Preparation method of superhydrophilic/underwater superoleophobic modified substrate material

An underwater super-oleophobic and base material technology, applied in the field of polymer materials, can solve the problems of many steps, harsh chemical conditions, and complicated, etc., and achieve the effect of stable coating, easy to obtain, and simple coating process

Active Publication Date: 2022-07-22
SUZHOU UNIV OF SCI & TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current method has certain defects, such as many and complicated steps, harsh chemical conditions or unstable modified coating, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of superhydrophilic/underwater superoleophobic modified substrate material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The present invention provides a method for preparing a superhydrophilic / underwater superoleophobic modified base material, which comprises the following steps:

[0026] Step 1, respectively preparing a certain concentration of styrene maleic anhydride copolymer solution and polyethyleneimine solution;

[0027] Step 2: Immerse the base material in the styrene maleic anhydride copolymer solution for a certain period of time, take it out and drain, then immerse it in the polyethyleneimine solution for a certain period of time, take out and drain it, and clean it with water to obtain a superhydrophilic / underwater solution. Modified substrate material with superoleophobic properties.

[0028] In step 1, the described styrene maleic anhydride copolymer solution is a solution formed by dissolving styrene maleic anhydride copolymer in tetrahydrofuran, N,N-dimethylformamide or acetone solvent, and its solution concentration is 0.1 -30% (wt%).

[0029] In step 1, the polyethyl...

Embodiment 1

[0037] A method for preparing a modified stainless steel screen with super-hydrophilic / underwater super-oleophobic properties that can be used for the treatment of oily wastewater, comprising the following steps:

[0038] (1) dissolving styrene maleic anhydride copolymer with a molecular weight of 1600 g / mol in N,N-dimethylformamide to prepare a 2% polymer solution;

[0039] (2) dissolving polyethyleneimine with a molecular weight of 10000 g / mol in deionized water to prepare a 2% polymer solution;

[0040] (3) Immerse the stainless steel mesh in the styrene maleic anhydride copolymer solution, stay for 10s, take out the drained solution, continue to immerse it in the polyethyleneimine solution, stay for 30min, take out the drained solution, and wash it with water.

Embodiment 2

[0042] A preparation method of a modified nylon mesh having super-hydrophilic / underwater super-oleophobic properties and can be used for the treatment of oily wastewater, comprising the following steps:

[0043] (1) dissolving a styrene maleic anhydride copolymer with a molecular weight of 1700 g / mol in tetrahydrofuran to prepare a 2% polymer solution;

[0044] (2) dissolving polyethyleneimine with a molecular weight of 5000 g / mol in deionized water to prepare a 2% polymer solution;

[0045] (3) Immerse the nylon mesh in the styrene maleic anhydride copolymer solution, stay for 20s, take out the drained solution, continue to immerse it in the polyethyleneimine solution, stay for 60min, take out the drained solution, and wash it with water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for quickly and easily preparing a superhydrophilic / underwater superoleophobic modified base material by using a commercial polymer. Specifically, the following methods and steps can be used to separately prepare a styrene maleic anhydride copolymer solution and a polyethyleneimine solution with a certain concentration; immerse the base material in the styrene maleic anhydride copolymer solution for a certain period of time, take it out and drain it, and then immerse it in a polyethyleneimine solution. In the ethyleneimine solution for a certain period of time, after being taken out and drained, the modified base material with superhydrophilic / underwater superoleophobic properties is obtained by washing with water. The method disclosed in the present invention greatly improves the superhydrophilic / submerged superoleophobic modification of the base material, and is suitable for emulsified oil separation.

Description

technical field [0001] The invention belongs to the field of polymer materials, in particular to a method for quickly and easily preparing a superhydrophilic / underwater superoleophobic modified base material by using a commercial polymer. Background technique [0002] Growing energy consumption has created a very large demand for the petrochemical industry, which is estimated to have reached 88 billion gallons of petroleum products annually throughout the world. At present, because many oil fields in the world are already in the middle and late stages of exploitation, the crude oil produced has high water content; crude oil pollution accidents caused by leakage from drilling platforms, oil tanks or oil tanker transportation occur frequently every year; oil refining, oil processing, edible oil Oil generation, metalworking, and other related industries generate large amounts of oily wastewater. Oily wastewater can alter soil physicochemical properties, affect drinking water q...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/233D06M15/61C08J9/42B01D69/02B01D71/34B01D61/14B01D67/00B01D39/10D06M101/06D06M101/34C08L27/16
CPCD06M15/233D06M15/61C08J9/42B01D69/02B01D71/34B01D61/147B01D67/0088B01D39/10D06M2101/06D06M2101/34C08J2327/16B01D2325/36B01D2239/0421B01D2239/10
Inventor 张干伟邢佳乐贾新应白仁碧沈舒苏周晓吉杨晶晶
Owner SUZHOU UNIV OF SCI & TECH