Method for preparing microlite from ceramic waste and microlite

A technology of ceramic waste and microcrystalline stone, applied in the field of methods and microcrystalline stone, can solve the problems that microcrystalline stone cannot be produced, and achieve the effect of high flatness and high whiteness

Inactive Publication Date: 2020-01-07
江西飞宇新能源科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The main purpose of the present invention is to provide a method of using ceramic waste to make microcrystalline stone and microcrystalline stone, aiming to solve the problem that ceramic waste cannot be used to make microcrystalline stone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing microlite from ceramic waste and microlite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] Take 60g of ceramic waste and crush it into 50 meshes, mix it with 11g of calcite powder, 3g of soda ash powder, 10g of quartz powder and 3g of red colored sand powder, and put it into the furnace after mixing evenly. After 2.5 hours of melting treatment, the molten liquid is obtained, and it enters the flow channel through the flow channel inlet, and a forming vessel filled with water is placed at the flow channel outlet, and water is sprayed on the outer wall of the channel at the same time, so that the molten liquid flows from the flow channel inlet. When it enters and flows out from the outlet of the runner, it can cool down to 1000°, and drop into the forming vessel from the outlet of the runner to form microcrystalline particles, and then put the microcrystalline particles into the crystallization mold and put them into the crystallization kiln Among them, the sintering temperature is 1000°, and the sintering time is 2 hours to obtain the molten crystallization liq...

Embodiment 2

[0055] Take 70g of ceramic waste and crush it into 200 mesh, mix it with 5g of calcite powder, 2g of soda ash powder, 20g of quartz powder and 5g of yellow colored sand powder, and put it into the furnace after mixing evenly. After melting for 1.5 hours, the molten liquid is obtained, and it enters the flow channel through the flow channel inlet, and a forming vessel filled with water is placed at the flow channel outlet, and water is sprayed on the outer wall of the channel at the same time, so that the molten liquid flows from the flow channel inlet When it enters and flows out from the outlet of the runner, it can cool down to 1100°, and drop into the forming vessel from the outlet of the runner to form microcrystalline particles, and then put the microcrystalline particles into the crystallization mold and put them into the crystallization kiln Among them, the sintering temperature is 1200°, and the sintering time is 3 hours to obtain the molten crystallization liquid, and ...

Embodiment 3

[0057] Take 80g of ceramic waste and crush it into 350 meshes, mix it with 8g of calcite powder, 1g of soda ash powder, 30g of quartz powder and 4g of blue colored sand powder, mix them evenly, put them into a furnace, and melt them at a melting temperature of 1600° The melting time is 2 hours, and the molten liquid is obtained after the melting treatment, which enters the flow channel through the inlet of the flow channel, and a forming vessel filled with water is placed at the outlet of the flow channel, and water is sprayed on the outer wall of the channel at the same time, so that the molten liquid flows from the flow channel When the inlet enters and flows out from the outlet of the flow channel, it can cool down to 1200°, and drop into the forming vessel from the outlet of the flow channel to form microcrystalline particles, and then put the microcrystalline particles into the crystallization mold and put them into the crystallization mold. In the kiln, the sintering temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing microlite from ceramic waste and the microlite, which comprises the following steps: pulverizing the ceramic waste to obtain waste fine powder; uniformlymixing the waste fine powder and other components in parts by mass as follows: 60-80 parts of the waste fine powder, 5-11 parts of calcite powder, 1-3 parts of soda ash powder, 10-30 parts of quartzpowder and 3-5 parts of colored sand powder to obtain mixed powder. According to the microlite provided by the invention, the ceramic tailings, calcite, soda ash and quartz powder are adopted to prepare the microlite; according to the method, the potassium element, the calcium element, the aluminum element and the silicon element in the ceramic tailings can be utilized to prepare the microlite, the ceramic tailings can be recycled, the environment is protected while the waste is utilized, and the microlite prepared by adopting the method is high in whiteness and planeness.

Description

technical field [0001] The invention relates to a method for preparing microcrystalline stones, in particular to a method for making microcrystalline stones by using ceramic waste and the microcrystalline stones. Background technique [0002] With the rapid development of social economy, ceramic industry wastes are increasing day by day, which puts great pressure on the urban environment, so the treatment and utilization of ceramic industry wastes is very important. At present, the treatment and utilization of ceramic industry waste in my country is relatively low, and funds are in short supply, resulting in a large amount of waste slag occupying cultivated land, polluting water and air, and a large amount of ceramic waste is no longer a problem that can be solved simply by landfilling. Therefore, it has become an urgent task for science and technology and environmental protection departments to pay attention to the recycling and reuse of ceramic waste, improve the technolog...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C10/00C03C6/04
CPCC03C1/002C03C10/0063
Inventor 魏绪春魏东东廖新
Owner 江西飞宇新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap