One-component moisture-curable organosilicon graffito-resistant intelligent coating material and preparation method thereof

A moisture-curing, silicone technology, applied in coatings and other directions, can solve the problems of incomplete protection and the effect of anti-graffiti coatings is not durable, and achieve the effects of easy brittle cracking, strong water and oil repellency, and good flexibility.

Active Publication Date: 2019-11-19
SHENZHEN GRANDLAND ENVIRONMENTAL COATING CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention provides a one-component moisture-cured organic silicon anti-graffiti smart coating and its preparation method to solve the problems of non-permanent anti-graffiti coating effect and incomplete protection. The anti-graffiti product coating has stronger hydrophobicity and oil resistance The marking pen has the characteristics of good prevention and control effect and long-lasting effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-component moisture-curable organosilicon graffito-resistant intelligent coating material and preparation method thereof
  • One-component moisture-curable organosilicon graffito-resistant intelligent coating material and preparation method thereof
  • One-component moisture-curable organosilicon graffito-resistant intelligent coating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The preparation method of the one-component moisture-cured silicone graffiti-resistant smart coating of the present invention is as follows:

[0025] step one:

[0026] Add 5.4kg of polyether-modified silane-terminated polymer WR1944 from Hairun Company and 3.0kg of bisaminosilane coupling agent KH-792 from the Chinese Academy of Sciences in a dry and clean paint mixing tank. Stir and mix at 500 rpm for 15 minutes, then seal the package and leave for 2 hours to prepare a premixed liquid of bisaminosilane coupling agent and polyether-modified silane-terminated polymer for use in Step 2.

[0027] Step two:

[0028] Add 78.5kg of pure silicone resin WR1189 from Hairun Company, 12.8kg polydimethylsiloxane resin WR1951 from Hairun Company, and bisaminosilane prepared in step 1 in a dry and clean paint mixing tank. Coupling agent and polyether-modified silane-terminated polymer premix 8.4kg, Silok 8225H silicone defoamer 0.3kg, start stirring after adding, at 500-700 rpm Sti...

Embodiment 2

[0030] The preparation method of the one-component moisture-cured silicone graffiti-resistant smart coating of the present invention is as follows:

[0031] step one:

[0032] Add 6.2kg of polyether-modified silane-terminated polymer WR1944 from Hairun Company and 3.5kg of bisaminosilane coupling agent KH-792 from the Chinese Academy of Sciences into a dry and clean paint mixing tank. Stir and mix at 500 rpm for 15 minutes, then seal the package and leave for 2 hours to prepare a premixed liquid of bisaminosilane coupling agent and polyether-modified silane-terminated polymer for use in Step 2.

[0033] Step two:

[0034] Add 76.4kg of pure silicone resin WR1189 from Hairun Company, 13.5kg polydimethylsiloxane resin WR1951 from Hairun Company, and bisaminosilane prepared in Step 1 into the dry and clean paint mixing tank. Coupling agent and polyether-modified silane-terminated polymer premix 9.7kg, Silok 8225H silicone defoamer 0.4kg, start stirring after adding, at 500 ~ 70...

Embodiment 3

[0036] The preparation method of the one-component moisture-cured silicone graffiti-resistant smart coating of the present invention is as follows:

[0037] step one:

[0038] Add 7.0kg of polyether-modified silane-terminated polymer WR1944 from Hairun Company and 4.0kg of bisaminosilane coupling agent KH-792 from the Chinese Academy of Sciences into a dry and clean paint tank. Stir and mix at 500 rpm for 15 minutes, then seal the package and leave for 2 hours to prepare a premixed liquid of bisaminosilane coupling agent and polyether-modified silane-terminated polymer for use in Step 2.

[0039] Step two:

[0040] Add 74.3kg of pure silicone resin WR1189 from Hairun Company, 14.2kg polydimethylsiloxane resin WR1951 from Hairun Company, and bisaminosilane prepared in step 1 in a dry and clean paint mixing tank. Coupling agent and polyether-modified silane-terminated polymer premix 11.0kg, Silok 8225H silicone defoamer 0.5kg, start stirring after adding, at 500-700 rpm Stir ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
flash pointaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a one-component moisture-curable organosilicon graffito-resistant intelligent coating material and a preparation method thereof, wherein the one-component moisture-curable organosilicon graffito-resistant intelligent coating material is obtained by mixing and blending the following components by weight: 74.3-78.5 parts of a pure silicon resin, 12.8-14.2 parts of a polydimethylsiloxane resin, 8.4-11.0 parts of a pre-mixed solution of a silane coupling agent and a silane-terminated polymer, and 0.3-0.5 part of an organosilicon defoamer, wherein the pre-mixed solution of the silane coupling agent and the silane-terminated polymer is obtained by mixing and blending the following components by weight: 5.4-7.0 parts of a polyether-modified silane-terminated polymer and 3.0-4.0 parts of a diaminosilane coupling agent. According to the present invention, the prepared one-component moisture-curable organosilicon graffito-resistant intelligent coating material can solve the problems of not lasting effect and incomplete protection of the graffito-resistant coating material, and further has the following characteristics that the hydrophobicity of the graffito-resistant product coating is strong, and the prevention and treatment effect on oily marking pens is good and long-lasting.

Description

technical field [0001] The invention relates to the technical field of new functional materials for architectural decoration, in particular to a one-component moisture-cured organic silicon graffiti-resistant intelligent paint and a preparation method thereof. Background technique [0002] Anti-graffiti coatings are produced in Europe and America, including sacrificial anti-graffiti coatings, semi-permanent anti-graffiti coatings and permanent anti-graffiti coatings. Graffiti materials are both water-based and oil-based. my country's anti-graffiti coatings started in 2004. In 2007, relevant norms and standards were introduced to carry out anti-graffiti rectification work. Many scientific research institutions and coating manufacturers began to get involved. [0003] The current anti-graffiti coating product system in the market basically uses non-organosilicon materials such as fluorocarbon, polyurethane, and acrylic acid as the main materials, and achieves the anti-graffit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D7/63C09D7/65
CPCC08L2205/025C08L2205/03C09D183/04C09D7/63C09D7/65C08L83/04C08L71/00C08K5/544
Inventor 徐新祥付超王鹏程刘述敏曾燕曼
Owner SHENZHEN GRANDLAND ENVIRONMENTAL COATING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com