Preparation method of high-purity transparent crystal fused magnesia

A technology of transparent crystals and fused magnesia, which is applied in the field of fused magnesia, can solve problems such as the difficulty in removing impurities or reducing the content, the inability to produce pure fused magnesia, and the impossibility of producing transparent crystals. Excellent erosion performance, large crystal grains, and compact structure

Active Publication Date: 2019-06-14
HENAN TENAI SPECIAL REFRACTORIES CO LTD +2
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are many kinds of processes and raw materials in the field of fused magnesia production. At present, the main raw material used is magnesite. Although its magnesium content is high, the existing production process cannot produce fused magnesia with high purity. Sand, due to the high content of SiO2, Fe2O3, and CaO in magnesite, it is very difficult to remove or reduce the content of these impurities
The flotation method currently used can only remove part of the impurities, so it is difficult to achieve a content of more than 99% of magnesium oxide with the existing technology. Due to the existence of impurities, it is impossible to produce transparent crystals.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-purity transparent crystal fused magnesia
  • Preparation method of high-purity transparent crystal fused magnesia
  • Preparation method of high-purity transparent crystal fused magnesia

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0014] The preparation method of high-purity transparent crystal fused magnesia of the present invention, the steps of described preparation method are as follows:

[0015] 1) Using salt lake bischofite as the initial raw material, magnesium hydroxide (MgCl 2 +Ca(OH) 2 →Mg(OH) 2 +CaCl 2 ), then lightly burn to generate lightly burned magnesia, the lightly burned temperature is 900°C and heat preservation for 1 hour, and the lightly burned magnesia is presse...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of high-purity transparent crystal fused magnesia. According to the preparation method, salt lake water chloromagnesite is adopted as a raw material, magnesium chloride generates magnesium hydrate sediments through an ammonia-lime method, magnesium hydrate is separated from a solution, and then the high-purity magnesium hydrate is slightly roasted to become slightly roasted magnesium oxide; the slightly roasted magnesium oxide is pressed into spheres to serve as raw materials, the spheres are smelted through an electric-arc furnace of 5000 KVA, andfusion is carried out through a high-voltage and high-current operation method; and at the later period of fusion, refining operation needs to be carried out, the temperature of fused liquid is increased to reach 3000 DEG C or above, after melting is completed, a molten lump has to be cooled slowly, and a high-purity transparent crystal fused magnesia clinker is obtained, wherein MgO is larger than or equal to 99%, SiO2 is smaller than or equal to 0.1%, Fe2O3 is smaller than or equal to 0.1%, and CaO is smaller than or equal to 0.1%.

Description

technical field [0001] The invention belongs to the field of electric fused magnesia, in particular to a preparation method of high-purity transparent crystal electric fused magnesia. Background technique [0002] At present, there are many kinds of processes and raw materials in the field of fused magnesia production. At present, the main raw material used is magnesite. Although its magnesium content is high, the existing production process cannot produce fused magnesia with high purity. Sand, due to the high content of SiO2, Fe2O3, and CaO in magnesite, it is very difficult to remove or reduce the content of these impurities. The flotation method currently used can only remove a part of impurities, so it is difficult to achieve a content of more than 99% of magnesium oxide by using the existing technology. Due to the existence of impurities, it is impossible to produce transparent crystals. Contents of the invention [0003] The object of the present invention is to pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B2/10C04B35/04
Inventor 代永信张永晨
Owner HENAN TENAI SPECIAL REFRACTORIES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products