Preparing method for activated aluminum oxide based anti-microbial film for fabrics

A technology of activated alumina and thin film, applied in the field of fabrics to improve the local environment

Inactive Publication Date: 2020-07-28
徐燚超
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problems in the prior art, the present invention provides a preparation method for fabrics based on activated alumina antibacterial films, which solves the problem of the safety of existing antibacterial fabrics. system, which can quickly combine to form negative oxygen ions, which not only have an antibacterial effect, but also benefit physical and mental health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0016] A kind of preparation method based on active aluminum oxide antibacterial film for fabric, comprises the steps:

[0017] Step 1, adding polyaniline to dimethylformamide and stirring evenly to form a solution, and adding absolute ethanol to form a viscous liquid; the concentration of polyaniline in dimethylformamide is 10-50g / L, so The added amount of absolute ethanol is 5-9% of the mass of dimethylformamide; the polyaniline is slowly added into the polyaniline, and continuously stirred at a stirring speed of 1000-2000r / min until completely Dissolve to form a solution, and at the same time, absolute ethanol can dissolve dimethylformamide, which greatly improves the overall film-forming and leveling properties of the solution;

[0018] Step 2, adding tourmaline powder to the viscous liquid for ultrasonic dispersion for 2-4 hours, and constant temperature ultrasonication for 20-30 minutes to obtain spinning solution; the amount of tourmaline powder added is 20-40% of the m...

Embodiment 1

[0023] A kind of preparation method based on active aluminum oxide antibacterial film for fabric, comprises the steps:

[0024] Step 1, polyaniline is added to dimethylformamide and stirred evenly to form a solution, and absolute ethanol is added to form a viscous liquid; the concentration of polyaniline in dimethylformamide is 10g / L, and the The addition of water ethanol is 5% of dimethyl formamide quality;

[0025] Step 2, adding tourmaline powder to the viscous liquid for ultrasonic dispersion for 2 hours, constant temperature ultrasonication for 20 minutes, to obtain spinning solution; the amount of tourmaline powder added is 20% of the mass of polyaniline, and the ultrasonic temperature for ultrasonic dispersion is 10°C. The ultrasonic frequency is 60kHz, the temperature of constant temperature ultrasonic is 80°C, and the ultrasonic frequency is 90kHz;

[0026] Step 3, adding the spinning solution to the electrospinning machine for high-voltage electrospinning to obtain ...

Embodiment 2

[0031] A kind of preparation method based on active aluminum oxide antibacterial film for fabric, comprises the steps:

[0032] Step 1, polyaniline is added to dimethylformamide and stirred evenly to form a solution, and absolute ethanol is added to form a viscous liquid; the concentration of polyaniline in dimethylformamide is 50g / L, and the The add-on of water ethanol is 9% of dimethylformamide quality;

[0033] Step 2, adding tourmaline powder to the viscous liquid for ultrasonic dispersion for 4 hours, and constant temperature ultrasonication for 30 minutes to obtain spinning solution; the amount of tourmaline powder added is 40% of the mass of polyaniline, and the ultrasonic temperature for ultrasonic dispersion is 20°C. The ultrasonic frequency is 90kHz, the constant temperature ultrasonic temperature is 90°C, and the ultrasonic frequency is 120kHz;

[0034] Step 3, adding the spinning solution to the electrospinning machine for high-voltage electrospinning to obtain fi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
antibacterial rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparing method for an activated aluminum oxide based anti-microbial film for fabrics. The preparing method comprises the steps that polyaniline is added in dimethyl formamide to be evenly stirred, dissolving liquid is formed, absolute ethyl alcohol is added, and viscous fluid is formed; tourmaline powder is added in the viscous fluid to be subjected to ultrasonic dispersion for 2-4 h, constant-temperature ultrasonic treatment is conducted for 20-30 min, and spinning liquid is obtained; the spinning liquid is added in an electrostatic spinning machine to be subjectedto high-voltage electrostatic spinning, and fiber monofilaments are obtained; then, the fiber monofilaments are woven to form a fiber net; aluminum hydroxide is evenly dispersed in the absolute ethylalcohol, and good turbid liquid is formed; and the surface of the fiber net is evenly coated with the dimethyl formamide, a liquid film is formed, the surface of the liquid film is evenly coated withthe turbid liquid, standing is conducted for 10-20 min, constant-temperature drying is conducted, and the anti-microbial film is obtained. Tourmaline powder negative ions are utilized for being combined with an activated aluminum oxide oxygen-rich system, negative oxygen ions can be formed through rapid combination, the anti-microbial effect is achieved, and physical and psychological health canbe benefited as well.

Description

technical field [0001] The invention belongs to the field of fabrics and relates to antibacterial fabrics, in particular to a preparation method for fabrics based on active alumina antibacterial films. Background technique [0002] Antibacterial fabric is a special functional fabric with good safety. It can efficiently and completely remove bacteria, fungus and mold on the fabric, keep the fabric clean, and prevent bacteria from regenerating and multiplying. Antibacterial fabrics have a good antibacterial effect, can eliminate the peculiar smell caused by bacteria, keep the fabric tidy, and avoid the reproduction of bacteria to reduce the risk of re-spread. Main application directions: socks, underwear, tooling fabrics, outdoor sports fabrics, etc. With the continuous improvement of people's living standards, people's pursuit of the comfort and functionality of clothing is getting higher and higher, so the demand for antibacterial materials and antibacterial clothing is inc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/45D01F6/94D01F1/10
CPCD01F1/103D01F6/94D06M11/45D06M16/00D06M2101/30
Inventor 徐燚超
Owner 徐燚超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com