A kind of preparation method of antiviral composite polyester fiber

A polyester fiber and anti-virus technology, applied in the field of polyester fiber, can solve problems such as unsatisfactory effects, and achieve the effects of easy industrialization, tight integration, and easy promotion.

Active Publication Date: 2022-05-13
浙江正凯化纤有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above two methods are not very effective

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of antiviral composite polyester fiber
  • A kind of preparation method of antiviral composite polyester fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] ① Preparation of sheath material

[0030] 1.1) Dissolve chitin sulfate in dimethylacetamide solution containing 6% lithium chloride, the concentration is controlled at 3%, and the temperature is 70°C.

[0031] 1.2) disperse graphene oxide in dimethylacetamide solvent, and control the concentration at 1%.

[0032] 1.3) Mix the solution prepared in 1.1) and 1.2) with the components of polyester polyurethane, the molar ratio of isocyanate group to hydroxyl group is 1.8, pre-polymerize at 90°C for 45min, after the pre-polymerization is completed, pour into the prepolymer Adding N,N-dimethylacetamide solvent to make a prepolymer solution with a mass percentage concentration of 50%;

[0033] 1.4) The chain extender is N,N-dimethylacetamide solution of ethylenediamine, diethylamine, pentamethylenediamine, the mass percent concentration is 5.0%, wherein, the molar ratio of ethylenediamine to pentamethylenediamine is 90: 10. The consumption of diethylamine is 3000ppm; the chai...

Embodiment 2

[0041] ① Preparation of sheath material

[0042] 1.1) Dissolve chitin sulfate in dimethylacetamide solution containing 6% lithium chloride, the concentration is controlled at 3%, and the temperature is 70°C.

[0043]1.2) disperse graphene oxide in dimethylacetamide solvent, and control the concentration at 1%.

[0044] 1.3) Mix the solution prepared in 1.1) and 1.2) with the components of polyester polyurethane, the molar ratio of isocyanate group to hydroxyl group is 1.8, pre-polymerize at 90°C for 45min, after the pre-polymerization is completed, pour into the prepolymer Adding N,N-dimethylacetamide solvent to make a prepolymer solution with a mass percentage concentration of 50%;

[0045] 1.4) The chain extender is N,N-dimethylacetamide solution of ethylenediamine, diethylamine, pentamethylenediamine, the mass percent concentration is 5.0%, wherein, the molar ratio of ethylenediamine to pentamethylenediamine is 90: 10. The consumption of diethylamine is 3000ppm; the chain...

Embodiment 3

[0053] ① Preparation of sheath material

[0054] 1.1) Dissolve chitin sulfate in dimethylacetamide solution containing 6% lithium chloride, the concentration is controlled at 3%, and the temperature is 70°C.

[0055] 1.2) disperse graphene oxide in dimethylacetamide solvent, and control the concentration at 1%.

[0056] 1.3) Mix the solution prepared in 1.1) and 1.2) with the components of polyester polyurethane, the molar ratio of isocyanate group to hydroxyl group is 1.8, pre-polymerize at 90°C for 45min, after the pre-polymerization is completed, pour into the prepolymer Adding N,N-dimethylacetamide solvent to make a prepolymer solution with a mass percentage concentration of 50%;

[0057] 1.4) The chain extender is N,N-dimethylacetamide solution of ethylenediamine, diethylamine, pentamethylenediamine, the mass percent concentration is 5.0%, wherein, the molar ratio of ethylenediamine to pentamethylenediamine is 90: 10. The consumption of diethylamine is 3000ppm; the chai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to view more

Abstract

An antiviral composite polyester fiber, characterized in that the polyester fiber comprises the following components and weight ratio: graphene oxide 0.05-0.2%, chitin sulfate 0.5-2.0%, polyester polyurethane polymer 10.0-30.0% , polyester polymer 67.8~89.45%; The polyester fiber includes a core material and a sheath material positioned at the periphery of the core, the aforementioned core material is a polyester polymer, and the aforementioned sheath material is graphene oxide, chitin sulfate Ester, polyester polyurethane polymer composition. The invention also discloses a preparation method of the polyester fiber. The antiviral composite polyester fiber produced by the invention has outstanding antiviral function, long-lasting effect, safety and reliability.

Description

technical field [0001] The invention relates to a polyester fiber, and also relates to a preparation method of the polyester fiber, which belongs to the technical field of chemical fibers. Background technique [0002] In the human living environment, viruses and other microorganisms are ubiquitous, causing great harm to human life and health, especially to infants, the elderly and those with low immune function. [0003] In recent years, outbreaks caused by viruses and the like have occurred frequently. Take influenza as an example, the influenza epidemic is higher than in previous years, and the number of cases and deaths is increasing. Since viruses such as influenza are easy to mutate and bring great difficulties to treatment, prevention is particularly important. In order to prevent, control and treat these infectious diseases, countries around the world have spent a lot of time and energy on research and development of antiviral products. [0004] Antiviral textiles...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/16D01F8/14D01F1/10D01D5/06D01D5/34C08G63/183C08G63/78C08G18/66C08G18/65C08G18/64C08G18/42C08G18/12
CPCD01F1/103D01F8/16D01F8/14D01D5/06D01D5/34C08G63/183C08G63/78C08G18/6484C08G18/42C08G18/12C08G18/3228
Inventor 王小华汪春波王炳奎陆清峰袁慧丽邓成浩
Owner 浙江正凯化纤有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap