Corrugated paper pulp with waterproof and fireproof characteristics

A pulp and corrugated technology, applied in the field of corrugated pulp and its production, can solve the problems of corrugated cartons such as fire prevention, waterproof, moisture resistance, high temperature resistance and poor flame retardancy, and achieve excellent pulp raw materials, simple production methods and good quality effects

Inactive Publication Date: 2020-02-18
鲍双铭
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The fireproof, waterproof, moistureproof, high temperature resistance and poor flame retardancy of corrugated boxes have always been the defects that have been criticized by the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A formulation of corrugated paper pulp with waterproof and fireproof properties, comprising the following components in parts by weight: 45 parts of plant fibers, 40 parts of ceramic fibers, 20 parts of aluminum hydroxide, 20 parts of ammonium chloride, 10 parts of rosin gum, and 20 parts of starch parts, 10 parts of chlorinated paraffin, 10 parts of titanium trioxide, 10 parts of silicone oil, 20 parts of flame retardant, 20 parts of titanium dioxide, 30 parts of polyvinyl alcohol, 20 parts of latex, 20 parts of hydrophobic agent, 1 part of paraffin, softening 10 servings and the right amount of water and the right amount of vegetable oil.

[0020] According to above-mentioned formula, the preparation method of described corrugated paper pulp is:

[0021] Step 1: First, add 45 parts of plant fiber and 40 parts of ceramic fiber into the mixer and mix it evenly;

[0022] Step 2: Add 10 parts of rosin gum and 20 parts of starch to the mixer, and mix them evenly with the ...

Embodiment 2

[0029] A formulation of corrugated paper pulp with waterproof and fireproof properties, comprising the following components in parts by weight: 60 parts of plant fibers, 50 parts of ceramic fibers, 30 parts of aluminum hydroxide, 30 parts of ammonium chloride, 20 parts of rosin gum, and 30 parts of starch parts, 20 parts of chlorinated paraffin, 20 parts of titanium trioxide, 20 parts of silicone oil, 30 parts of flame retardant, 30 parts of titanium dioxide, 40 parts of polyvinyl alcohol, 30 parts of latex, 30 parts of hydrophobic agent, 10 parts of paraffin, softening 20 servings of the medicine and the right amount of water and the right amount of vegetable oil.

[0030] According to above-mentioned formula, the preparation method of described corrugated paper pulp is:

[0031] Step 1: First, add 60 parts of plant fiber and 50 parts of ceramic fiber into the mixer and mix it evenly;

[0032] Step 2: Add 20 parts of rosin gum and 30 parts of starch to the mixer, and mix the...

Embodiment 3

[0039] The corrugated paper pulp prepared by the method for producing corrugated paper pulp is put into a mold to form, and the obtained corrugated cardboard can be grilled at a flame temperature of 1000-1600 degrees without burning.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses corrugated paper pulp with waterproof and fireproof characteristics, and belongs to the technical field of papermaking. The corrugated paper pulp comprises plant fibers, ceramic fibers, aluminum hydroxide, ammonium chloride, rosin size, starch, chlorinated paraffin, dititanium trioxide, silicone oil, a flame retardant, titanium dioxide, polyvinyl alcohol, latex, a water repellent agent, paraffin, a softener, water and vegetable oil. A preparation method comprises the steps: firstly, uniformly stirring the plant fibers and the ceramic fibers, adding the rosin size and the starch into the mixture, and uniformly stirring; then adding an aqueous solution of aluminum hydroxide and ammonium chloride, and uniformly stirring; adding silicone oil, chlorinated paraffin and adititanium trioxide solution, and uniformly stirring; adding the flame retardant, titanium dioxide and water, and uniformly stirring; uniformly stirring the polyvinyl alcohol solution, the latex and ahydrophobic agent solution, adding a solution formed by paraffin, the softener and a proper amount of water into the obtained solution, and uniformly stirring to form the corrugated paper pulp. Corrugated board prepared from the corrugated paper pulp has the characteristics of fire resistance, flame retardancy, high temperature resistance, water resistance and moisture resistance.

Description

technical field [0001] The invention belongs to the technical field of papermaking, and more particularly relates to a corrugated pulp with flame-retardant, waterproof, fire-proof, high-temperature resistance properties and a preparation method thereof. Background technique [0002] Corrugated box is one of the most widely used packaging products, and its dosage has always been the first of various packaging products. For more than half a century, corrugated boxes have gradually replaced wooden boxes and other transportation packaging containers with their superior performance and good processing performance, and have become the main force of transportation packaging. The fireproof, waterproof, moisture-proof, high temperature resistance and poor flame retardancy of corrugated boxes have always been the defects that have been criticized by the market. SUMMARY OF THE INVENTION [0003] The purpose of the present invention is to overcome the deficiencies existing in the pri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H11/00D21H13/38D21B1/34
CPCD21H11/00D21H13/38D21B1/34
Inventor 鲍双铭金乌兰
Owner 鲍双铭
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap