Coated flame retardant and preparation method thereof

A kind of flame retardant and coated technology, which is applied in the field of coated flame retardants and their preparation, can solve the problems of long heating time of flame retardants, affecting the appearance of products, unacceptable to users, etc., and achieves strong polarity and melting point Low, improve the effect of thermal decomposition

Inactive Publication Date: 2020-05-19
GUANGDONG IND TECHN COLLEGE
12 Cites 0 Cited by

AI-Extracted Technical Summary

Problems solved by technology

However, due to the addition of flame retardants, the flame retardants are heated for a long time during the preparation process, and the shearing effect is strong, and the flame retardants will be decomposed to varying degrees, resulting in the prepared composite materials being ine...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Abstract

The invention discloses a coated flame retardant. The metal salt of the ethylene-acrylic acid copolymer is mainly used as the coating resin and has excellent compatibility with the flame-retardant component (especially the metal salt flame-retardant component), so that the thermal decomposition of the flame retardant in the processing process of the flame-retardant component can be improved, and the toughness of the flame-retardant modified plastic can also be improved.

Technology Topic

Examples

  • Experimental program(1)
  • Effect test(1)

Example Embodiment

[0024] The present invention will be described in detail below in conjunction with specific embodiments. The following examples will help those skilled in the art to further understand the present invention, but do not limit the present invention in any form. It should be pointed out that for those of ordinary skill in the art, a number of modifications and improvements can be made without departing from the concept of the present invention. These all belong to the protection scope of the present invention.
[0025] The sources of raw materials used in the present invention are as follows:
[0026] PBT: L09XM, Jiangsu Heshili New Material Co., Ltd., with a viscosity of 0.93dl/g;
[0027] Polyamide: PA6, molecular weight is about 25,000.
[0028] Coating flame retardant A: diethyl aluminum hypophosphite; coating resin is ethylene-methacrylic acid copolymer sodium salt, melt index is 1.1g/10min (190℃, 2.16kg), melting point is 96℃, commercially available . The weight content of the coating resin is 20%.
[0029] Coated flame retardant B: melamine phosphate; coating resin is ethylene-methacrylic acid copolymer sodium salt; melt index is 1.1g/10min (190℃, 2.16kg), melting point is 96℃, commercially available. The weight content of the coating resin is 20%.
[0030] Coated flame retardant C: diethyl aluminum hypophosphite; coating resin is ethylene-ethyl acrylic acid copolymer zinc salt, melt index is 4.5g/10min (190℃, 2.16kg), melting point is 85℃, commercially available . The weight content of the coating resin is 20%.
[0031] Coating flame retardant D: diethyl aluminum hypophosphite; coating resin is ethylene-butyl acrylic copolymer magnesium salt, melt index is 1.3g/10min (190℃, 2.16kg), melting point is 88℃, commercially available . The weight content of the coating resin is 20%.
[0032] Coated flame retardant E: diethyl aluminum hypophosphite; coating resin is ethylene-methacrylic acid copolymer, and the weight content of methacrylic acid monomer is 20%.
[0033] Glass fiber: CPIC ECS305K;
[0034] Antioxidant: hindered phenolic antioxidant.
[0035] The preparation method of the coated flame retardant is as follows: the flame retardant ingredients and the coated resin are extruded and pelletized through a twin-screw extruder to obtain the coated flame retardant. The screw temperature range is 150~200℃, and the screw speed is 200 -250 rpm.
[0036] The preparation method of the flame-retardant modified plastic: mix the polymer (PBT, PA6), the coated flame retardant, and the auxiliary (comparative example file 2 additionally adds the sodium salt of ethylene-methacrylic acid copolymer) and pass the twin screw. The extruder extrudes and granulates to obtain the flame-retardant modified plastic. Glass fiber side feeding, the temperature range of the screw is: PBT 230~250℃, polyamide 230-280℃, 300~600rpm.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melt index1.1g/10min
Melt index4.5g/10min
Melt index1.3g/10min
tensileMPa
Particle sizePa
strength10

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Similar technology patents

Classification and recommendation of technical efficacy words

  • Strong polarity
  • Low melting point

Preparation method of photo-crosslinking polyvinyl alcohol/cellulose nanocrystal (PVA/CNC) composite film

ActiveCN104497330AStrong polarityHighly hydrophilic and water solubleDouble bondPolyvinyl alcohol
Owner:深圳市大亚洲电子材料有限公司

High-performance fabric self-pressurization carrier dyeing method

InactiveCN110106719AStrong polarityChange in surface activityDyeing processChemistrySolubility
Owner:WUHAN TEXTILE UNIV

Method for manufacturing magnetoresistance effect element using simultaneous sputtering of Zn and ZnO

ActiveUS20100142098A1Strong polarityDecrease diversionSpark gapsNanomagnetismNegative potentialPhysics
Owner:TDK CORPARATION

Compounds with physiological cooling effect

InactiveUS7030273B1Low melting pointPronounced effectOrganic chemistryMucous membranePhotochemistry
Owner:QAROMA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products