Low-smoke halogen-free flame-retardant ABS material for edge sealing strips, and preparation method thereof

A technology of ABS material and edge banding, which is applied in the field of low-smoke halogen-free flame-retardant ABS material for edge banding and its preparation, and can solve problems such as chipping of edge banding, affecting the physical and mechanical properties of ABS, and decreasing impact strength. Achieve the effects of reducing impact, improving the chance of human escape, and reducing mixing torque and load

Active Publication Date: 2019-11-12
东莞市华富立装饰建材有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] As an effective inorganic flame retardant for low-smoke, halogen-free flame-retardant ABS materials, such as magnesium hydroxide and aluminum hydroxide, a large amount of filling is required to achieve the expected flame-retardant effect, which greatly affects the physical and mechanical properties of ABS, especially the impact The strength drops a lot, and even turns into a brittle material, which causes the edge banding to collapse when it is used for edge banding.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-smoke halogen-free flame-retardant ABS material for edge sealing strips, and preparation method thereof
  • Low-smoke halogen-free flame-retardant ABS material for edge sealing strips, and preparation method thereof
  • Low-smoke halogen-free flame-retardant ABS material for edge sealing strips, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A low-smoke halogen-free flame-retardant ABS material for edge banding, comprising the following raw materials in parts by weight:

[0035]

[0036] Wherein, the mesh number of the halogen-free flame retardant filler is 8000 mesh.

[0037] The ABS resin is an ABS resin with a polybutadiene content of 30 wt %; the melt flow rate of the ABS resin is 50 g / min.

[0038] The halogen-free flame retardant filler is magnesium aluminum hydrotalcite.

[0039] The smoke suppressant is ferrocene.

[0040] The surface modifier is a silane coupling agent.

[0041] The silane coupling agent is KH550.

[0042] The lubricant is formed by mixing polyethylene wax and magnesium stearate at a weight ratio of 2:1.

[0043] The preparation method of the above-mentioned low-smoke halogen-free flame-retardant ABS material for edge banding comprises the following steps:

[0044] (S1), take raw material by weight, standby;

[0045] (S2), blend the halogen-free flame retardant filler, smo...

Embodiment 2

[0050] A low-smoke halogen-free flame-retardant ABS material for edge banding, comprising the following raw materials in parts by weight:

[0051]

[0052] Wherein, the mesh number of the halogen-free flame retardant filler is 7500 mesh.

[0053] The ABS resin is an ABS resin with a polybutadiene content of 29 wt %; the melt flow rate of the ABS resin is 48 g / min.

[0054] The halogen-free flame retardant filler is magnesium aluminum hydrotalcite.

[0055] The smoke suppressant is ferrocene.

[0056] The surface modifier is a silane coupling agent.

[0057] The silane coupling agent is KH560.

[0058] The lubricant is formed by mixing polyethylene wax and magnesium stearate at a weight ratio of 2:1.

[0059] The preparation method of the above-mentioned low-smoke halogen-free flame-retardant ABS material for edge banding comprises the following steps:

[0060] (S1), take raw material by weight, standby;

[0061] (S2), blend the halogen-free flame retardant filler, smo...

Embodiment 3

[0066] A low-smoke halogen-free flame-retardant ABS material for edge banding, comprising the following raw materials in parts by weight:

[0067]

[0068] Wherein, the mesh number of the halogen-free flame retardant filler is 10000 mesh.

[0069] The ABS resin is an ABS resin with a polybutadiene content of 28 wt %; the melt flow rate of the ABS resin is 45 g / min.

[0070] The halogen-free flame retardant filler is magnesium aluminum hydrotalcite.

[0071] The smoke suppressant is ferrocene.

[0072] The surface modifier is a silane coupling agent.

[0073] The silane coupling agent is KH570.

[0074] The lubricant is formed by mixing polyethylene wax and magnesium stearate at a weight ratio of 2:1.

[0075] The preparation method of the above-mentioned low-smoke halogen-free flame-retardant ABS material for edge banding comprises the following steps:

[0076] (S1), take raw material by weight, standby;

[0077] (S2), blend the halogen-free flame retardant filler, sm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melting pointaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of edge sealing strip material modification, particularly to a low-smoke halogen-free flame-retardant ABS material for edge sealing strips, and a preparation method thereof, wherein the low-smoke halogen-free flame-retardant ABS material comprises the following materials: an ABS resin, a halogen-free flame-retardant filler, a smoke suppressant, a surface modifier and a lubricant, wherein the halogen-free flame-retardant filler has a particle size of 7500-10000 mesh. According to the present invention, the ABS material can increase the compatibilityamong the halogen-free flame-retardant filler, the smoke suppressant and the ABS resin, such that the flame-retardant smoke suppressing effect of the ABS material is increased, the ABS material is strengthened, and the condition that the excessive filling with the halogen-free flame-retardant filler and the smoke suppressant can reduce the mechanical property of the ABS material so as to cause theABS material embrittlement can be avoided so as to avoid the embrittlement of the edge sealing strip prepared from the ABS material and reduce the probability of the corner chipping of the edge sealing strip.

Description

technical field [0001] The invention relates to the technical field of modification of edge banding materials, in particular to a low-smoke, halogen-free flame-retardant ABS material for edge banding and a preparation method thereof. Background technique [0002] It is understood that when a fire breaks out, it is the toxic gas and highly toxic smoke released when the material burns that causes harm to the human body. The strong and diffuse smoke makes the victim unable to distinguish the direction, thus prolonging the stay time at the fire scene Therefore, in order to avoid and reduce the secondary damage caused by fire and fire, low-smoke halogen-free flame-retardant home decoration materials are more and more popular. [0003] The edge bands commonly used in home decoration are generally divided into log edge bands, PVC edge bands and ABS edge bands. Although the log edge banding is simple to make, it is expensive, especially with the gradual improvement of people's awar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L23/06C08K13/06C08K9/06C08K3/26C08K5/098C08K3/22
CPCC08L55/02C08L2201/02C08L2201/22C08K2003/2224C08K2003/2227C08K2201/005C08L23/06C08K9/06C08K3/26C08K5/098C08K13/06C08K3/22
Inventor 谭洪汝罗绍伟李贝特
Owner 东莞市华富立装饰建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products