Preparation method of cellulose diacetate fiber for textile

A technology of cellulose diacetate and fiber, which is applied in the field of preparation of cellulose diacetate fiber for textiles, can solve the problems of zero research on diacetate fiber short filaments, increased environmental protection costs, and environmental hazards, so as to reduce curl damage and alleviate Effects with low intensity and little environmental impact

Active Publication Date: 2021-06-04
HUBEI XINYANG SPECIAL FIBER CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The long / short triacetate fiber uses di / chloroform as a solvent, which seriously endangers the environment, and the cost of environmental protection is increasing day by day.
Moreover, my country has conducted in-depth research on tobacco tow. There are professional research institutes and more than 10 manufacturers, but the research on short diacetate fibers for textiles is almost zero. At present, there is no enterprise commercially producing acetate fibers. Short filament

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The preparation method of cellulose diacetate fiber for weaving comprises the following steps:

[0030] 1) Prepare the spinning slurry according to the solid-liquid ratio of 30:70; the solid phase is cellulose diacetate and wood pulp fiber, and the mass ratio of the two is 99.92:0.08; the liquid phase is a mixed solution of acetone, water and internal lubricant, The mass ratio of acetone, water, and internal lubricant in the liquid phase is 94.7:5:0.3; the solid-liquid two-phase is mixed evenly by high-shear stirring for 8 hours, and the viscosity of the slurry is about 180 Pa·s at 50 °C. Wherein the number-average molecular weight of cellulose diacetate is 45000, and the acetyl value is 53.5; the average length of wood pulp fiber is 3800 microns, and the internal lubricant is 10# white oil.

[0031] 2) The spinning slurry is filtered by a filter press for secondary filtration, in which the primary filter is 85kg of pre-coated wood pulp, the pre-coating concentration is...

Embodiment 2

[0035] The preparation method of cellulose diacetate fiber for weaving comprises the following steps:

[0036] 1) Prepare the spinning slurry according to the solid-liquid ratio of 29:71; the solid phase is cellulose diacetate and wood pulp fiber, and the mass ratio of the two is 99.94:0.06; the liquid phase is a mixed solution of acetone, water and internal lubricant, The mass ratio of acetone, water and internal lubricant in the liquid phase is 94.7:4.5:0.2; the solid and liquid phases are mixed evenly by high-shear stirring for 8 hours, and the viscosity of the slurry is about 175 Pa·s at 50 °C. Wherein the number-average molecular weight of cellulose diacetate is 43,000, and the acetyl value is 53.4; the average length of wood pulp fibers is 3,200 microns, and the internal lubricant is 26# white oil.

[0037] 2) The spinning slurry is filtered by a filter press for secondary filtration, wherein the primary filter is pre-coated wood pulp 100kg, pre-coated concentration 1.5%...

Embodiment 3

[0041] The preparation method of cellulose diacetate fiber for weaving comprises the following steps:

[0042] 1) Prepare the spinning slurry according to the solid-liquid ratio of 30:70; the solid phase is cellulose diacetate and wood pulp fiber, and the mass ratio of the two is 99.96:0.04; the liquid phase is a mixed solution of acetone, water and internal lubricant, The mass ratio of acetone, water, and internal lubricant in the liquid phase is 94.7:5:0.3; the solid-liquid two-phase is mixed evenly by high-shear stirring for 6 hours, and the viscosity of the slurry is about 165 Pa·s at 50 °C. Wherein the number-average molecular weight of cellulose diacetate is 42,000, and the acetyl value is 53.5; the average length of wood pulp fibers is 2,900 microns, and the internal lubricant is 10# white oil.

[0043] 2) The spinning slurry is filtered by a filter press for secondary filtration, in which the primary filter is pre-coated wood pulp 100kg, pre-coated concentration 1%, pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of cellulose diacetate fiber for textile, 1) adopting solid phase and liquid phase to prepare spinning slurry; wherein the solid phase is cellulose diacetate and wood pulp fiber, and the liquid phase is acetone, water and The mixed solution of the internal lubricant; the solid-liquid two-phase is stirred and mixed evenly to obtain the spinning slurry; 2) the spinning slurry is filtered by a filter press, and the pressure difference is as low as 0.1‑0.3MPa, and the obtained filtrate is subjected to the second stage Filtration; 3) Pressurize and heat the filtrate obtained in step 2) to 1.0Mpa and above 59°C, and then perform dry spinning after passing through a candle filter and a precision metering pump. During the spinning process, flash spinning technology is used , the draft ratio is 1.5-2.0; 4) crimping the formed fiber after spinning in step 3) to obtain cellulose diacetate fiber. By adopting the above method, the industrialization of the cellulose diacetate fiber for textile can be realized, and the short fiber with high strength and low denier can be produced.

Description

technical field [0001] The invention belongs to the field of diacetate fiber spinning, in particular to a preparation method of cellulose diacetate fiber for textile. Background technique [0002] At present, diacetate cellulose tow for cigarettes is in a saturated state in the world. As the number of smokers decreases and the output of cigarettes decreases, the tobacco tow industry needs transformation and upgrading to improve the competitiveness of enterprises. With viscose fiber production causing serious environmental pollution, the demand for triacetate / diacetate fiber textile raw materials is increasing day by day. The long / short triacetate fiber uses di / chloroform as a solvent, which seriously endangers the environment, and the cost of environmental protection is increasing day by day. The performance of diacetate fiber textile materials is similar to that of triacetate fiber, but in terms of demand, it is mainly short yarn, which is blended with polyester and spand...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01D1/02D01D1/10D01D5/04D01D5/084D01D5/096D01F2/30D01F1/10
CPCD01D1/02D01D1/106D01D5/04D01D5/084D01D5/096D01F1/10D01F2/30
Inventor 叶小波叶兆清冯明华黄爱成周全林冯艳洲
Owner HUBEI XINYANG SPECIAL FIBER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com