A kind of hierarchical porous pole piece and its preparation method and application

A technology of layers and pole pieces, applied in the field of lithium ion battery pole pieces and their preparation, can solve the problems of affecting the adhesion performance of the pole pieces and the shedding of the active material of the pole pieces, so as to accelerate the diffusion of lithium ions, improve the uniformity, and control the strong effect

Active Publication Date: 2021-10-15
CENT SOUTH UNIV
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this method of mixing solvents can use the volatilization of the solvent to create pores, due to the uniform distribution of the solvent, it will affect the bonding performance of the pole piece during the evaporation process, and it is easy to cause the active material on the pole piece to fall off.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hierarchical porous pole piece and its preparation method and application
  • A kind of hierarchical porous pole piece and its preparation method and application
  • A kind of hierarchical porous pole piece and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0097] LiFePO 4 , PVDF, acetylene black, and NMP agent are mixed according to 8:1:1, and 0.8% (as LiFePO 4 , PVDF, the total weight of acetylene black as a benchmark) has an average particle size of 1000nm elemental sulfur powder (particle size standard deviation σ=5nm). Mix evenly to be slurry A (in slurry A, NMP content is 70wt.%);

[0098] LiFePO 4 , PVDF, acetylene black, and NMP agent are mixed according to 8:1:1, and 1.5% (as LiFePO 4 , PVDF, the total weight of acetylene black as a basis) has an average particle size of 100nm elemental sulfur powder (particle size standard deviation σ=5nm). Mix evenly to form slurry B (in slurry B, the NMP content is 70wt.%).

[0099] Coat the slurry A on the aluminum foil, control the coating thickness to 20 μm, and dry at 110°C for 3 hours; after drying, apply the slurry B on the pole piece, control the coating thickness to 60 μm, set Dry at 110°C for 3 hours; after drying, compact it, then place the pole piece at 180°C and dry f...

Embodiment 2

[0103] LiCoO 2 , PVDF, acetylene black, and NMP agent are mixed according to 9:0.5:1, and 0.5% (as LiCoO 2 , PVDF, the total weight of acetylene black as a basis) has an average particle size of 700nm elemental sulfur powder (standard deviation of particle size σ=5nm). Mix evenly to be slurry A (in slurry A, NMP content is 72wt.%);

[0104] LiCoO 2 , PVDF, acetylene black, and NMP agent are mixed according to 9:0.5:1, and 2% (as LiCoO 2 , PVDF, the total weight of acetylene black as a basis) has an average particle size of 10nm elemental sulfur powder (standard deviation of particle size σ=5nm). Mix evenly to form slurry B (in slurry B, the NMP content is 72wt.%).

[0105] Coat the slurry A on the aluminum foil, control the coating thickness to 10 μm, and dry at 80°C for 3 hours; after drying, apply the slurry B on the pole piece, control the coating thickness to 100 μm, and place Dry at 80°C for 3 hours; after drying, compact it, then place the pole piece at 200°C and dr...

Embodiment 3

[0108] LiFePO 4 , PVDF, carbon nanotubes, and NMP agent are mixed according to 9:1:1, and 1.5% (as LiFePO 4 , PVDF, based on the total weight of carbon nanotubes) with an average particle size of 500nm elemental sulfur powder (standard deviation of particle size σ=5nm). Mix evenly to be slurry A (in slurry A, NMP content is 80wt.%);

[0109] LiFePO 4 , PVDF, carbon nanotubes, and NMP agent are mixed according to 9:1:1, and 1.8% (as LiFePO 4 , PVDF, based on the total weight of carbon nanotubes) with an average particle size of 300nm elemental sulfur powder (standard deviation σ=5nm of particle size). Mix evenly to form slurry B (in slurry B, the NMP content is 80wt.%).

[0110] Coat the slurry A on the aluminum foil, control the coating thickness to 15 μm, and dry at 120°C for 3 hours; after drying, apply the slurry B on the pole piece, control the coating thickness to 80 μm, and place Dry at 120°C for 3 hours; after drying, place the pole piece at 190°C for 50 minutes. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a layered porous pole piece and a preparation method thereof; the pore structure of the pole piece is regulated and controlled in stages by using graded coating and the addition of a pore-forming agent, which not only improves the liquid absorption capacity of the pole piece, but also ensures the activity of the pole piece. The maximization of the material can ensure the energy density of the battery on the basis of improving the electrochemical performance of the pole piece. The pole piece and the lithium piece are assembled into a button battery, which proves that the material exhibits excellent electrochemical performance, can effectively reduce electrode polarization, and improve the energy density and cycle stability of the battery.

Description

technical field [0001] The invention relates to a lithium-ion battery pole piece and a preparation method thereof, belonging to the field of lithium-ion batteries. Background technique [0002] Energy is an important material basis for developing the national economy and improving people's living standards, and it is also an important factor that directly affects economic development. Since the beginning of the 21st century, problems such as resource shortage, environmental pollution, and greenhouse effect caused by traditional energy utilization methods have become increasingly prominent. Improving the energy structure and developing efficient and clean new energy sources has become a global consensus. Lithium-ion batteries are favored by people because of their superior properties such as safety, environmental protection, high specific energy and good electrochemical performance. In order to improve the electrochemical performance of lithium ions and increase the energy d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/04H01M4/131H01M4/133H01M4/134H01M4/136H01M4/1391H01M4/1393H01M4/1395H01M4/1397H01M10/0525
CPCH01M4/0404H01M4/043H01M4/0471H01M4/131H01M4/133H01M4/134H01M4/136H01M4/1391H01M4/1393H01M4/1395H01M4/1397H01M10/0525Y02E60/10
Inventor 赖延清张治安王麒羽洪波向前张凯方静
Owner CENT SOUTH UNIV