Microwave dielectric ceramic material and preparation method thereof

A technology of microwave dielectric ceramics and raw materials, applied in the field of dielectric ceramics, can solve problems such as low quality factor and single dielectric constant, and achieve the effect of improving quality factor, expanding the range of dielectric constant, and broad application prospects

Active Publication Date: 2022-04-22
SHENZHEN ZHENHUA FU ELECTRONICS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a microwave dielectric ceramic material and its preparation method, aiming to solve the technical problems of the existing microwave dielectric ceramic material with relatively single dielectric constant and low quality factor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microwave dielectric ceramic material and preparation method thereof
  • Microwave dielectric ceramic material and preparation method thereof
  • Microwave dielectric ceramic material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] On the other hand, an embodiment of the present invention also provides a method for preparing a microwave dielectric ceramic material, comprising the following steps:

[0040] S01: Provide the raw materials for the preparation of the microwave dielectric ceramic material described in the embodiment of the present invention;

[0041] S02: mixing the titanium dioxide, silicon dioxide, zinc oxide and lithium carbonate, performing the first ball milling treatment, and then performing the first sintering to obtain an initial sintered product;

[0042] S03: Mixing the initial sintered product with the boron oxide and / or boric acid, performing a second ball milling treatment, and then performing a second sintering to obtain the microwave dielectric ceramic material.

[0043] The preparation method of the microwave dielectric ceramic material provided by the embodiment of the present invention is prepared by using special preparation raw materials. Firstly, the ceramic main pa...

Embodiment 1

[0050] A microwave dielectric ceramic material is made of the following raw materials in parts by weight:

[0051] 12 parts of titanium dioxide;

[0052] 65 parts of zinc oxide;

[0053] 24 parts of silicon dioxide;

[0054] Lithium carbonate 0.1 part;

[0055] Boron oxide 3 parts.

[0056] The preparation method of the microwave dielectric ceramic material comprises:

[0057] Put the titanium dioxide, zinc oxide, silicon dioxide and lithium carbonate in the above parts by weight into a ball mill jar for ball milling, and pre-sinter at 900°C after drying. Then add the remaining boron oxide by weight, perform ball milling for the second time, dry and shape, and then sinter at 900°C to obtain a microwave dielectric ceramic material. The preparation method can finally obtain a microwave dielectric ceramic material with a dielectric constant of 8, a quality factor Qf of 20000 GHz, and a temperature coefficient of resonance frequency of 0 ppm / °C.

Embodiment 2

[0068] A microwave dielectric ceramic material is made of the following raw materials in parts by weight:

[0069] 56 parts of titanium dioxide;

[0070] 34 parts of zinc oxide;

[0071] Silicon dioxide 0.1 part;

[0072] Lithium carbonate 11 parts;

[0073] Boron oxide 1 part.

[0074] The preparation method of the microwave dielectric ceramic material comprises:

[0075] Put the titanium dioxide, zinc oxide, silicon dioxide and lithium carbonate in the above parts by weight into a ball mill jar for ball milling, and pre-sinter at 900°C after drying. Then add the remaining boron oxide by weight, perform ball milling for the second time, dry and shape, and then sinter at 900°C to obtain a microwave dielectric ceramic material. The preparation method can finally obtain a microwave dielectric ceramic material with a dielectric constant of 25, a quality factor Qf of 30000 GHz, and a resonant frequency temperature coefficient of 0 ppm / °C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality factoraaaaaaaaaa
resonant frequency temperature coefficientaaaaaaaaaa
quality factoraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of dielectric ceramics, in particular to a microwave dielectric ceramic material and a preparation method thereof. The raw materials for preparing the microwave dielectric ceramic material include the following components in parts by weight: 12-56 parts of titanium dioxide; 0.1-24 parts of silicon dioxide; 0.1-65 parts of zinc oxide; 0.1-11 parts of lithium carbonate; boron oxide / or boric acid 0.25 to 8 servings. The microwave dielectric ceramic material prepared from the raw material can not only expand the dielectric constant range of the microwave dielectric ceramic material, improve its quality factor, but also make the resonant frequency temperature coefficient of the microwave dielectric ceramic material close to zero, so it can be adapted to The electrical requirements of the matrix materials required by a variety of LTCC components, and can be well matched with silver electrodes for co-firing, which has broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of dielectric ceramics, and in particular relates to a microwave dielectric ceramic material and a preparation method thereof. Background technique [0002] Low temperature co-fired ceramic (Low Temperature Co-fired Ceramic, LTCC) technology is a remarkable integrated component technology developed in 1982. It has become the development direction of the passive device field and the economic growth point of the new component industry. In the future Communications, wireless local area network (WLAN), digital signal processor, global positioning system (GPS) receiving components, automotive electronics and other fields have a huge market of tens of billions of dollars every year. Apply LTCC technology to produce filters, baluns, couplers, power dividers, antennas and other products. Low-temperature co-fired microwave dielectric ceramics are the key basic materials for the preparation of LTCC devices. In addit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/453C04B35/46C04B35/622C04B35/626C04B35/64
CPCC04B35/453C04B35/46C04B35/622C04B35/62675C04B35/64C04B2235/3232C04B2235/3418C04B2235/3203C04B2235/3409C04B2235/3284C04B2235/656C04B2235/96
Inventor 刘洋朱建华肖倩黎燕林张婷王东王智会
Owner SHENZHEN ZHENHUA FU ELECTRONICS