High-temperature-resistant composite reinforced gel plugging agent and preparation method thereof

A technology of loss-stopping agent and high temperature resistance, which is applied in the field of drilling fluid plugging, can solve the problems of difficulty in entering the leakage layer, failure of plugging cracks and pores, and insufficient residence time, etc. Effective blocking time and good rigidity

Active Publication Date: 2020-01-31
RES INST OF SHAANXI YANCHANG PETROLEUM GRP
View PDF13 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently adopted gel plugging technology has achieved relatively good results in field application, but there are still problems that the gel particles absorb water and expand too fast, making it difficult for the plugging agent to enter the leakage layer; the temperature resistance is i

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant composite reinforced gel plugging agent and preparation method thereof
  • High-temperature-resistant composite reinforced gel plugging agent and preparation method thereof
  • High-temperature-resistant composite reinforced gel plugging agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The preparation of cross-linking agent WEG comprises steps:

[0058] (1) hydroxyethyl methacrylate and α-methylstyrene (mass ratio 4:1) monomer and 1g tert-butyl peroxybenzoate were dispersed in deionized water of 15ml and 5ml respectively with a total mass of 10g, Obtain solutions A and B;

[0059] (2) The required surfactant Maize 49 (polyoxyethylene stearate) and glyceryl monostearate are mixed in a mass ratio of 5:15 for a total of 40g to obtain a composite surfactant; The active agent was dissolved in 160ml of methylcyclohexane at 60°C to obtain a microemulsion;

[0060] (3) Using the dropping method, solution A and solution B are respectively added dropwise to the microemulsion successively. After the dropwise addition, continue to stir with a magnetic stirrer at a rate of 400r / min and react at a constant temperature of 60°C for 4h to obtain the microemulsion; to the microemulsion 2 g of dibenzoyl peroxide was added to the mixture, high-pressure nitrogen gas was...

Embodiment 2

[0062] A high-temperature-resistant composite strengthened gel plugging agent, which is prepared from the following raw materials in parts by mass: 20 parts of copolymerized reaction monomers; 1.0 parts of cross-linking agent WEG prepared by the method in Example 1; 0.2 parts of initiator; resin-based support Granules 1.0 parts.

[0063] The copolymerization reaction monomer is hydroxyethyl methacrylate, dimethylaminoethyl methacrylate and β-hydroxyethyl methacrylate, and the mass ratio is 4:2:1; the initiator is peroxygen Compound initiator cumene hydroperoxide; The resin-based support particles are boron phenolic resin particles (spherical particles, the average particle diameter is 32 μm, and the density is 1.41 g / cm 3 ) and bismaleimide resin particles (spherical particles with an average particle size of 30 μm and a density of 1.43 g / cm 3 ) combination, the mass ratio of boron phenolic resin particles and bismaleimide resin particles is 2:1.

[0064] The preparation met...

Embodiment 3

[0067] A high-temperature-resistant composite reinforced gel plugging agent, which is prepared from the following raw materials in parts by mass: 20 parts of copolymerized reaction monomers; 2.0 parts of crosslinking agent WEG prepared by the method in Example 1; 0.2 parts of initiator; resin-based support Granules 1.5 parts.

[0068] The copolymerization reaction monomer is hydroxyethyl methacrylate, dimethylaminoethyl methacrylate and β-hydroxyethyl methacrylate, and the mass ratio is 4:2:1; the initiator is peroxygen Compound initiator cumene hydroperoxide; The resin-based support particles are boron phenolic resin particles (spherical particles, the average particle diameter is 32 μm, and the density is 1.41 g / cm 3 ) and bismaleimide resin particles (spherical particles with an average particle size of 30 μm and a density of 1.43 g / cm 3 ) combination, the mass ratio of boron phenolic resin particles and bismaleimide resin particles is 2:1.

[0069] The preparation method...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Densityaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-temperature-resistant composite reinforced gel plugging agent and a preparation method thereof. The gel plugging agent is prepared from the following raw materials in parts by mass: 15-35 parts of a copolymerization monomer; 1.0 to 2.0 parts of cross-linking agent WEG; 0.1 to 0.5 part of an initiator; and 0.5 to 2.0 parts of resin-based support particles; wherein thecopolymerization monomer is a combination of three or more than three components selected from polyoxyethylene ether, hydroxyethyl methacrylate, dimethylaminoethyl methacrylate, 2-ethyl methacrylate,beta-hydroxyethyl methacrylate or N-vinyl pyrrolidone. The plugging agent provided by the invention has the characteristics of high temperature resistance and delayed expansion, can fully and smoothlyenter stratum cracks, and achieve the purpose of effectively plugging crack pores.

Description

technical field [0001] The invention relates to a high-temperature-resistant composite reinforced gel plugging agent and a preparation method thereof, belonging to drilling fluid plugging technology in the field of petroleum exploration and development. Background technique [0002] Lost circulation is a common phenomenon in the process of oil drilling. According to statistics, the occurrence rate of lost circulation accounts for 20% to 25% of the total number of wells in the world. Lost circulation will not only cause huge economic losses to the drilling project, but also lead to a serious drop in well pressure, which will have a great impact on the stability of the inner wall of the oil well. In severe cases, it will lead to blowout accidents, which seriously threaten the safety of drilling operations. sex. In recent years, as the exploration and development of oil and gas resources continue to deepen into the formation, the problem of lost circulation has been paid more ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09K8/44
CPCC09K8/44
Inventor 李伟王波张文哲李红梅王涛
Owner RES INST OF SHAANXI YANCHANG PETROLEUM GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap