High-strength high-fluidity polypropylene bonding resin and preparation method thereof

A high-fluidity and resin-bonding technology, used in polymer adhesive additives, non-polymer adhesive additives, adhesives, etc., can solve the problems of low strength and good fluidity, and achieve simple preparation process and raw materials. and the effect of easy access to equipment

Inactive Publication Date: 2020-04-28
SHANGHAI BANZAN MACROMOLECULE MATERIAL
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a high-strength and high-fluidity polypropylene adhesive resin and its preparation method for the deficiencies of the prior art, which solves the problem of good fluidity but low strength of the polypropylene adhesive resin in the prior art question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength high-fluidity polypropylene bonding resin and preparation method thereof
  • High-strength high-fluidity polypropylene bonding resin and preparation method thereof
  • High-strength high-fluidity polypropylene bonding resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high-strength and high-fluidity polypropylene adhesive resin, comprising the following components by weight:

[0026]

[0027] Wherein, the monofilament diameter of the quartz fiber is 6-12 μm, the softening point is 550-630° C., and the density is 2.35-2.72 g / cm 3 , the length is 2-5mm;

[0028] The particle size of the talcum powder is 1250 mesh, and the specific gravity is 2.7-2.8.

[0029] The polar compatibilizer is maleic anhydride grafted polypropylene with a density of 0.865-0.875g / cm3, a grafting rate of 0.8-1.5%, a tensile strength of 25-28MPa, and a melting point of 135-140°C. Under the conditions of 190°C and 2.16kg, its melt index is 45-50g / 10min.

[0030] The preparation method of the above high-strength and high-fluidity polypropylene adhesive resin comprises the following steps:

[0031] (1) Weigh polypropylene, talcum powder, quartz fiber, polar compatibilizer, and paraffin particles according to the proportion, then mix them evenly, and the mix...

Embodiment 2

[0034] A high-strength and high-fluidity polypropylene adhesive resin, comprising the following components by weight:

[0035]

[0036]

[0037] Wherein, the monofilament diameter of the quartz fiber is 6-12 μm, the softening point is 550-630° C., and the density is 2.35-2.72 g / cm 3 , the length is 2-5mm;

[0038] The particle size of the talcum powder is 1250 mesh, and the specific gravity is 2.7-2.8.

[0039] The polar compatibilizer is maleic anhydride grafted polypropylene with a density of 0.865-0.875g / cm3, a grafting rate of 0.8-1.5%, a tensile strength of 25-28MPa, and a melting point of 135-140°C. Under the conditions of 190°C and 2.16kg, its melt index is 45-50g / 10min.

[0040] The preparation method of the above high-strength and high-fluidity polypropylene adhesive resin comprises the following steps:

[0041] (1) Weigh polypropylene, talcum powder, quartz fiber, polar compatibilizer, and paraffin particles according to the proportion, then mix them evenly,...

Embodiment 3

[0044] A high-strength and high-fluidity polypropylene adhesive resin, comprising the following components by weight:

[0045]

[0046] Wherein, the monofilament diameter of the quartz fiber is 6-12 μm, the softening point is 550-630° C., and the density is 2.35-2.72 g / cm 3 , the length is 2-5mm;

[0047] The particle size of the talcum powder is 1250 mesh, and the specific gravity is 2.7-2.8.

[0048] The polar compatibilizer is maleic anhydride grafted polypropylene with a density of 0.865-0.875g / cm3, a grafting rate of 0.8-1.5%, a tensile strength of 25-28MPa, and a melting point of 135-140°C. Under the conditions of 190°C and 2.16kg, its melt index is 45-50g / 10min.

[0049] The preparation method of the above high transparency and high oxygen resistance polypropylene composite material comprises the following steps:

[0050] (1) Weigh polypropylene, talcum powder, quartz fiber, polar compatibilizer, and paraffin particles according to the proportion, then mix them ev...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
softening pointaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses polypropylene bonding resin with high strength and high fluidity. The polypropylene bonding resin comprises the following components in parts by weight: 60-81 parts of polypropylene; 12 to 20 parts of a polar compatilizer; 11 to 20 parts of talcum powder; 6-10 parts of paraffin particles; and 1-10 parts of quartz fiber; wherein the monofilament diameter of the quartz fiberis 6-12 [mu] m, the softening point is 550-630 DEG C, and the density is 2.35-2.72 g/cm<3>. According to the high-strength and high-fluidity polypropylene bonding resin, under the compounding action of the quartz fiber, the polar compatilizer, the talcum powder and the paraffin particles, the polypropylene bonding resin has high strength and high fluidity. In addition, the invention further discloses a preparation method of the polypropylene bonding resin, the preparation process is simple, raw materials and equipment are easy to obtain, and large-scale production can be achieved.

Description

technical field [0001] The invention relates to the technical field of manufacturing polypropylene adhesive resin, in particular to a high-strength and high-fluidity polypropylene adhesive resin and a preparation method thereof. Background technique [0002] Polymer-type polypropylene materials have a lower heat distortion temperature (100°C), low transparency, low gloss, and low rigidity. The impact strength of polymer-type polypropylene materials increases with the increase of ethylene content, while Strength decreases with increasing ethylene content. The Vicat softening temperature of the polymer-type polypropylene material is 150°C, and its Vicat softening temperature is relatively high, so the material has better dimensional stability when heated, the smaller the thermal deformation, the better the thermal deformation resistance. In addition, due to the high crystallinity of the polymer-type polypropylene material, this material has strong surface stiffness and good s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/12C09J11/04C09J11/08
CPCC08K2201/004C08K2201/005C08L2205/03C09J11/04C09J11/08C09J123/12C08L51/06C08L91/06C08K3/34C08K7/10
Inventor 李楠毕宏海储江顺肖传富杨少辉孙晓光毕宏江欧阳贵汪丽
Owner SHANGHAI BANZAN MACROMOLECULE MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap