A kind of acid-resistant strong gel plugging agent and preparation method thereof

A strong gel and plugging agent technology, which is applied in the direction of chemical instruments and methods, drilling compositions, etc., can solve the problem of low acid resistance of plugging agents, and achieve the effects of strong plugging performance, not easy to dehydrate, and wide sources

Active Publication Date: 2022-02-01
BC P INC CHINA NAT PETROLEUM CORP +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the acid resistance of plugging agents researched and developed in my country is generally not high, especially the research on acid-resistant strong gel plugging agents suitable for combined operation of water plugging and acidification in low permeability reservoirs is almost blank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of acid-resistant strong gel plugging agent and preparation method thereof
  • A kind of acid-resistant strong gel plugging agent and preparation method thereof
  • A kind of acid-resistant strong gel plugging agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] An acid-resistant strong gel plugging agent, in terms of weight percentage, its components are:

[0038] Main agent: 3-10%;

[0039] Acid resistant monomer: 0.1-1.0%;

[0040] Initiator: 0.1-0.5%;

[0041] Cross-linking agent: 0.5%-1.5%.

[0042] An acid-resistant strong gel plugging agent is prepared by the following method, comprising the following steps

[0043] Step 1: Take the main ingredient of the formula first, put it in a heat-resistant HDPE bottle, put the heat-resistant HDPE bottle on a magnetic stirrer, and stir evenly.

[0044] Step 2: On the basis of Step 1, add the formula amount of acid-resistant monomer, and stir until it is uniform and transparent.

[0045] Step 3: On the basis of Step 2, add a crosslinking agent and an initiator, stir evenly, and place the evenly stirred solution in a constant temperature oven to form a gel.

Embodiment 2

[0047] An acid-resistant strong gel plugging agent, in terms of weight percentage, its components are:

[0048] Main ingredient: 3%;

[0049] Acid resistant monomer: 0.1%;

[0050] Initiator: 0.1%;

[0051] Cross-linking agent: 0.5%.

[0052] The main agent is one of acrylamide, acrylonitrile and acrylic acid or a mixture thereof.

[0053] The acid-resistant monomers are acrylic esters containing fluorine groups.

[0054] The initiator is one of potassium persulfate, ammonium persulfate and azobisisobutyronitrile or a mixture thereof.

[0055] The crosslinking agent is one of N,N-methylenebisacrylamide and polyethyleneimine or a mixture thereof.

[0056] An acid-resistant strong gel plugging agent is prepared by the following method, comprising the following steps

[0057] Step 1: Take 3% acrylonitrile first, put it in a heat-resistant HDPE bottle, place the heat-resistant HDPE bottle on a magnetic stirrer, and stir evenly.

[0058] Step 2: On the basis of Step 1, add 0...

Embodiment 3

[0062] An acid-resistant strong gel plugging agent, in terms of weight percentage, its components are:

[0063] Main agent: 10%; the main agent is acrylic acid;

[0064] Acid-resistant monomer: 1.0%; the acid-resistant monomer is fluorohexyl ethyl acrylate;

[0065] Initiator: 0.5%; the initiator is azobisisobutyronitrile;

[0066] Cross-linking agent: 1.5%; the cross-linking agent is a mixture of N,N-methylenebisacrylamide and polyethyleneimine.

[0067] An acid-resistant strong gel plugging agent is prepared by the following method, comprising the following steps

[0068] Step 1: first take 10% acrylic acid, put it in a heat-resistant HDPE bottle, place the heat-resistant HDPE bottle on a magnetic stirrer, and stir evenly.

[0069] Step 2: On the basis of Step 1, add 1.0% ethyl fluorohexyl acrylate, and stir until uniform and transparent.

[0070]Step 3: On the basis of step 2, add 1.5% of a mixture of N,N-methylenebisacrylamide and polyethyleneimine and 0.5% of azobisis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of oil well water plugging used in oil exploitation, in particular to an acid-resistant strong gel plugging agent and a preparation method thereof. In terms of weight percentage, its components are: main agent: 3-10%; acid-resistant Monomer: 0.1‑1.0%; Initiator: 0.1‑0.5%; Crosslinker: 0.5%‑1.5%. The acid-resistant strong gel plugging agent of the invention has simple preparation method, wide source of raw materials, strong plugging performance and good acid resistance, and provides a new technical reserve for the chemical profile control and water plugging technology.

Description

[0001] Technical field [0002] The invention relates to the technical field of oil well water plugging used in oil exploitation, in particular to an acid-resistant strong gel plugging agent and a preparation method thereof. Background technique [0003] During the development of low-permeability reservoirs, due to the influence of formation fractures and heterogeneity, coupled with fracturing and putting into production, it is very easy to cause water inflow after oil well measures, a large increase in water cut, and high water cut. The existence of these wells is serious. It will affect the production capacity of oil wells and the long-term stable production of oil fields. At present, the conventional water shutoff technology has problems such as failure to plug wells with high water cut or difficulty in increasing production after plugging, and has been unable to meet the needs of water control and production increase in such reservoirs. [0004] The combined operation of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/512C09K8/50
CPCC09K8/512C09K8/5083C09K8/50
Inventor 王玉功李勇武龙徐洋谢新秋邹鸿江万向辉徐杰唐冬珠杨发宋振云汪小宇金娜王所良蒋文学许伟星李珊贺华镭李雪李丹诗佳庆
Owner BC P INC CHINA NAT PETROLEUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More