A low elastic modulus, high strength amplitude modulation decomposition type zr-nb-ti alloy material and preparation method thereof

A low elastic modulus, zr-nb-ti technology, applied in prosthetics, medical science, etc., can solve problems such as low elastic modulus, achieve low elastic modulus, good ductility, and improve the effect of alloy strength

Active Publication Date: 2020-11-06
XIANGTAN UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problem that zirconium alloys in the prior art cannot achieve low elastic modulus and high strength at the same time, the purpose of the present invention is to provide a low elastic modulus, high strength amplitude modulation decomposition type Zr-Nb-Ti alloy material and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low elastic modulus, high strength amplitude modulation decomposition type zr-nb-ti alloy material and preparation method thereof
  • A low elastic modulus, high strength amplitude modulation decomposition type zr-nb-ti alloy material and preparation method thereof
  • A low elastic modulus, high strength amplitude modulation decomposition type zr-nb-ti alloy material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] (1) Weighing: Weigh raw materials: made of 30% Ti, 30% Nb, and Zr in the atomic percentage of elements, and weigh high-purity titanium grains, high-purity niobium grains, and high-purity zirconium grains respectively. The purity of high-purity titanium particles, high-purity niobium particles, and high-purity zirconium particles is not less than 99.99%.

[0046] (2) Melting: put the raw materials weighed in step (1) into a vacuum arc melting furnace for melting, the melting current is 220A, and the melting suspension time is 65s. In order to improve the accuracy and uniformity of the composition, the ingot needs to be smelted six times repeatedly to obtain the ingot.

[0047] (3) Suction casting: putting the ingot obtained in step (2) into a vacuum arc melting furnace for suction casting to obtain a zirconium alloy rod.

[0048] (4) Microstructure control: the suction casting rod obtained in step (3) is subjected to solution treatment, and in the solution treatment ste...

Embodiment 2

[0051] (1) Weigh each component: Weigh the raw material: it is made of 33% Ti, 31% Nb, and the balance is Zr according to the atomic percentage of the elements. Weigh high-purity titanium grains, high-purity niobium grains, and high-purity zirconium grains respectively . The purity of high-purity titanium particles, high-purity niobium particles, and high-purity zirconium particles is not less than 99.99%.

[0052] (2) Melting: put the raw materials weighed in step (1) into a vacuum arc melting furnace for melting, the melting current is 200A, and the melting suspension time is 90s. In order to improve the accuracy and uniformity of the composition, the ingot needs to be smelted six times repeatedly to obtain the ingot.

[0053] (3) Suction casting: putting the ingot obtained in step (2) into a vacuum arc melting furnace for suction casting to obtain a zirconium alloy rod.

[0054] (4) Microstructure control: the suction casting rod obtained in step (3) is subjected to solut...

Embodiment 3

[0057] (1) Weigh each component: Weigh the raw material: it is made of 30% Ti, 30% Nb, and the balance is Zr according to the atomic percentage of the elements. Weigh high-purity titanium grains, high-purity niobium grains, and high-purity zirconium grains respectively . The purity of high-purity titanium particles, high-purity niobium particles, and high-purity zirconium particles is not less than 99.99%.

[0058] (2) Melting: put the raw materials weighed in step (1) into a vacuum arc melting furnace for melting, the melting current is 230A, and the melting suspension time is 85s. In order to improve the accuracy and uniformity of the composition, the ingot needs to be smelted six times repeatedly to obtain the ingot.

[0059] (3) Suction casting: putting the ingot obtained in step (2) into a vacuum arc melting furnace for suction casting to obtain a zirconium alloy rod.

[0060] (4) Microstructure control: the suction casting rod obtained in step (3) is subjected to solut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
elastic modulusaaaaaaaaaa
compressive yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-elasticity-modulus and high-strength spinodal decomposition type Zr-Nb-Ti alloy material and a preparation method thereof. The Zr-Nb-Ti alloy material comprises the following components in atomic percentage: 20-50% of Ti, 15-45% of Nb and the balance of Zr. The preparation method comprises the following steps: a titanium source, a niobium source and a zirconium sourceare prepared according to designed ratios; zirconium alloy ingots are obtained through multiple times of smelting; zirconium alloy rods are obtained through the zirconium alloy ingots by suction casting; and solid-solution treatment and aging treatment are performed on the zirconium alloy rods in sequence to obtain the Zr-Nb-Ti alloy material. The zirconium alloy material is higher in strength and low in elasticity modulus; the highest strength can reach 1130.8+ / -8.5 MPa; and the elasticity modulus is maintained between 40-50 GPa, and is near the elasticity modulus of human bodies.

Description

technical field [0001] The invention belongs to the technical field of medical zirconium alloys, in particular to a low elastic modulus, high-strength amplitude modulation decomposition type Zr-Nb-Ti alloy material and a preparation method thereof. [0002] technical background [0003] In recent years, with the development of society and the improvement of human living standards, people's demand for safe and reliable biological implant materials is increasing. Therefore, a large number of scientific researchers have conducted in-depth research on implantable biological hard tissue materials. To develop alloys for human implants, the alloys are first required to have excellent biocompatibility. Nowadays, the biocompatible alloying elements used in biomedical metal materials mainly include Ti, Zr, Nb, Ta, Mo, Sn, Mg, Zn, etc. Secondly, this type of alloy needs to have high strength and excellent corrosion resistance. On this basis, the alloy also needs to have a lower elasti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C16/00A61L27/04A61L27/06C22C1/02C22C14/00C22F1/18
CPCA61L27/047A61L27/06C22C1/02C22C14/00C22C16/00C22F1/183C22F1/186
Inventor 林建国易琼华张德闯檀朝桂龚伦军马蓦
Owner XIANGTAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com