A technology of photocatalyst and activated carbon, which is applied in the direction of catalyst activation/preparation, metal/metal oxide/metal hydroxide catalyst, physical/chemical process catalyst, etc. Large specific surface area, the effect of realizing industrial production

Active Publication Date: 2019-08-23
KUNMING UNIV OF SCI & TECH
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Catalysts for photocatalytic water treatment in the prior art generally use TiO 2 Supported metal oxide catalysts, but with a band gap of 3.2 eV, can only absorb ultraviolet light and fail to absorb visible light. Therefore, it is necessary to develop a photocatalyst for water treatment that can absorb both ultraviolet and visible light

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of tetragonal-phase bismuth oxide activated carbon photocatalyst
  • Preparation method and application of tetragonal-phase bismuth oxide activated carbon photocatalyst
  • Preparation method and application of tetragonal-phase bismuth oxide activated carbon photocatalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: a kind of preparation method of square phase bismuth oxide activated carbon photocatalyst, concrete steps are as follows:

[0027] (1) Put the deactivated activated carbon under the conditions of microwave power of 800W and temperature of 600°C for 30 minutes to obtain regenerated activated carbon; the deactivated activated carbon is the deactivated activated carbon treated with anthraquinone, and the particle size of the deactivated activated carbon is The diameter is 180 mesh, and the methylene blue adsorption value is 30mg / g;

[0028] (2) Mix the regenerated activated carbon in step (1) with lysine solution and bismuth nitrate solution evenly, impregnate and react for 180 minutes under stirring conditions, and then place it in microwave roasting for 10 minutes at a microwave power of 700W and a temperature of 500°C. Pros and Cons 2 o 3 -AC photocatalyst; Wherein the concentration of lysine solution is 0.5 g / L, the concentration of bismuth nitrate solu...

Embodiment 2

[0030] Embodiment 2: a kind of preparation method of square phase bismuth oxide activated carbon photocatalyst, concrete steps are as follows:

[0031] (1) Put the deactivated activated carbon under the conditions of microwave power of 1000 W and temperature of 900 °C for 10 minutes to obtain regenerated activated carbon; the deactivated activated carbon is the deactivated activated carbon treated with anthraquinone, and the deactivated activated carbon is The particle size is 200 mesh, and the adsorption value of methylene blue is 45mg / g;

[0032] (2) Mix the regenerated activated carbon in step (1) with lysine solution and bismuth nitrate solution evenly, impregnate and react for 120 minutes under stirring conditions, and then place it in microwave roasting for 30 minutes at a microwave power of 500W and a temperature of 300°C. Pros and Cons 2 o 3 -AC photocatalyst; Wherein the concentration of lysine solution is 0.1 g / L, the concentration of bismuth nitrate solution is 0....

Embodiment 3

[0034] Embodiment 3: a kind of preparation method of square phase bismuth oxide activated carbon photocatalyst, concrete steps are as follows:

[0035](1) Put the deactivated activated carbon under the conditions of microwave power of 1000W and temperature of 800°C for 20 minutes to obtain regenerated activated carbon; the deactivated activated carbon is deactivated activated carbon treated with anthraquinone, and the particle size of the deactivated activated carbon is 200 mesh, methylene blue adsorption value is 45mg / g;

[0036] (2) Mix the regenerated activated carbon in step (1) with lysine solution and bismuth nitrate solution evenly, impregnate and react for 160 minutes under stirring conditions, and then place it in microwave roasting for 20 minutes at a microwave power of 1000W and a temperature of 900°C. Pros and Cons 2 o 3 -AC photocatalyst; Wherein the concentration of lysine solution is 0.1 g / L, the concentration of bismuth nitrate solution is 0.15mol / L, the soli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method and application of a tetragonal-phase bismuth oxide activated carbon photocatalyst and belongs to the technical field of photocatalysts. The preparation method disclosed by the invention comprises the following steps: reacting inactivated activated carbon at a constant temperature under conditions of a microwave power of 800-1000W and a temperature of600-900 DEG C for 10-30 minutes so as to obtain regenerated activated carbon; uniformly mixing the regenerated activated carbon with a lysine solution and a bismuth nitrate solution, and carrying outan impregnated reaction under stirred conditions for 120-240 minutes; and performing microwave roasting under the conditions of a microwave power of 500-1000W and a temperature of 300-900 DEG C for 10-30 minutes so as to obtain the tetragonal-phase Bi2O3-AC photocatalyst. According to the preparation method disclosed by the invention, the inactivated activated carbon serves as a carrier of a metaloxide, and the prepared tetragonal-phase bismuth oxide activated carbon photocatalyst can achieve effects of improving the adsorption capacity and degrading dyes in dye wastewater under visible / ultraviolet light irradiation.

Description

technical field [0001] The invention relates to a preparation method and application of a square-phase bismuth oxide activated carbon photocatalyst, belonging to the technical field of photocatalysts. Background technique [0002] Activated carbon has excellent properties such as developed pore structure, high specific surface area, and recyclability. It is a good adsorbent and can be widely used to treat industrial wastewater. After a period of use, a large amount of deactivated activated carbon will be produced due to the deactivation of activated carbon. If deactivated activated carbon cannot be used efficiently, it will have a serious impact on the environment and human health, so the treatment of deactivated activated carbon has become an inevitable trend. [0003] Bismuth oxide (Bi 2 o 3 ) is a P-type semiconductor material, and the crystal forms included are monoclinic α-Bi 2 o 3 , tetragonal β-Bi 2 o 3 , cubic γ-Bi 2 o 3 and δ-Bi 2 o 3 . Bi 2 o 3 It is c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/18B01J35/10B01J37/02B01J37/08B01J37/34C02F1/30C02F101/38C02F101/30
CPCB01J23/18C02F1/30B01J37/346B01J37/086B01J37/0203C02F2101/40C02F2101/308C02F2305/10B01J35/61B01J35/39