Antirust agent used for manufacturing road lamp pole and preparation method thereof

A technology of antirust agent and street light pole, which is applied in the field of antirust agent production, can solve problems such as not being very environmentally friendly, and achieve excellent environmental protection performance

Inactive Publication Date: 2020-02-04
江苏飞腾光电科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional antirust agents contain heavy metals such as lead, which are not very environmentally friendly. In today's society, the requirements for environmental protection are becoming more and more stringent. An environmentally friendly antirust agent is the general trend

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An antirust agent for the manufacture of street light poles is characterized in that, in terms of weight percentage, it comprises the following components: 30% phosphoric acid, 5% zinc sulfate, 1.8% petroleum ether, 0.8% lanolin antirust agent, polyhydric alcohol 0.3%, the remainder is water, and the lanolin rust inhibitor is lanolin magnesium soap rust inhibitor.

[0018] A kind of preparation technology for the antirust agent that street light pole is made, carries out as follows:

[0019] (A) mixing sherwood oil and polyhydric alcohol;

[0020] (B) Carry out a heating and preheating procedure, wherein the temperature is 50°C and the preheating time is 10 minutes;

[0021] (C) add lanolin antirust agent, mix with water;

[0022] (D) Filtration procedures are performed to obtain finished antirust agents for lamp pole manufacture.

Embodiment 2

[0024] An antirust agent for the manufacture of street light poles, characterized in that, in terms of weight percentage, it contains the following components: 45% phosphoric acid, 15% zinc sulfate, 1.8% petroleum ether, 1% lanolin antirust agent, polyol 1%, the rest is water, lanolin rust inhibitor is lanolin magnesium soap rust inhibitor.

[0025] A kind of preparation technology for the antirust agent that street light pole is made, carries out as follows:

[0026] (A) mixing sherwood oil and polyhydric alcohol;

[0027] (B) Carry out heating and preheating procedures, wherein the temperature is 75°C and the preheating time is 30 minutes;

[0028] (C) add lanolin antirust agent, mix with water;

[0029] (D) Filtration procedures are performed to obtain finished antirust agents for lamp pole manufacture.

Embodiment 3

[0031] An antirust agent for the manufacture of street light poles is characterized in that, in terms of weight percentage, it contains the following components: 30% phosphoric acid, 15% zinc sulfate, 1.8% petroleum ether, 0.8% lanolin antirust agent, polyol 0.5%, the rest is water, lanolin rust inhibitor is lanolin magnesium soap rust inhibitor.

[0032] A kind of preparation technology for the antirust agent that street light pole is made, carries out as follows:

[0033] (A) mixing sherwood oil and polyhydric alcohol;

[0034] (B) Carry out heating and preheating procedures, wherein the temperature is 60°C and the preheating time is 20 minutes;

[0035] (C) add lanolin antirust agent, mix with water;

[0036] (D) Filtration procedures are performed to obtain finished antirust agents for lamp pole manufacture. The antirust agent used in the manufacture of street light poles of the present invention adopts phosphoric acid, zinc sulfate, petroleum ether, lanolin antirust ag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antirust agent used for manufacturing a road lamp pole and a preparation method thereof. The antirust agent comprises the following components of, in percentage by weight, phosphoric acid 30 to 45%, zinc sulfate 5 to 15%, petroleum ether 1.5 to 2%, a lanolin antirust agent 0.5 to 1%, polyol 0.3 to 1%, and the balance water. The preparation method of the antirust agent comprises the following steps that (A), the petroleum ether and the polyol are mixed; (B) heating and preheating procedures are carried out, wherein the temperature is 50 DEG C to 75 DEG C and the preheating time is 10 to 30 minutes; (C) the lanolin antirust agent is added and is mixed with water evenly; and (D) the filtering procedure is executed to obtain the finished antirust agent used for manufacturing the road lamp pole. According to the antirust agent used for manufacturing the road lamp pole, the phosphoric acid, the zinc sulfate, the petroleum ether, the lanolin antirust agent, the polyol and water are adopted and lead and other heavy metals are not adopted, so that the material is very environmentally friendly, and the antirust agent produced has excellent environmental protectionperformance.

Description

technical field [0001] The invention relates to the field of antirust agent production, in particular to an antirust agent used for manufacturing street light poles and a preparation method thereof. Background technique [0002] Metal processing parts are easy to rust during the production, processing and transportation. This requires the use of anti-rust oil to form a film on the metal surface to prevent metal corrosion. The anti-rust agent uses high-quality anti-corrosion raw materials and various additives. Processed with anti-corrosion agent, it can protect the surface from moisture, chemicals, air and other corrosive products. It is an environmentally friendly product. It can be widely used in inter-process rust prevention of steel, stainless steel, alloy steel product components and materials in various industries. [0003] Traditional antirust agents contain heavy metals such as lead, which are not very environmentally friendly. In today's society, the requirements ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23F11/10C23F11/18
CPCC23F11/10C23F11/188
Inventor 李卫松胡恒全
Owner 江苏飞腾光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap