A kind of reworkable adhesive and reworkable adhesive tape and a kind of adhesive tape stripping method

A technology of reworkable tape and reworkable tape, applied in the direction of adhesive, bonding method, adhesive type, etc., can solve the problems of electronic product shell deformation, tape breakage, battery rework, etc., to achieve good peeling performance, easy toxicity, The effect of improving low temperature resistance

Active Publication Date: 2021-11-12
DWELL PHOTOELECTRIC MATERIAL SUZHOU
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional acrylic strong-adhesive PET double-sided tapes do not have heavy-duty properties and can severely damage batteries or deform electronics housings when removed
Synthetic rubber-type pull-out glue solves the problem of battery rework or after-sales repair of electronic products to a certain extent, but during heavy work, the tape still has a high probability of breaking when pulled, and when the tape breaks, it increases the difficulty of rework

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of reworkable adhesive and reworkable adhesive tape and a kind of adhesive tape stripping method
  • A kind of reworkable adhesive and reworkable adhesive tape and a kind of adhesive tape stripping method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Preparation of Reworkable Adhesives

[0043] 50 parts of styrene-isoprene-styrene, 50 parts of styrene-butadiene-styrene, C 5 30 parts of petroleum resin, 70 parts of terpene phenol resin, 5 parts of liquid petroleum resin, 10 parts of nitrile rubber, 0.5 parts of phenolic antioxidant, 0.5 part of phosphite antioxidant, 15 parts of titanium dioxide, 110 parts of toluene and acetic acid Mix 110 parts of ethyl ester in a mixing tank to obtain a reworkable adhesive.

[0044] Making Reworkable Tapes

[0045] Reference attached figure 1 , coating a reworkable adhesive on the release surface of the first release profile layer to form an adhesive layer 1, and the thickness of the adhesive layer 1 is 100 μm.

[0046] Attach the release surface of the second release profile layer 2 to the side of the adhesive layer 1 facing away from the first release profile layer, and place it in a constant temperature oven for curing after winding. The adhesive layer 1 is provided with a ...

Embodiment 2

[0052]Preparation of Reworkable Adhesives

[0053] 50 parts of styrene-isoprene-styrene, 50 parts of styrene-butadiene-styrene, C 5 40 parts of petroleum resin, 60 parts of terpene phenol resin, 5 parts of liquid petroleum resin, 10 parts of nitrile rubber, 0.5 part of phenolic antioxidant, 0.5 part of phosphite antioxidant, 15 parts of titanium dioxide, 110 parts of toluene and acetic acid Mix 110 parts of ethyl ester in a mixing tank to obtain a reworkable adhesive.

[0054] Making Reworkable Tapes

[0055] A reworkable adhesive is coated on the release surface of the first release profile layer to form an adhesive layer, and the thickness of the adhesive layer is 100 μm.

[0056] Attach the release surface of the second release profile layer to the side of the adhesive layer facing away from the first release profile layer, roll it up and place it in a constant temperature oven for curing. The adhesive layer adopts a die-cutting method to open a plurality of grooves pene...

Embodiment 3

[0061] Preparation of Reworkable Adhesives

[0062] 50 parts of styrene-isoprene-styrene, 50 parts of styrene-butadiene-styrene, C 5 50 parts of petroleum resin, 50 parts of terpene phenol resin, 5 parts of liquid petroleum resin, 10 parts of nitrile rubber, 0.5 part of phenolic antioxidant, 0.5 part of phosphite antioxidant, 15 parts of titanium dioxide, 110 parts of toluene and acetic acid Mix 110 parts of ethyl ester in a mixing tank to obtain a reworkable adhesive.

[0063] Making Reworkable Tapes

[0064] A reworkable adhesive is coated on the release surface of the first release profile layer to form an adhesive layer, and the thickness of the adhesive layer is 100 μm.

[0065] Attach the release surface of the second release profile layer to the side of the adhesive layer facing away from the first release profile layer, roll it up and place it in a constant temperature oven for curing. The adhesive layer adopts a die-cutting method to open a plurality of grooves pen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
softening pointaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a reworkable adhesive, a reworkable adhesive tape and a tape stripping method. The reworkable adhesive includes the following components: 95-105 parts of synthetic rubber, 100-110 parts of tackifying resin, 8-12 parts of nitrile rubber, 0.5-1.5 parts of anti-aging agent, 10-20 parts of color paste, 210-100 parts of solvent 230 copies. The reworkable adhesive tape includes a release profile layer and an adhesive layer. The adhesive layer is provided with a plurality of interconnected grooves, and at least one groove forms a liquid inlet in the adhesive layer. The adhesive layer of the reworkable tape is attached between the first part and the second part, and the debonding agent is dripped from the liquid inlet until the debonding agent flows into the groove of the adhesive layer evenly, and the second part is pulled out The second part is separated from the adhesive layer, and then the adhesive layer is pulled to separate the adhesive layer from the first part to complete tape peeling. The reworkable adhesive tape of the present invention has good peeling performance on the surfaces of SUS boards, anode aluminum boards, PC boards, aluminum-plastic films, etc., and has good impact resistance performance, and is not easy to break when peeling off.

Description

technical field [0001] The invention relates to the technical field of bonding technology of electronic accessories, in particular to a reworkable adhesive, a reworkable adhesive tape and a tape stripping method. Background technique [0002] In electronic products such as smartphones and tablets, PET double-sided tapes or synthetic rubber-type pull-out adhesives are commonly used to fix batteries on both sides with strong adhesion polyacrylate pressure-sensitive adhesives. When electronic products are reworked or repaired after sales, the adhesive tape needs to be removed first. Traditional acrylic strong-adhesive PET double-sided tapes do not have heavy-duty properties, and when removed, can severely damage batteries or deform electronics cases. Synthetic rubber-type pull-out glue solves the problem of battery rework or after-sales repair of electronic products to a certain extent, but during heavy work, the tape still has a high probability of breaking when pulled, and w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J145/00C09J153/02C09J157/02C09J109/02C09J7/30C09J7/40C09J5/00
CPCC08L2205/025C08L2205/035C08L2207/04C09J5/00C09J145/00C09J153/02C09J157/02C09J2203/326C09J7/30C09J7/40C08L57/02C08L53/02C08L9/02C08L45/00
Inventor 袁勇慕鹏燕管丹陈余谦
Owner DWELL PHOTOELECTRIC MATERIAL SUZHOU