Lightweight and hemp addition polyurethane sole and preparation method thereof

A polyurethane, lightweight technology, applied in the field of sole materials, can solve the problems of poor wear resistance, cracking of soles, intolerant of hydrolysis, etc., and achieve the effects of high wear resistance, improved mechanical stability, strength, and good impact resistance.

Inactive Publication Date: 2019-08-20
泉州邦尼生物科技有限公司
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] However, the currently produced polyurethane soles have poor wear resistance and are not resistant to hydrolysis, which can easily lead to cracks and breakage of the soles, resulting in certain limitations in the application range of polyurethane soles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of lightweight hemp polyurethane sole, comprises each raw material of following parts by weight:

[0030] Azodicarbonamide 3, polysorbate 0.7, phosphorous acid 1, polycarbonate diol 80, isophorone diisocyanate 60-, initiator 1, dibutyltin dilaurate 0.5, color paste 0.1, light filler Dispersion liquid 50, p-toluenesulfonic acid 0.01.

[0031] Described initiator is dicumyl peroxide.

[0032] Described lightweight filler dispersion liquid is made up of the raw material of following weight part:

[0033] Baking soda 2, sawdust 40, light calcium carbonate 10, bisphenol a 0.3, trimethylolpropane 3, methyl methacrylate 15, ammonium persulfate 0.5.

[0034] The preparation method of described lightweight filler dispersion liquid, comprises the following steps:

[0035] (1) Take ammonium persulfate, add it to deionized water 40 times its weight, and stir evenly to obtain ammonium persulfate aqueous solution;

[0036] (2) Take sawdust, grind it into fine powder, mix i...

Embodiment 2

[0045] A kind of lightweight hemp polyurethane sole, comprises each raw material of following parts by weight:

[0046] Azodicarbonamide 4, polysorbate 1, phosphorous acid 2, polycarbonate diol 100, isophorone diisocyanate 70, initiator 2, dibutyltin dilaurate 1, color paste 0.2, light filler dispersion Liquid 63, p-toluenesulfonic acid 0.02.

[0047] Described initiator is dicumyl peroxide.

[0048] Described lightweight filler dispersion liquid is made up of the raw material of following weight part:

[0049] Baking soda 3, sawdust 55, light calcium carbonate 15, bisphenol a 0.7, trimethylol propane 5, methyl methacrylate 20, ammonium persulfate 0.8.

[0050] The preparation method of described lightweight filler dispersion liquid, comprises the following steps:

[0051] (1) Take ammonium persulfate, add it to deionized water 60 times its weight, and stir evenly to obtain ammonium persulfate aqueous solution;

[0052] (2) Take sawdust, grind it into fine powder, mix it w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lightweight and hemp addition polyurethane sole. The sole material comprises the following raw materials in parts by weight: 3-4 parts of azodicarbonamide, 0.7-1 parts of polysorbate, 1-2 parts of phosphorous acid, 80-100 parts of polycarbonate diol, 60-70 parts of isophorone diisocyanate, 1-2 parts of an initiator, 0.5-1 parts of dibutyltin dilaurate, 0.1-0.2 part of a color paste, 50-63 parts of a lightweight filler dispersion, and 0.01-0.02 part of p-toluenesulfonic acid. The sole material is light in weight, good in impact resistance, high in wear resistance, andsuperior in overall performance.

Description

technical field [0001] The invention belongs to the field of shoe sole materials, and in particular relates to a lightweight hemp polyurethane shoe sole and a preparation method thereof. Background technique [0002] Polyurethane sole material has the following advantages: [0003] 1. It has the characteristics of softness, warmth, oil resistance, flex resistance, and wear resistance. It is more than 6 times more wear-resistant than rubber. It can adjust the density and hardness in a wide range according to the requirements of use. It can be made into double-color (double-density) double layers. Sole, the lower sole is a micro-foamed high wear-resistant working surface, and the inner sole is elastic foam that is comfortable to wear; [0004] 2. Very light, with a specific gravity of only 0.3-0.8, much lighter than commonly used sole materials. It is more suitable for thick-soled shoes that require impact resistance and anti-perforation. 15% of the world's safety protection ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L97/02C08L33/12C08K3/26C08G18/75C08G18/44C08J9/10A43B13/04C08G101/00
CPCA43B13/04C08G18/44C08G18/755C08G2101/00C08J9/0061C08J9/0066C08J9/103C08J2203/04C08J2375/04C08J2433/12C08J2497/02C08K2003/265
Inventor 吕正军王连波秦壮利李宁
Owner 泉州邦尼生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com