A kind of preparation method of swimsuit fabric

A technology for fabrics and swimsuits is applied in the field of preparation of swimsuit fabrics to achieve the effects of eliminating stress concentration, avoiding unevenness of fabrics and wide application range

Active Publication Date: 2021-01-05
JIANGSU HENGLI CHEM FIBER
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a method for preparing swimwear fabrics, with the purpose of solving the problem of how to give the fabrics a better elastic recovery rate when spandex is not used in the prior art when weaving swimsuit fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of swimsuit fabric
  • A kind of preparation method of swimsuit fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A preparation method of a swimsuit fabric, the process is as follows:

[0037](1) Preparation of modified PET: in the process of preparation, the addition of PTMG is 10wt% of the addition of polyethylene terephthalate; The intrinsic viscosity of permanent PET is 0.6dL / g, and the content of silver ions is 115ppm;

[0038] (2) FDY silk is prepared by the process of FDY process and circular side-by-side composite fibers by the modified PET (prepared in step (1)) and PTT (intrinsic viscosity is 1.17dL / g) with a mass ratio of 50:50; for FDY The silk is subjected to a relaxation heat treatment at a temperature of 97°C for 25 minutes to obtain an elastic polyester fiber; specifically:

[0039] The parameters of the FDY process are: the spinning temperature is 275°C, the temperature of the spinning box corresponding to the modified PET is 280°C, the temperature of the spinning box corresponding to the PTT is 272°C, the cooling temperature is 20°C, and the cooling wind speed is...

Embodiment 2

[0047] A preparation method of a swimsuit fabric, the process is as follows:

[0048] (1) Preparation of modified PET: in the process of preparation, the addition of PTMG is 9wt% of the addition of polyethylene terephthalate; The intrinsic viscosity of permanent PET is 0.61dL / g, and the content of silver ions is 200ppm;

[0049] (2) FDY silk is prepared by the process of FDY process and circular side-by-side composite fibers by the modified PET (prepared in step (1)) and PTT (intrinsic viscosity is 1.21dL / g) with a mass ratio of 50:50; for FDY The silk is subjected to a relaxation heat treatment at a temperature of 110° C. for 22 minutes to obtain an elastic polyester fiber; specifically:

[0050] The parameters of the FDY process are: the spinning temperature is 277°C, the temperature of the spinning box corresponding to the modified PET is 281°C, the temperature of the spinning box corresponding to the PTT is 274°C, the cooling temperature is 23°C, and the cooling wind spee...

Embodiment 3

[0058] A preparation method of a swimsuit fabric, the process is as follows:

[0059] (1) Preparation of modified PET: in the process of preparation, the addition of PTMG is 8wt% of the addition of polyethylene terephthalate; The intrinsic viscosity of permanent PET is 0.63dL / g, and the content of silver ions is 120ppm;

[0060] (2) FDY silk is prepared by the process of FDY process and circular side-by-side composite fibers by mass ratio of modified PET (prepared in step (1)) and PTT (intrinsic viscosity is 1.14dL / g) with a mass ratio of 50:50; for FDY The silk is subjected to a relaxation heat treatment at a temperature of 100°C for 23 minutes to obtain an elastic polyester fiber; specifically:

[0061] The parameters of the FDY process are: the spinning temperature is 276°C, the temperature of the spinning box corresponding to the modified PET is 283°C, the temperature of the spinning box corresponding to the PTT is 271°C, the cooling temperature is 21°C, and the cooling w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
elongation at breakaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a swimsuit fabric. The preparation method comprises the steps of: firstly, preparing elastic polyester fibers, i.e., in the process of preparing roundside-by-side composite fibers from modified PET (which contains an antibacterial agent) and PTT according to an FDY process, changing spinneret orifices on a spinneret plate into a three-leaf shape from a round shape, adopting annular blowing cooling, controlling arrangement of the three-leaf-shaped spinneret orifices on the spinneret plate to meet a certain conditions and then carrying out relaxation thermal treatment to obtain the elastic polyester fibers; and then by using the elastic polyester fibers as a raw material, carrying out flow of antioxidation finishing (after attaching antioxidation finishing liquid to the elastic polyester fibers in an electrostatic spraying mode (a distance is 15 to 50mm, and a voltage is 30 to 100V), carrying out microwave treatment (a frequency is 80 to150MHZ, and time is 10 to 15min)), spinning, weaving and anti-ultraviolet-ray finishing so as to prepare the swimsuit fabric. The swimsuit fabric has an elastic elongation gamma 1 of 133 to 138% and an elastic recovery rate gamma 2 of 98 to 100%.

Description

technical field [0001] The invention belongs to the technical field of textile fabrics, and relates to a preparation method of swimwear fabrics. Background technique [0002] Swimsuits generally use multi-material blended fabrics, the most common being nylon and ammonia, polyester and ammonia. Spandex is generally not used alone, but applied in an appropriate amount in the fabric to improve the stretchability of the fabric. Among them, the Lycra produced by the former DuPont Company in the United States can be stretched to 4 to 7 times the original length, and can quickly restore the original length after the external force is released; after it is blended with various fibers, the fabric can keep the fabric close to the body; The spandex content in swimsuits is about 15% to 20%, and such swimsuits can expand and contract freely with body movements. If the proportion of spandex is further increased, the dimensional stability of the fabric will deteriorate, because spandex w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01D5/22D01D5/253D01D10/02D01F8/14D01F1/10D06M11/46D06M11/45D06M11/70D06M13/148D06M13/228D06M13/152D06M15/227D06M101/32
CPCD01D5/22D01D5/253D01D10/02D01F1/106D01F8/14D06M11/45D06M11/46D06M11/70D06M13/148D06M13/152D06M13/228D06M15/227D06M2101/32D06M2200/25D10B2331/04D10B2401/061D10B2501/00
Inventor 陈瑞尹立新杨超明王雪
Owner JIANGSU HENGLI CHEM FIBER