A kind of graphene-silicon composite material and its preparation method, electrode material and battery

A technology of silicon composite materials and graphene-like materials, applied in negative electrodes, battery electrodes, secondary batteries, etc., can solve the problems of reduced cycle performance, electrode structure collapse, mechanical pulverization, etc., to improve structural stability, combined with Tight and uniform, uniform distribution of silicon carbon

Active Publication Date: 2021-03-12
内蒙古信敏惠纳米科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the charging and discharging process of lithium-ion batteries, repeated lithium ion intercalation will cause a huge volume expansion of silicon-based materials, and the volume expansion rate can even reach 300%, which will easily lead to the destruction of the structure of silicon-based materials and mechanical pulverization. Lead to the collapse of the electrode structure and peeling off of the electrode material, seriously reducing its cycle performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene-silicon composite material and its preparation method, electrode material and battery
  • A kind of graphene-silicon composite material and its preparation method, electrode material and battery
  • A kind of graphene-silicon composite material and its preparation method, electrode material and battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Such as figure 1 and figure 2 Shown, the embodiment of the present invention provides a kind of preparation method of graphene-silicon composite material, the preparation method of this graphene-silicon composite material comprises:

[0040] Step S200: Mix the positively charged silicon-based material dispersion and the negatively charged graphene-based material dispersion, so that the positively charged silicon-based material dispersion contains the positively charged silicon-based material and the negatively charged silicon-based material. The negatively charged graphene-like material contained in the charged graphene-like material dispersion is assembled together under electrostatic action to obtain a graphene-silicon self-assembled material dispersion; optionally, the negatively charged graphene-like material dispersion Added to the dispersion of positively charged silicon materials, so that the two are mixed together; in this process, the dispersion of negatively...

Embodiment 2

[0074] An embodiment of the present invention provides a graphene-silicon composite material, which is prepared by the above-mentioned preparation method of the graphene-silicon composite material. It is found through experiments that the resistivity of the graphene-silicon composite material is 10Ω·cm-20mΩ·cm, and has relatively high conductivity.

[0075] Compared with the prior art, the beneficial effect of the graphene-silicon composite material provided by the embodiment of the present invention is the same as the beneficial effect of the above-mentioned preparation method of the graphene-silicon composite material, which will not be repeated here.

[0076]In some practicable ways, considering that there are relatively few amination reagents reacting with nano-silicon and organic carboxylation reagents reacting with graphene, after the graphene-silicon self-assembled material is sintered in an inert environment, the obtained graphene - The mass percentage of the silicon-b...

Embodiment 3

[0078] An embodiment of the present invention provides an electrode material, which includes the above-mentioned graphene-silicon composite material.

[0079] Compared with the prior art, the beneficial effect of the electrode material provided by the embodiment of the present invention is the same as that of the above-mentioned method for preparing the graphene-silicon composite material, and will not be repeated here.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene-silicon composite material, a preparation method thereof, an electrode material and a battery, and relates to the technical field of batteries to improve the structural stability of an electrode containing a silicon-based material, thereby ensuring the cycle performance of the battery. The preparation method of the graphene-silicon composite material comprises: mixing a positively charged silicon-based material dispersion with a negatively charged graphene-based material dispersion, so that the positively charged silicon-based material and the negatively charged The graphene-like materials are assembled together under electrostatic action to obtain a graphene-silicon self-assembly material dispersion; the graphene-silicon self-assembly material dispersion is dried by spray drying to obtain a graphene-silicon self-assembly material; The graphene-silicon self-assembled material is sintered in an inert environment to obtain a graphene-silicon composite material. The graphene-silicon composite material is prepared by the above-mentioned preparation method. The graphene-silicon composite material provided by the invention is used in batteries.

Description

technical field [0001] The invention relates to the technical field of batteries, in particular to a graphene-silicon composite material, a preparation method thereof, an electrode material and a battery. Background technique [0002] In recent years, with the rapid development of new energy vehicles and portable electronic products, lithium-ion batteries have received more extensive attention and more in-depth research. Anode materials are an important part of lithium-ion batteries, which directly affect key indicators such as energy density, cycle life, and safety performance of batteries. [0003] Silicon-based material is a negative electrode material with ultra-high specific capacity (theoretical capacity 4200mAh / g), which is more than ten times the capacity of traditional carbon-based materials, and the discharge platform is equivalent to it. Therefore, silicon-based materials are regarded as the next generation The preferred anode material for lithium-ion batteries. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/38H01M4/583H01M4/62H01M10/0525B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00H01M4/386H01M4/583H01M4/625H01M10/0525H01M2004/027Y02E60/10
Inventor 郝胐王文阁闫晓荣袁伟李金来
Owner 内蒙古信敏惠纳米科技有限公司