Method for preparing Al/CuO nano energetic material based on alkaline catalysis sol-gel method

A sol-gel method and alkaline technology, which can be used in offensive equipment, explosives processing equipment, explosives, etc., can solve the problems of unfavorable mixing of nano-Al particles and CuO, difficulty in Al dispersion, etc., and achieve the effect of avoiding settlement and solving poor dispersion

Inactive Publication Date: 2019-07-19
ZHONGBEI UNIV
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the typical scheme for the preparation of Al / CuO nanocomposite energetic material systems based on sol-gel is the reaction route of copper chloride and propylene oxide, but in practice, it is found that this route is difficult to disperse Al, which is not conducive to nano-Al particles Mixing with CuO

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Weigh 0.8g of sodium dodecylsulfonate, 2.4g of urea and 5ml of deionized water, put them in a three-necked bottle, stir in a constant temperature water bath at 50°C at 350r / s for 1h, measure the pH between 7-8 Weakly alkaline;

[0022] 720mg Cu(NO 3 ) 2 ·3H 2 O was dispersed in 3ml of absolute ethanol, placed in an ultrasonic water bath for 30 minutes, and then added dropwise to the above-mentioned three-neck flask; then 5ml of propylene oxide was added dropwise, and stirred at 260r / s for 20min;

[0023] Take 40mg of nano-aluminum powder (nAl) and disperse it in 3ml of absolute ethanol, seal it, place it in an ultrasonic water bath for 10 minutes, and then drop it into the above-mentioned three-necked bottle; stir for 1 hour, take it out and seal it, and put it in the refrigerator for 5 minutes to obtain wet gel.

[0024] After the obtained wet gel was left to stand in the refrigerator for 2-3 days, the gel was placed in a vacuum freeze dryer for freeze-drying to ob...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing an Al / CuO nano energetic material based on an alkaline catalysis sol-gel method. According to the method, the Al / CuO nano energetic material is preparedby adopting a sol-gel method in a weakly alkaline environment and by taking urea as an alkaline catalyst and sodium dodecyl sulfate as a surfactant, wherein the pH value of the weakly alkaline environment is 7-9. The problem that the gel condition of an Al / CuO system is difficult to control is solved, the gel time is shortened, sedimentation of nAl in CuO gel is avoided, and the problem that the nanometer energetic material is prone to sedimentation and poor in dispersity after mixing is solved.

Description

technical field [0001] The invention relates to the field of composite energetic materials, in particular to a method for preparing Al / CuO nanometer energetic materials based on an alkaline catalytic sol-gel method. Background technique [0002] Energetic materials refer to single-substance compounds or mixtures that contain explosive groups or are composed of oxidizers and combustion agents, and can independently undergo chemical reactions, burn or explode, and output energy. Among them, composite energetic materials are the most diverse and powerful, and have been extensively studied. The composite system composed of nAl / CuO is an important class of nanocomposite energetic materials. Its theoretical enthalpy density is 4.07kJ / g, which is higher than other systems. Therefore, it is one of the general energetic aluminothermic systems. Therefore, there are currently many Researchers have invested in the development of nano-Al / CuO system nano-composite energetic material form...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C06B33/00C06B21/00
CPCC06B21/00C06B33/00
Inventor 陈晓勇王新新熊继军梁庭贾平岗洪应平雷程刘文怡李晨张泽宇王佳乐
Owner ZHONGBEI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap