Method for producing 8021 aluminum alloy soft wrapping foil for lithium batteries by casting and rolling method

An aluminum alloy and lithium battery technology, applied in the field of aluminum material processing, can solve the problems of poor puncture resistance and stability, poor adhesion and composite performance, poor cold stamping formability, etc., to eliminate metal rolling resistance, reduce hydrogen and Oxidized slag inclusion content, good sealing effect

Active Publication Date: 2022-03-15
JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing 8021 aluminum alloy soft wrapping foil for lithium batteries and its manufacturing method have the following problems: the existing soft wrapping foil for aluminum-plastic film has low barrier properties, poor cold stamping formability, poor puncture resistance and poor stability, resulting in During the lamination process of aluminum-plastic film, its bonding performance is not good, and it is easy to fall off and delaminate; therefore, it is urgent to provide a kind of 8021 aluminum alloy soft wrapping foil for lithium batteries with good folding resistance, stamping resistance and sealing performance and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for producing 8021 soft-packed aluminum foil for lithium batteries by casting and rolling, the mass percentages of each element in the aluminum foil are as follows: Fe=1.61%, Si0.12%, Cu0.05%, Mn0.05%, Mg0.01 %, Cr<0.05%, Zn<0.05%, Ti0.042%, and the rest is Al.

[0029] The preparation method of the above-mentioned 8021 aluminum alloy soft package foil for the lithium battery comprises the following steps:

[0030] (1) Smelting process: a. Add aluminum ingots into the melting furnace and smelt at 700-760°C. After smelting for 4-6 hours, the aluminum hydration level will be reduced. Calculate and add appropriate amount of various intermediate alloys and / or metal additives, stir and then smelt for 1 to 2 hours, then carry out 2 times of refining, continue to smelt for 0.5 to 1 hour after the refining is completed, and carry out a particle refining before turning down the furnace to complete Smelting operation in the smelting furnace; b. Import the molten aluminu...

Embodiment 2

[0033] A method for producing 8021 soft-packed aluminum foil for lithium batteries by casting and rolling, wherein the mass percentages of each chemical component in the molten solution after smelting are: the mass percentages of each element in the aluminum foil are as follows: Fe1.56%, Si0.15 %, Cu0.05%, Mn0.03%, Mg0.01%, Cr3 / h, the hydrogen content of the front box aluminum liquid is 0.11mL / (100g*Al), the temperature of the front box aluminum liquid is 693°C, the size of the roll gap is 5.28mm, the casting and rolling area is 52mm, and the production speed is 750mm / min. The thickness of the slab is 7.0mm; the homogenization and annealing process of the casting and rolling slab: the material temperature is 500°C, and the holding time is 8h. All the other are the same as example 1. The tensile strength of the final 8021 soft wrapping foil material is 110Mpa, the elongation reaches 20%, the cupping value is 8.1mm, and the pinhole rate is 0 / m 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
thicknessaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for producing 8021 aluminum alloy soft-wrapped foil for lithium batteries by a casting and rolling method, and belongs to the field of aluminum processing. The steps of the method are: smelting-casting-rolled strip-cast-rolled coil annealing-cold rolling-intermediate annealing-foil rolling-finished product annealing-coiling-inspection, packaging, and storage; the cast-rolled strip is based on the chemical composition of 8021 aluminum alloy The aluminum alloy melt is smelted, and then cast and rolled into a metal strip; the temperature of the front box is 680-700°C, the liquid level of the front box is 150-240mm, the rolling speed is 0.65-0.85m / min, and the thickness of the slab is 5.5-7.5 mm. The 8021 alloy aluminum foil blank produced by the casting-rolling method in the present invention has good metallurgical properties and processing microstructure properties. Compared with the hot-rolling method, the casting-rolling method has a shorter production cycle, saves energy, and reduces production costs.

Description

technical field [0001] The invention belongs to the field of aluminum material processing, and in particular relates to a method for producing 8021 aluminum alloy soft wrapping foil for lithium batteries by casting and rolling. Background technique [0002] Aluminum alloy soft wrapping foil is one of the key materials for lithium batteries. Aluminum alloy soft wrapping foil for 8021 batteries has the characteristics of high plasticity, good corrosion resistance, good electrical conductivity and thermal conductivity, good formability and certain strength. Widely used in the electronics industry. However, the existing 8021 aluminum alloy soft wrapping foil for lithium batteries and its manufacturing method have the following problems: the existing soft wrapping foil for aluminum-plastic film has low barrier properties, poor cold stamping formability, poor puncture resistance and poor stability, resulting in During the lamination process of aluminum-plastic film, its adhesion ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/00C22C1/06C22C1/02C22F1/04
CPCC22C21/00C22C1/026C22C1/06C22F1/04
Inventor 左源董则防符豪万宝伟陈建华王雪云王毓玮殷文奇
Owner JIANGSU DINGSHENG NEW MATERIAL JOINT STOCK CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com