Aluminium alloy welding wire containing TiB2 particles

A technology of aluminum alloy welding wire and particles, applied in the field of aluminum alloy welding wire, can solve the problem of easy cracking of aluminum alloy, and achieve the effects of improving the strength of the weld, improving the comprehensive performance and reducing the internal stress.

Active Publication Date: 2020-05-08
SHANGHAI JIAO TONG UNIV
View PDF13 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, there is an urgent need to develop an aluminum alloy welding wire containing ceramic particles, which can not only improve the strength and thermal stability of the weld, but also solve the problem of easy cracking in welding of 7XXX series aluminum alloys.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A TiB-containing 2 Granular aluminum alloy welding wire, the aluminum alloy welding wire contains the following elements by weight percentage: Zn is 1.1%, Mg is 4.1%, Cu is 1.3%, Zr is 0.2%, Cr is 0.15%, Fe is 0.3%, Si is 0.2% %, Mn 0.4%, TiB 2 Ceramic particles are 5%, the balance is Al, among them, TiB 2 The particle size of the ceramic particles is 11 microns to 13 microns.

Embodiment 2

[0040] A TiB-containing 2 Granular aluminum alloy welding wire, the aluminum alloy welding wire contains the following elements by weight percentage: Zn is 3.1%, Mg is 4.9%, Cu is 1.7%, Zr is 0.15%, Cr is 0.1%, Fe is 0.2%, Si is 0.15% %, Mn 0.15%, TiB 2 The ceramic particles are 4%, the balance is Al, among them, TiB 2 The particle size of the ceramic particles is 14 microns to 16 microns.

Embodiment 3

[0042] A TiB-containing 2 Granular aluminum alloy welding wire, the aluminum alloy welding wire contains the following elements by weight percentage: Zn is 1.6%, Mg is 4.7%, Cu is 1.4%, Zr is 0.15%, Cr is 0.1%, Fe is 0.2%, Si is 0.15% %, Mn 0.15%, TiB 2 Ceramic particles are 3%, the balance is Al, among them, TiB 2 The particle size of the ceramic particles is 17 microns-20 microns.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an aluminium alloy welding wire containing TiB2 particles. The aluminium alloy welding wire comprises the following elements by weight: 1.1%-3.1% of Zn, 4.1%-4.9% of Mg, 1.3%-1.7% of Cu, 0.02%-0.3% of Zr, 0.03%-0.3% of Cr, 0.01%-0.4% of Fe, 0.01%-0.3% of Si, 0.01%-0.4% of Mn, no more than 6% of TiB2 particles and the balance Al, wherein the diameter of the TiB2 particles is11 micrometers-30 micrometers.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy welding wire, in particular to a TiB-containing 2 Granular aluminum alloy welding wire and a preparation method thereof. Background technique [0002] Because of its low density, good electrical conductivity, high plasticity, easy processing and many other excellent properties, aluminum alloy has a wide range of applications in the fields of aerospace, electronics, automobiles and transportation. It can be said that aluminum is the material with the largest amount of use and the widest application range among non-ferrous metal materials. Among various aluminum alloys, 7XXX series aluminum alloys are also called high-strength aluminum alloys or superhard aluminum alloys because they have the highest strength among aluminum alloys. As a high-performance material, 7XXX series high-strength aluminum alloy has the advantages of high specific strength, specific stiffness, good stress corrosion ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/28B23K35/40C22C21/08C22C32/00
CPCB23K35/288B23K35/40C22C21/08C22C32/0073
Inventor 夏存娟陈东吴一杨青峰李宇罡耿继伟王浩伟
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap