A kind of nickel-vanadium master alloy and preparation method thereof

An intermediate alloy, nickel-vanadium technology, applied in the field of metallurgy, can solve problems such as high cost and complicated production process of high-purity vanadium, and achieve the effects of avoiding pollution, facilitating separation, and good heat preservation performance

Active Publication Date: 2021-05-14
METALINK SPECIAL ALLOYS CORP
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The addition of vanadium to nickel-based superalloys can use metal vanadium, aluminum-vanadium alloys or nickel-vanadium alloys. The production process of high-purity vanadium is complicated and the cost is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nickel-vanadium master alloy and preparation method thereof
  • A kind of nickel-vanadium master alloy and preparation method thereof
  • A kind of nickel-vanadium master alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A preparation method of a nickel-vanadium master alloy material, comprising the following steps:

[0018] 1) Selection and analysis of raw materials: The raw materials are vanadium pentoxide, nickel oxide, aluminum powder, aluminum-magnesium alloy and the purity control of the furnace powder is as follows:

[0019] Table 1

[0020]

[0021] 2) Raw material pretreatment: put the vanadium pentoxide into a drying furnace, and dry it at 300° C. for 24 hours. Put the nickelous oxide into the sintering furnace and sinter at 800°C for 8 hours.

[0022] 3) Mixing: Weigh the baked raw materials according to the formula, put them into a V-shaped mixer and mix them evenly. When mixing the materials, the temperature of the materials must be controlled below 150°C. It is necessary to ensure that the materials are fully mixed. The time is 15 minutes.

[0023] 4) Bake and dry the alumina crucible.

[0024] 5) Reaction: Put the uniformly mixed raw materials into the alumina furn...

Embodiment 2

[0041] The preparation method of the present embodiment is basically the same as that of Example 1, the difference is as follows:

[0042] 1. Process conditions

[0043] Table 4

[0044] raw material baking temperature 300℃(±20℃) raw material baking time 18 hours NiO sintering temperature 900℃ Sintering time 8 hours Mixing time 15 minutes Charge temperature 70℃ Reaction time 64s cooling time 40 hours Alloy ingot weight 143㎏ Broken particle size 10～30㎜

[0045] 2. Formula

[0046] table 5

[0047]

[0048] 3. Reaction situation: the reaction process is relatively fast, the recovery rate of vanadium: 94.16%, and the recovery rate of nickel: 97.33%.

[0049] 4. Alloy analysis results

[0050] Table 6

[0051]

Embodiment 3

[0053] The preparation method of the present embodiment is basically the same as that of Example 1, the difference is as follows:

[0054] 1. Process conditions

[0055] Table 7

[0056] raw material baking temperature 180℃(±20℃) raw material baking time 12 hours NiO sintering temperature 700℃ Sintering time 8 hours Mixing time 15 minutes Charge temperature 70℃ Reaction time 61s cooling time 40 hours Alloy ingot weight 142㎏ Broken particle size 10～30㎜

[0057] 2. Formula

[0058] Table 8

[0059]

[0060] 3. Reaction situation: intense reaction, vanadium recovery rate: 94.16%, nickel recovery rate: 97.13%.

[0061] 4. Alloy analysis results

[0062] Table 9

[0063]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an alloy and a preparation method thereof, in particular to a nickel-vanadium master alloy and a preparation method thereof, belonging to the technical field of metallurgy. The alloy of the present invention contains the following elements in mass percentage: 60%-70% of vanadium, 30%-40% of nickel, ≤1.5% of aluminum, and the remaining total trace elements and impurities are less than 1%. The invention also discloses a preparation method of the nickel vanadium master alloy material. The nickel-vanadium master alloy of the present invention can greatly reduce the temperature for smelting nickel-based alloys; the preparation of the nickel-vanadium master alloy adopts strict raw material control, the product has high purity, low impurity content, good controllability, high production efficiency, and alloy nitrogen and oxygen Lower content, more pure.

Description

technical field [0001] The invention relates to an alloy and a preparation method thereof, in particular to a nickel-vanadium master alloy and a preparation method thereof, belonging to the technical field of metallurgy. Background technique [0002] The melting point of metal vanadium is 1890°C, while the melting point of the nickel-vanadium master alloy mentioned in the present invention is about 1450°C, which greatly reduces the melting point of vanadium and is a necessary additive for smelting nickel-based vanadium-containing superalloys. Vanadium addition plays a role of solid solution strengthening in superalloys and improves the physical properties of superalloys. The vanadium element added to the nickel-based superalloy can be metal vanadium, aluminum-vanadium alloy or nickel-vanadium alloy. The production process of high-purity vanadium is complicated and the cost is high. Contents of the invention [0003] The object of the present invention is to propose a nick...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C27/02C22C1/03
CPCC22C1/03C22C27/025
Inventor 马步洋王晓蓉陈道华贾明
Owner METALINK SPECIAL ALLOYS CORP