatomaceous earth 14, benzyltriphenylphosphine chloride 3, polyvinylpyrrolidone 2, fatty acid polyethylene glycol ester 0.4, saturated octadecylamide 1.

[0054] The preparation method of described modified monomer solution, comprises the following steps:

[0055] (1) Take diatomite, calcinate at 700°C for 2 hours, cool to room temperature, grind into fine powder, blend with benzyltriphenylphosphine chloride, and add to thionyl chloride whose weight is 1 ti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bacteriostasis nylon sock. The sock is prepared from, by weight, 10-17 parts of cotton fiber, 150-180 parts of a modified monomer solution, 4-7 parts of an initiator, 2-3 parts of Dabco T, 1-2 parts of OIT, 2-4 parts of calcium propionate, 3-5 parts of beewax, 4-6 parts of dithio-salicylic acid and 3-5 parts of pentaerythritol. The beewax is subjected to surface esterification treatment, the bonding strength of beewax between matrixes is improved, and therefore the finished product stability is further improved. By adding OIT, calcium propionate and the like, the goodcooperative bacteriostasis effect can be achieved, and the quality of the finished sock is improved.

Description

technical field [0001] The invention belongs to the field of daily necessities, and in particular relates to a bacteriostatic nylon stocking and a preparation method thereof. Background technique [0002] At present, most of the socks that people wear have not been treated with antibacterial, and a lot of bacteria will grow when worn for a long time, especially for people who are prone to sweating, which will not only cause a lot of inconvenience to people's lives, but also endanger human health. At present, many companies will post-process socks, such as microwave sterilization, etc., but these have not solved the antibacterial problem from the source of the material, and bacteria are still easy to breed after wearing for a long time. Contents of the invention [0003] The purpose of the present invention is to provide a kind of antibacterial nylon socks and preparation method thereof. [0004] To achieve the above object, the present invention adopts the following techn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/90D01F1/10C08G69/14C08G69/16
Inventor 王安丽
Owner 安徽倍发来纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More