A production method and technology of copper wire, applied in the field of electric wire, can solve the problems of high production cost of high-purity copper wire, unable to meet market demand, increase production cost, etc., and achieve the effect of avoiding processing damage, improving elongation performance, and avoiding fracture

Inactive Publication Date: 2019-08-16
惠州市秋叶原铜业发展有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the current production cost of high-purity copper wire is high, especially the qualified rate of copper wire products with small diameter is low, which cannot meet the current market demand
In addition, the ductility of copper is worse than that of gold, and the method of doping gold is generally used to improve the ductility, which undoubtedly increases the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A kind of production method of making copper wire, concrete steps are as follows:

[0026] (1) Using the electrolytic copper plate without delamination defects as the raw material, cut it into copper strips, then process it into copper rods with circular cross-sections, and then make them into round copper wires for later use;

[0027] (2) Preparation of wire drawing protection solution: Dissolve polyethylene glycol 400 in absolute ethanol, then add polyvinyl butyral, stir well until completely dissolved to obtain the first solution; heat perfluoropolyether to 70 ℃, add the first solution and polydimethylsiloxane, and ultrasonically vibrate for 20 minutes to obtain;

[0028] (3) Polish the round copper wire obtained in step (1), phosphating the coating, and then immerse it in the drawing protection solution obtained in step (2), ultrasonically oscillate for 2 hours, take it out, and then heat it up and then cool it down. Finally, the copper wire is obtained by stretchi...

Embodiment 2

[0037] A kind of production method of making copper wire, concrete steps are as follows:

[0038] (1) Using the electrolytic copper plate without delamination defects as the raw material, cut it into copper strips, then process it into copper rods with circular cross-sections, and then make them into round copper wires for later use;

[0039] (2) Preparation of wire drawing protection solution: Dissolve polyethylene glycol 400 in absolute ethanol, then add polyvinyl butyral, stir well until completely dissolved to obtain the first solution; heat perfluoropolyether to 80 ℃, add the first solution and polydimethylsiloxane, and ultrasonically oscillate for 30 minutes to obtain;

[0040] (3) Polishing the round copper wire obtained in step (1), phosphating the coating, and then immersing it in the wire drawing protection solution obtained in step (2), ultrasonically oscillating for 3 hours, taking it out and performing heat treatment after heating up and then cooling down, Finall...

Embodiment 3

[0049] A kind of production method of making copper wire, concrete steps are as follows:

[0050] (1) Using the electrolytic copper plate without delamination defects as the raw material, cut it into copper strips, then process it into copper rods with circular cross-sections, and then make them into round copper wires for later use;

[0051] (2) Preparation of wire drawing protection solution: Dissolve polyethylene glycol 400 in absolute ethanol, then add polyvinyl butyral, stir well until completely dissolved to obtain the first solution; heat perfluoropolyether to 70 ℃, add the first solution and polydimethylsiloxane, and ultrasonically oscillate for 30 minutes to obtain;

[0052] (3) Polish the round copper wire obtained in step (1), phosphating the coating, and then immerse it in the drawing protection solution obtained in step (2), ultrasonically oscillate for 2 hours, take it out, and then heat it up and then cool it down. Finally, the copper wire is obtained by stretc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Resistivityaaaaaaaaaa
Login to view more

Abstract

The invention provides a production method for manufacturing a copper wire. The production method comprises the steps that an electrolytic copper plate without layering defects is taken as a raw material, slit into copper strips, and then machined into cooper rods; then a wire rod copper wire material is manufactured, polishing is conducted, a coating is subjected to phosphorization, soaking treatment is conducted through wiredrawing protecting liquid, heat treatment is conducted, and finally, the copper wire is formed by stretching through a wire drawing machine. The copper wire has the excellent extending performance, and the product pass rate is high.

Description

technical field [0001] The invention relates to the technical field of wires, in particular to a production method for making copper wires. Background technique [0002] Copper (4N copper) with a purity of more than 99.99% belongs to chivalrous high-purity copper, while ultra-high-purity copper (5N-7N) can be broadly called high-purity copper. High-purity copper wires based on generalized high-purity copper have broad application prospects in electronic and electrical products as high-end electronic materials, such as: high-definition TV signal lines, high-quality speaker wires, special enameled wires for electric vehicle motors, vacuum Target materials for evaporation, copper strips for solar photovoltaics, etc. Compared with conventional copper, high-purity copper wire has higher purity, fewer lattice defects and impurities, which in turn endows higher electrical conductivity, better heat dissipation and better flexibility. These characteristics are The high fidelity, lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21C37/04B21C9/02
CPCB21C9/02B21C37/04
Inventor 杨忠义
Owner 惠州市秋叶原铜业发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap