Discoloring body having glossiness
A technology of discoloration and gloss, applied in the field of discoloration, can solve the problem of difficult to reflect the uniform brightness of the surface, and achieve the effect of excellent applicability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 101
[0086] Example 101 (with reference to figure 1 )
[0087] In the white T / C (65 / 35) wide material (unit area weight: 120g / cm2) that is used as the support body 12 2 ), the colored layer 13 is formed by solid printing on the entire surface using pink non-discoloration ink. Next, on the colored layer 13, 15 parts of wet-process silicic acid [trade name: Nipponsil E-200, manufactured by Nippon Silicon Industry Co., Ltd.], 30 parts of polyurethane emulsion [trade name: Highland HW-930, manufactured by Dainippon Ink Co., Ltd. Chemical Industry Co., Ltd., solid content 50%], 40 parts of water, 0.5 parts of silicone-based defoamer, 3 parts of thickener for water-based ink, 1 part of ethylene glycol, 3 parts of blocked isocyanate cross-linking agent The mixed and stirred white screen printing ink was solid-printed on the entire surface with a 100-mesh screen plate, and dried and cured at 130° C. for 5 minutes to form the porous layer 14 . In addition, on a release sheet made of a po...
Embodiment 102
[0092] In the white T / C (65 / 35) wide material (weight per unit area: 120g / cm2) as a support 2 ) using four-color non-discoloration inks consisting of pink, orange, blue, and light green to form a wavy colored layer (ribbon-shaped colored image) in which 1 cm wide curved ribbon-shaped images are arranged adjacent to each other. Next, on the colored layer, 15 parts of wet-process silicic acid [trade name: Nipponsil E-200, manufactured by Nippon Silicon Industry Co., Ltd.], 30 parts of polyurethane emulsion [trade name: Highland HW-930, manufactured by Dainippon Ink Chemical Co., Ltd. Kogyo Co., Ltd., solid content 50%], 40 parts of water, 0.5 parts of silicone-based defoamer, 3 parts of thickener for water-based ink, 1 part of ethylene glycol, and 3 parts of blocked isocyanate crosslinking agent are uniformly mixed The stirred white ink for screen printing was solid-printed on the entire surface with a 100-mesh screen plate, and dried and cured at 130° C. for 5 minutes to form a...
Embodiment 103
[0097] In the white polyester taffeta fabric as the support (weight per unit area: 80g / cm 2 ), using blue non-discoloration ink, solid printing is performed on the entire surface to form a colored layer. Next, on the colored layer, 15 parts of wet-process silicic acid [trade name: Nipponsil E-200, manufactured by Nippon Silicon Industry Co., Ltd.], 30 parts of polyurethane emulsion [trade name: Highland HW-930, manufactured by Dainippon Ink Chemical Co., Ltd. Kogyo Co., Ltd., solid content 50%], 40 parts of water, 0.5 parts of silicone-based defoamer, 3 parts of thickener for water-based ink, 1 part of ethylene glycol, and 3 parts of blocked isocyanate crosslinking agent are uniformly mixed The stirred white ink for screen printing was solid-printed on the entire surface with a 100-mesh screen plate, and dried and cured at 130° C. for 5 minutes to form a porous layer. In addition, on a release sheet made of a polyethylene terephthalate resin film with a thickness of 25 μm coa...
PUM
| Property | Measurement | Unit |
|---|---|---|
| Thickness | aaaaa | aaaaa |
| Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More