A kind of ultrafine-grain high-strength toughness high-entropy alloy containing rare earth GD and preparation method thereof

A high-entropy alloy and ultra-fine grain technology is applied in the field of high-entropy alloys to achieve the effects of low forming temperature, convenient operation and no dendrite segregation.

Inactive Publication Date: 2021-07-20
SOUTH CHINA UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The present invention adopts the powder metallurgy method (MA+SPS), and on the basis of the existing CoCrFeMnNi high-entropy alloy system, a small amount of rare earth element Gd is added to achieve the purpose of regulating the structure and improving the strength. So far, there is no relevant literature report

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultrafine-grain high-strength toughness high-entropy alloy containing rare earth GD and preparation method thereof
  • A kind of ultrafine-grain high-strength toughness high-entropy alloy containing rare earth GD and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A preparation method of an ultra-fine-grained high-strength toughness high-entropy alloy containing rare earth Gd, which adopts the method of combining mechanical alloying and spark plasma sintering technology, and includes the following steps and process conditions:

[0038] Step 1: Mix the powder

[0039] According to the atomic ratio of Co 19.8%, Cr 19.8%, Fe 19.8%, Mn 19.8%, Ni 19.8%, Gd1%, weigh the elemental powder, and then dry mix it in a powder mixer for 12-24 hours until uniform, and the powder purity is high at 99.5%;

[0040] Step 2: Prepare alloy powder by mechanical alloying method

[0041]Put the uniformly mixed powder into a ball milling tank, and then perform ball milling on a planetary high-energy ball mill until the alloy powder with a single-phase FCC structure is obtained; the material of the tank body and the balls are made of stainless steel, and the tank is vacuumed and filled with High-purity argon (99.99%) was used as a protective atmosphere;...

Embodiment 2

[0053] A preparation method of an ultra-fine-grained high-strength toughness high-entropy alloy containing rare earth Gd, which adopts the method of combining mechanical alloying and spark plasma sintering technology, and includes the following steps and process conditions:

[0054] Step 1: Mix the powder

[0055] According to the atomic ratio of Co 19.6%, Cr 19.6%, Fe 19.6%, Mn 19.6%, Ni 19.6%, Gd2%, weigh the elemental powder, and then dry mix it in a powder mixer for 12-24 hours until uniform, and the powder purity is high at 99.5%;

[0056] Step 2: Prepare alloy powder by mechanical alloying method

[0057] Put the uniformly mixed powder into a ball milling tank, and then perform ball milling on a planetary high-energy ball mill until the alloy powder with a single-phase FCC structure is obtained; the material of the tank body and the balls are made of stainless steel, and the tank is vacuumed and filled with High-purity argon (99.99%) was used as the protective atmosphe...

Embodiment 3

[0069] A preparation method of an ultra-fine-grained high-strength toughness high-entropy alloy containing rare earth Gd, which adopts the method of combining mechanical alloying and spark plasma sintering technology, and includes the following steps and process conditions:

[0070] Step 1: Mix the powder

[0071] According to the atomic ratio of Co 19.4%, Cr 19.4%, Fe 19.4%, Mn 19.4%, Ni 19.4%, Gd3%, weigh the elemental powder, and then dry mix it in a powder mixer for 12-24 hours until uniform, and the powder purity is high at 99.5%;

[0072] Step 2: Prepare alloy powder by mechanical alloying method

[0073] Put the uniformly mixed powder into a ball milling tank, and then perform ball milling on a planetary high-energy ball mill until the alloy powder with a single-phase FCC structure is obtained; the material of the tank body and the balls are made of stainless steel, and the tank is vacuumed and filled with High-purity argon (99.99%) was used as the protective atmosphe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
tensile yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of high-entropy alloys, and discloses an ultrafine-grained high-strength and tough CoCrFeMnNiGd containing rare earth Gd x High-entropy alloys and methods for their preparation. The atomic percentage content of each element of the high-entropy alloy of the present invention is Co 18%-20%, Cr 18%-20%, Fe 19%-22%, Mn 19%-22%, Ni 18%-22%, Gd 1 %‑3%. The present invention also provides a preparation method of the above-mentioned high-entropy alloy, which adopts the combination of mechanical alloying and discharge plasma sintering. The present invention controls the adverse effects of impurity oxygen introduced in the preparation process by doping the rare earth element Gd, precipitates the strengthening phase, and combines the powder metallurgy preparation process to refine the grains, so that the high-entropy alloy has very excellent comprehensive mechanical properties , the best compressive yield strength at room temperature reaches 1621MPa, the plastic strain is 35.4%, and the maximum compressive strength is 2685MPa.

Description

technical field [0001] The invention belongs to the technical field of high-entropy alloys, in particular to an ultra-fine-grained high-strength CoCrFeMnNiGd containing rare earth Gd x High-entropy alloys and methods for their preparation. Background technique [0002] As a new type of structural and functional materials, high-entropy alloys have attracted a lot of attention since they were proposed. Because of its unique design concept, the high-entropy alloy has a special structure and excellent performance. High-entropy alloys can generally be defined as five or more elements that are alloyed according to an equiatomic ratio or close to an equiatomic ratio, and tend to form a single-phase solid solution alloy. However, the current research on high-entropy alloys is not limited to this, and there are no strict requirements for element types and atomic ratios. Because of the special structure, high-entropy alloys often exhibit excellent properties different from traditio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C30/00C22C1/04B22F9/04B22F3/105
CPCB22F3/105B22F9/04B22F2009/043C22C1/04C22C30/00
Inventor 龙雁张伟华彭亮李贵琦彭海燕
Owner SOUTH CHINA UNIV OF TECH