A kind of vanadium-based lead-free glass powder and its preparation method and application

A technology of fine vanadium-based lead-free glass and lead-free glass powder, which is applied in glass manufacturing equipment, glass furnace equipment, glass molding, etc., and can solve the problems of large particle size, low conversion efficiency of solar cells, and high glass transition temperature of glass powder. problem, to achieve the effects of reduced transition temperature, simple screening and simple conditions

Active Publication Date: 2022-05-03
江苏聚盈新材料科技有限公司
View PDF17 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the high glass transition temperature and large particle size of the glass frit used in the existing preparation of lead-free paste, the price of lead-free paste is expensive, it is not conducive to large-scale production, and the existing paste is used The problem of low conversion efficiency of solar cells, and provide a vanadium-based lead-free glass powder and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of vanadium-based lead-free glass powder and its preparation method and application
  • A kind of vanadium-based lead-free glass powder and its preparation method and application
  • A kind of vanadium-based lead-free glass powder and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0021] Specific implementation mode one: this implementation mode is a kind of vanadium-based lead-free glass powder with 40 parts to 75 parts V by weight. 2 o 5 , 2 to 8 copies of Bi 2 o 3 , 3~6 copiesP 2 o 5 , 1 to 8 copies B 2 o 3 , 1 to 5 parts of SiO 2 , 0 to 3 parts of Na 2 O, 0 to 2 parts of Cu 2 O, 2 to 8 parts of ZnO, 1 to 5 parts of Al 2 o 3 , 0 to 3 parts of TiO 2 , 0 to 3 parts of Sb 2 o 3 , 0 to 3 Li 2 O and 0 to 1 part of Ag 2 O prepared.

specific Embodiment approach 2

[0022] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that a vanadium-based lead-free glass powder consists of 40 parts to 55 parts by weight of V 2 o 5 , 6 to 8 copies of Bi 2 o 3 , 4~6 copiesP 2 o 5 , 1 to 4 copies B 2 o 3 , 2 to 5 parts of SiO 2 , 1 to 3 parts of Na 2 O, 1-2 parts of Cu 2 O, 2 to 4 parts of ZnO, 3 to 5 parts of Al 2 o 3 , 2 to 3 parts of TiO 2 , 1 to 2 parts of Sb 2 o 3 , 1 to 2 Li 2 O and 0.5-1 part of Ag 2 O prepared. Other steps are the same as in the first embodiment.

specific Embodiment approach 3

[0023] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is that: a vanadium-based lead-free glass powder consists of 50 parts by weight of V 2 o 5 , 6 Bi 2 o 3 , 5 copies of P 2 o 5 , 4 copies of B 2 o 3 , 3 parts of SiO 2 , 2 Na 2 O, 2 parts of Cu 2 O, 3 parts ZnO, 2 parts Al 2 o 3 , 1 part of TiO 2 , 1 part of Sb 2 o 3 , 1 Li 2 O and 1 part Ag 2 O prepared. Other steps are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

A vanadium-based lead-free glass powder and its preparation method and application, which relate to a glass powder and its preparation method and application. The purpose of the present invention is to solve the high glass transition temperature and large particle size of the glass frit used in the existing preparation of lead-free paste, the price of lead-free paste is expensive, it is not conducive to large-scale production, and the existing paste is used The problem of low conversion efficiency of solar cells. Vanadium-based lead-free glass powder is composed of V 2 o 5 、 Bi 2 o 3 ,P 2 o 5 , B 2 o 3 , SiO 2 、Na 2 O, Cu 2 O, ZnO, Al 2 o 3 、TiO 2 , Sb 2 o 3 , Li 2 O and Ag 2 O prepared. Methods: 1. Weighing; 2. Mixing; 3. Melting; 4. Quenching; 5. Grading. Vanadium-based lead-free glass powder is used to prepare front silver paste for crystalline silicon solar cells. The invention can obtain a vanadium-based lead-free glass powder.

Description

technical field [0001] The invention relates to a glass powder and its preparation method and application. Background technique [0002] With the increasing global energy demand, global warming and environmental pollution, countries are increasingly looking for alternative energy sources. Because solar energy is the only inexhaustible energy source in the world. People are beginning to turn their attention to clean and renewable energy sources such as solar energy. Lead-free crystalline silicon solar cells are one of the main ways of solar energy applications. Under the action of light, the crystalline silicon solar cell converts solar energy into electrical energy through silver grid lines, and the surface electrodes and silver grid lines are made of conductive silver paste. However, the conductive paste used in traditional crystalline silicon solar cells contains lead paste, which pollutes the environment during the production process. At the same time, the glass powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C12/00C03C6/04C03B5/16C03B19/00H01L31/0224H01B1/20
CPCC03C12/00C03C1/00C03B5/16C03B19/00H01L31/022425H01B1/20Y02E10/50
Inventor 王惠白晋涛崔春婷
Owner 江苏聚盈新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More