Preparing method of glass-flake mastic resin

A technology of glass flakes and cement, which is applied in the direction of anti-corrosion coatings, coatings, etc., can solve problems such as shedding, poor corrosion resistance and impermeability, and easy cracking of glass flake cement, so as to prevent falling off, be difficult to crack and fall off, and improve Effect of Crosslink Density on Micro-Space Structure

Inactive Publication Date: 2019-09-06
刘勇
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The technical problem to be solved by the present invention is to provide a preparation method of glass flake cement in view of the defects that the current glass flake cement is easy to crack and fall off, and has poor corrosion resistance and permeability resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparing method of glass-flake mastic resin

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0031] Preparation of reactants:

[0032] Weigh 500g of wheat straw and put it into a pulverizer to pulverize to obtain pulverized products. Mix the pulverized products with aluminum chloride at a mass ratio of 10:1 and put them into the reactor, impregnate them with distilled water, and fill the reactor with nitrogen until the pressure in the reactor rises. As high as 1.8MPa, raise the temperature in the kettle to 160°C, and react at constant temperature and pressure for 60 minutes to prepare the reactant.

[0033] Preparation of heat-treated products:

[0034] Put the above reactants and 4% sodium hydroxide solution into a beaker at a mass ratio of 1:5, mix and stir with a stirrer at a speed of 500r / min for 30min, filter after stirring to obtain a filter residue, and place the filter residue in a tubular In the furnace, the tube furnace was evacuated, the temperature in the furnace was raised to 230° C., and the heat treatment product was obtained by constant temperature he...

example 2

[0042] Preparation of reactants:

[0043] Weigh 600g of wheat straw and put it into a pulverizer to pulverize to obtain pulverized products. Mix the pulverized products with aluminum chloride at a mass ratio of 10:1 and put them into the reactor, impregnate them with distilled water, and fill the reactor with nitrogen until the pressure in the reactor rises. As high as 1.9MPa, raise the temperature in the kettle to 170°C, and react at constant temperature and pressure for 70 minutes to prepare the reactant.

[0044] Preparation of heat-treated products:

[0045] Put the above reactant and sodium hydroxide solution with a mass fraction of 6% into a beaker at a mass ratio of 1:5, mix and stir with a stirrer at a speed of 550r / min for 35min, filter after stirring to obtain a filter residue, and place the filter residue in a tubular In the furnace, the tube furnace was evacuated, the temperature in the furnace was raised to 235° C., and the heat treatment product was obtained by ...

example 3

[0053] Preparation of reactants:

[0054] Weigh 700g of wheat straw and put it into a pulverizer to pulverize to obtain pulverized products. Mix the pulverized products with aluminum chloride at a mass ratio of 10:1 and put them into the reactor, impregnate them with distilled water, and fill the reactor with nitrogen until the pressure in the reactor rises. As high as 2.0MPa, raise the temperature in the kettle to 180°C, and react at constant temperature and pressure for 80 minutes to prepare the reactant.

[0055] Preparation of heat-treated products:

[0056] Put the above reactant and sodium hydroxide solution with a mass fraction of 8% into a beaker at a mass ratio of 1:5, mix and stir with a stirrer at a speed of 600r / min for 40min, filter after stirring to obtain a filter residue, and place the filter residue in a tubular In the furnace, the tube furnace was evacuated, the temperature in the furnace was raised to 240° C., and the heat treatment product was obtained by ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparing method of glass-flake mastic resin, and belongs to the technical field of preparation of chemical coatings. The preparing method comprises the steps of firstly, taking wheat straw and aluminum chloride as raw materials to prepare a calcined product, then mixing the calcined product with glucose and potato slices for microbial fermentation treatment, conductinghigh-temperature calcination, and then mixing a calcined product with polyurethane, glass flakes and other auxiliary agents to obtain the glass-flake mastic resin. According to the preparing method, part of fibers are decomposed into carboxy groups, hydroxy groups, epoxy groups and other organic groups, the bonding effect among all molecules in the glass-flake mastic resin is enhanced, and the crosslinking density of the microcosmic spatial structure of the mastic resin is increased; meanwhile, cracking of a mastic resin coating is effectively prevented, and shedding is avoided. According to the preparing method, aluminum ions are introduced into the glass-flake mastic resin, then alkaline liquor is dropwise added so that the aluminum ions can form an aluminum hydroxide precipitate to coatthe fibers, and it is ensured that the mastic resin coating is unlikely to be corroded by microorganisms and salt; meanwhile, the glass-flake mastic resin has good permeation resistance and a wide application prospect.

Description

technical field [0001] The invention relates to a method for preparing glass flake cement, which belongs to the technical field of chemical coating preparation. Background technique [0002] Glass flake cement is a mixed material that is composed of resin as a binder and added with glass flake pigments, curing agents, additives and solvents. It can be scraped and wiped. Glass flake cement has become an indispensable and important raw material for the production of heavy-duty anti-corrosion coatings, pearlescent pigments and plastic products due to its excellent properties such as high temperature resistance, corrosion resistance, wear resistance, penetration resistance, adhesion, durability and impact resistance. The glass flake cement component contains a large number of glass flakes, which have strong shielding properties after film formation, can effectively prevent the penetration of corrosive media, and achieve the purpose of isolation and antirust. Glass flake coating...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D5/08C09D7/65C09D7/61
CPCC09D4/06C09D5/08C09D7/61C09D7/65C09D7/70
Inventor 刘勇
Owner 刘勇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products