Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of high-hardness and high-strength WC-CO-based cemented carbide, its preparation method and cutting tool

A cemented carbide, high-strength technology, applied in the field of cutting tools, its preparation, high-hardness and high-strength WC-Co-based cemented carbide, can solve the problem of difficulty in improving the strength of the alloy, increase the strength and hardness, and increase the service life. , to achieve the effect of high hardness and high strength performance

Active Publication Date: 2021-06-29
江西江钨硬质合金有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the process of alloy sintering, crystal grains often aggregate to form polycrystals, thus forming a bottleneck, making it difficult to improve the strength of the alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-hardness and high-strength WC-CO-based cemented carbide, its preparation method and cutting tool

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A high-hardness and high-strength WC-Co-based cemented carbide, comprising the following raw materials in parts by weight: 80 parts of WC powder, 5 parts of Co powder, and 0.5 parts of additives;

[0029] The additive is composed of metal carbide Cr 3 C 2 and metal nitride Cr 3 N 2 composition.

[0030] The metal carbide accounts for 0.1% of the total mass of the raw material.

[0031] The metal nitride accounts for 0.1% of the total mass of raw materials.

[0032] The average particle size of the WC powder and Co powder is 0.3 μm.

[0033] A preparation method of high-hardness and high-strength WC-Co-based cemented carbide, comprising the following steps:

[0034] S1: Take WC powder, Co powder, and additives in proportion, use ethanol as the grinding medium, PEG (polyethylene glycol) as the binder, and mix them into initial materials. Under the same conditions, the ball mill was fully ground for 10 hours to form a mixture, which was dried, sieved, and molded int...

Embodiment 2

[0042] A high-hardness and high-strength WC-Co-based cemented carbide, comprising the following raw materials in parts by weight: 85 parts of WC powder, 10 parts of Co powder, and 1 part of additive;

[0043] The additives consist of metal carbides VC and metal nitrides VN.

[0044] The metal carbide accounts for 0.3% of the total mass of the raw material.

[0045] The metal nitride accounts for 0.3% of the total mass of raw materials.

[0046] The particle size of the WC powder and Co powder is 0.6 μm.

[0047] A preparation method of high-hardness and high-strength WC-Co-based cemented carbide, comprising the following steps:

[0048] S1: Take WC powder, Co powder, and additives in proportion, use ethanol as the grinding medium, PEG (polyethylene glycol) as the binder, and mix them into initial materials. Under the condition of ball milling for 15 hours, the mixture was fully ground. The mixture is dried, sieved, and molded into a sample strip under a one-way load of 5-1...

Embodiment 3

[0056] A high-hardness and high-strength WC-Co-based cemented carbide, comprising the following raw materials in parts by weight: 90 parts of WC powder, 15 parts of Co powder, and 3 parts of additives;

[0057] The additive consists of metal carbide TiC and metal nitride TaN.

[0058] The metal carbide accounts for 0.5% of the total mass of the raw material.

[0059] The metal nitride accounts for 0.5% of the total mass of raw materials.

[0060] The particle size of the WC powder and Co powder is 0.8 μm.

[0061] A preparation method of high-hardness and high-strength WC-Co-based cemented carbide, comprising the following steps:

[0062] S1: Take WC powder, Co powder, and additives in proportion, use ethanol as the grinding medium, PEG (polyethylene glycol) as the binder, and mix them into initial materials. Under these conditions, the ball mill was fully ground for 20 hours to form a mixture. The mixture is dried, sieved, and molded into a sample strip under a one-way load...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-hardness and high-strength WC-Co-based cemented carbide, comprising the following raw materials in parts by weight: 80-90 parts of WC powder, 5-15 parts of Co powder, 0.5-3 parts of additives; The additives are composed of metal carbides and metal nitrides; the bending strength of this cemented carbide is as high as 4810N / mm 2 , the hardness is as high as 94.5HRa, and the invention also discloses the preparation method of the cemented carbide. The cemented carbide is prepared by multi-stage firing of raw materials with a thickness of 0.8 μm or less, and the additives used effectively inhibit the formation of polycrystals during the sintering growth of the alloy. , so as to realize the high hardness and high strength performance of cemented carbide, and the invention also discloses a cutting tool made of the cemented carbide, due to the increase of its strength and hardness, the defect resistance is improved, and the service life is obviously increased.

Description

technical field [0001] The invention relates to the field of cemented carbide, in particular to a high-hardness and high-strength WC-Co-based cemented carbide, a preparation method thereof and a cutting tool. Background technique [0002] Cemented carbide is mainly composed of micron-scale / nano-scale powders of carbides of high-hardness refractory metals (that is, as a hard phase), with cobalt (Co) as a binder phase, supplemented by inhibitors, and processed in a vacuum furnace or Powder metallurgy products sintered in a hydrogen reduction furnace. For the current cemented carbide materials, hardness and flexural strength are two important testing standards. Among them, the cemented carbide prepared by fine particle powder has higher flexural strength and hardness than the cemented carbide prepared by medium and coarse particle powder. At present, in the market of fine-grained cemented carbide, the hardness of common mainstream products is 91.5-94HRA, and the bending stren...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C29/08B22F5/00C22C1/05
CPCB22F5/00B22F2005/001C22C1/051C22C29/067C22C29/08
Inventor 郭永忠汤昌仁曾程遥
Owner 江西江钨硬质合金有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More