A kind of high-temperature-resistant water-based drilling fluid cutting agent and preparation method thereof

A technology of water-based drilling fluid and high temperature resistance, which is applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problems of excessive viscosity increasing effect and low temperature resistance, and increase the probability of effective interaction, Low apparent viscosity, good cutting effect

Active Publication Date: 2021-08-17
CHINA PETROLEUM & CHEM CORP +1
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problems of excessive viscosity increasing effect and low temperature resistance (<150°C) in the existing water-based drilling fluid cutting agent products, the present invention proposes a high-temperature resistant water-based drilling fluid cutting agent, specifically The invention relates to a high temperature resistant water-based drilling fluid cutting agent and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-temperature-resistant water-based drilling fluid cutting agent and preparation method thereof
  • A kind of high-temperature-resistant water-based drilling fluid cutting agent and preparation method thereof
  • A kind of high-temperature-resistant water-based drilling fluid cutting agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] Add 800 parts of deionized water to the reaction kettle equipped with stirrer, temperature controller, air duct and reflux condenser, add 110 parts of acrylamide (monomer A), 30 parts of N-vinylpyrrolidone (monomer B), 30 parts of C18PEGMA macromer, produced by Evonik Industrial Group (monomer D) and 30 parts of methacryloyloxyethyltrimethylammonium chloride (monomer C), stirred with 30% hydrogen The sodium oxide solution adjusted the pH value of the monomer solution to 9, and finally added 2 parts of pentaerythritol and stirred until the pentaerythritol was completely dissolved.

[0050] Start the temperature control device, control the temperature of the monomer solution to 50°C, and at the same time, pass nitrogen gas under stirring for 40 minutes, then add 7 parts of ammonium persulfate, and react for 5 hours. After the reaction is finished, cool to room temperature, discharge, cut, dry, and pulverize, and the obtained powder product is the temperature-resistant wat...

Embodiment 2

[0052] Add 800 parts of deionized water to the reaction kettle equipped with stirrer, temperature controller, air duct and reflux condenser, add 110 parts of acrylamide (monomer A), 30 parts of N-vinylpyrrolidone (monomer B), 30 parts of C18PEGMA macromer (monomer D) and 30 parts of methacryloxyethyltrimethylammonium chloride (monomer C), after stirring evenly, adjust the monomer with 30% sodium hydroxide solution The pH value of the solution was 9, and finally 2 parts of dipentaerythritol was added and stirred until the dipentaerythritol was completely dissolved.

[0053] Start the temperature control device, control the temperature of the monomer solution to 50°C, at the same time, pass nitrogen gas under stirring for 40 minutes, then add 8 parts of ammonium persulfate, and react for 5 hours. After the reaction is finished, cool to room temperature, discharge, cut, dry, and pulverize, and the obtained powder product is the temperature-resistant water-based drilling fluid cut...

Embodiment 3

[0055] Add 800 parts of deionized water to the reaction kettle equipped with stirrer, temperature controller, air duct and reflux condenser, add 160 parts of acrylamide (monomer A), 20 parts of N-vinylpyrrolidone (monomer B), 10 parts of C18PEGMA macromer (monomer D) and 10 parts of methacryloyloxyethyltrimethylammonium chloride (monomer C), after stirring evenly, adjust the monomer with 30% sodium hydroxide solution The pH value of the solution was 9, and finally 2 parts of pentaerythritol was added and stirred until the pentaerythritol was completely dissolved.

[0056] Start the temperature control device, control the temperature of the monomer solution to 50°C, and at the same time, pass nitrogen gas under stirring for 40 minutes, then add 7 parts of ammonium persulfate, and react for 5 hours. After the reaction is finished, cool to room temperature, discharge, cut, dry, and pulverize, and the obtained powder product is the temperature-resistant water-based drilling fluid ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-temperature-resistant water-based drilling fluid cutting agent and a preparation method thereof in the field of petroleum drilling working fluids. The high-temperature-resistant water-based drilling fluid shear lifting agent comprises the following components copolymerized by weight percentage: (1) 40% to 80% of monomer A; (2) 10% to 20% of monomer B; (3) 5% to 20% of monomer C; (4) 5% to 20% of monomer D; said monomer A is selected from acrylamide, N,N-dimethylacrylamide, isobutyl At least one of methacrylamide and acrylonitrile; the monomer B is selected from N-vinylpyrrolidone; the monomer C is selected from methacryloyloxyethyltrimethylammonium chloride, dimethyl diene At least one of propyl ammonium chloride; the monomer D is selected from the amphiphilic macromonomer C18PEGMA; the high temperature resistant water-based drilling fluid cutting agent of the present invention has good cutting performance and temperature resistance, The temperature resistance can reach 150°C, and it can be used as a shear-lifting agent for oil drilling working fluid, improving the suspension stability of the working fluid to the lightening agent or weighting agent, and enhancing the system's rock-carrying ability and wellbore purification ability.

Description

technical field [0001] The invention relates to the field of petroleum drilling working fluids, and more particularly relates to a high-temperature-resistant water-based drilling fluid cutting agent and a preparation method thereof. Background technique [0002] Cutting agent is a core treatment agent for drilling fluid. Its main function is to increase the shear force of the drilling fluid system, enhance the cuttings carrying capacity of the drilling fluid, and improve the wellbore purification effect of the drilling fluid. In addition, in low-density or high-density drilling fluids, it is often necessary to add solid-phase materials such as hollow microbead lightening agents or barite weighting agents. Due to the density difference between the solid-phase materials and the drilling fluid, in order to prevent the lightening agent from floating or For the weighting agent to settle, it is necessary to increase the shear force of the drilling fluid to enhance the suspension p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/035C08F283/06C08F220/56C08F220/54C08F220/48C08F226/10C08F220/34C08F226/04C08F2/10C08F4/40
CPCC08F2/10C08F4/40C08F283/065C09K8/035C08F220/56C08F220/54C08F220/48C08F226/10C08F220/34C08F226/04
Inventor 赵素丽杨小华林永学陈铖杨帆
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com