Preparation method of coating paper

A modification and weight technology, applied in special paper, paper, papermaking, etc., can solve problems such as abnormal pressing of decorative paper and wear-resistant paper, and achieve the effect of solving abnormal pressing problems and saving forest resources.

Inactive Publication Date: 2019-07-23
HUBEI HONGLIAN IND
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Aiming at the deficiencies of the prior art, the present invention provides a method for preparing sprayed paper, which can prepare a sprayed paper with both decorative effects and wear-resistant effects, and solves the problem of abnormal pressing of decorative paper and wear-resistant paper produced by different manufacturers , and save forest resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of coating paper

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] In order to achieve the above object, the invention provides a kind of preparation method of spray paper, it is characterized in that, comprises the following steps:

[0021] (1) Immerse the base paper in the impregnating glue, then roll it with a roller, and then place it in an oven to dry, wherein, the impregnating glue contains 43-45% by weight of modified urea-formaldehyde resin, 0.2-0.3% by weight of permeated agent, 0.1-2% by weight of curing agent and 53-56% by weight of water;

[0022] (2) Spray the spray glue onto the upper surface of the paper obtained in step (1) by spraying equipment, then level it with a leveling roller, and then place it in an oven to dry, wherein the spray glue contains modified melamine formaldehyde resin , modified urea-formaldehyde resin, penetrating agent, suspending agent, defoamer, curing agent, aluminum oxide and water, wherein the weight ratio of modified melamine-formaldehyde resin to modified urea-formaldehyde resin is 1.3-1.6:1...

Embodiment 1

[0046] The base paper is immersed in the impregnation glue that contains 45% by weight of polyvinyl alcohol modified urea-formaldehyde resin, 0.2% by weight of penetrating agent, 0.1% by weight of curing agent and 54.7% by weight of water, then rolled with a roller, and then placed Dry in 6 ovens for 8 minutes, the temperature of each oven is 125°C, 125°C, 125°C, 120°C, 120°C, 120°C respectively.

[0047] The triethanolamine modified melamine formaldehyde resin containing 30% by weight, the polyvinyl alcohol modified urea-formaldehyde resin of 20% by weight, the penetrating agent of 0.3% by weight, the suspending agent of 0.1% by weight, the defoamer of 0.005% by weight by spraying equipment , 0.1% by weight of curing agent, 12% by weight of Al2O3 and 41.495% by weight of water sprayed on the upper surface of the paper impregnated in the dipping glue, then flattened with a leveling roller, and then placed Dry in 6 ovens for 5 minutes, the temperature of each oven is 145°C, 140...

Embodiment 2

[0051] The base paper is immersed in the impregnating glue that contains 44% by weight of polyvinyl alcohol modified urea-formaldehyde resin, 0.3% by weight of penetrant, 1% by weight of curing agent and 54.7% by weight of water, then rolled with a roller, and then placed Dry in 5 ovens for 8.5 minutes, the temperature of each oven is 135°C, 130°C, 135°C, 130°C, 130°C respectively.

[0052] The triethanolamine modified melamine formaldehyde resin containing 30% by weight, the polyvinyl alcohol modified urea-formaldehyde resin of 20% by weight, the penetrating agent of 1% by weight, the suspending agent of 1% by weight, the defoamer of 0.01% by weight by spraying equipment , 1% by weight of curing agent, 10% by weight of aluminum oxide and 36.99% by weight of water spray glue on the upper surface of the paper impregnated in the obtained dipping glue, followed by leveling with a leveling roller, and then placed Dry in 5 ovens for 4.5 minutes, the temperature of each oven is 145°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of coating paper preparation, in particular to a preparation method of coating paper. The method comprises following steps: (1), base paper is soaked in an impregnating adhesive containing modified urea-formaldehyde resin, a penetrating agent, a curing agent and water, rolled by a roller and dried in a drying oven; (2), a spraying adhesive containing modified melamino-formaldehyde resin, the modified urea-formaldehyde resin, the penetrating agent, a suspending agent, a defoaming agent, the curing agent, aluminium oxide and water is sprayed to the upper surface of the paper obtained in step (1) by spraying equipment, and then the paper is leveled by a leveling roller and dried in the drying oven; (3), the front and back surfaces of the paper obtained in step (2) are coated with a mesh coating adhesive containing the modified melamino-formaldehyde resin, a mold release agent, a dedusting agent, the curing agent and water by a round roller with a grid structure, and then the paper is dried in the drying oven. According to the method, the coating paper with both wear-resistant effect and decorative effect can be prepared, and forest resources are saved.

Description

technical field [0001] The invention relates to the field of spray-coated paper manufacture, in particular to a preparation method of spray-coated paper. Background technique [0002] With the heating up of the real estate industry, people's requirements for living environment and working environment are constantly improving, and people pay more and more attention to the quality of house decoration. As an important part of the overall decoration of the house, the decoration of the floor will inevitably receive great attention from the relevant market. [0003] In the floor production process, in order to make the floor look more beautiful, a layer of decorative paper is usually covered on the surface of the floor; at the same time, in order to enhance the wear resistance of the floor and prolong the service life of the floor, it is also necessary to cover a layer of durable paper on the surface of the floor. grinding paper. [0004] In order to make the floor look beautifu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/00D21H23/50D21H23/56D21H25/06
CPCD21H23/50D21H23/56D21H25/06D21H27/00
Inventor 罗爱军李红明
Owner HUBEI HONGLIAN IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com