Thermocuring quantum dot ink and preparation method and use method thereof

A technology of quantum dots and thermal curing, which is applied in inks, applications, household appliances, etc., can solve the problems of unfavorable industrial production, difficult long-term storage, easy agglomeration and precipitation of inks, etc., and achieve improved adhesion, uniform dispersion, and leveling effects Good results

Inactive Publication Date: 2020-08-07
AENEQ CO LTD
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ink used in this inkjet process is generally used for the preparation of quantum dot films of electroluminescent components. This ink is easy to agglomerate and precipitate, and it is not easy to store for a long time, which is not conducive to industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Add 53 parts of cyclohexanone as a solvent in the stirred tank, stir at a stirring speed of 400r / min under normal temperature and pressure; add 25 parts of bisphenol A epoxy solid resin, increase the speed to 3000r / min, and stir for 3 hours Filtrate to obtain the epoxy resin solution, and the epoxy resin solution adds 2 parts of hyperbranched macromolecule dispersants, 1 part of polyether modified silicone defoamer, 15 parts of oil-soluble quantum dots successively under 600r / min rotating speed , 1 part of modified acrylate copolymer and 3 parts of amino-type silane coupling agent, and stir evenly to obtain quantum dot ink.

Embodiment 2

[0018] Add 53 parts of cyclohexanone as a solvent in the stirred tank, stir at a stirring speed of 400r / min under normal temperature and pressure; add 30 parts of bisphenol A epoxy solid resin, increase the speed to 3000r / min, and stir for 3 hours Filtrate to obtain epoxy resin solution, epoxy resin solution adds 2 parts of hyperbranched macromolecule dispersants, 1 part of polyether modified silicone defoamer, 10 parts of oil-soluble quantum dots successively under 600r / min rotating speed , 1 part of modified acrylate copolymer and 3 parts of amino-type silane coupling agent, and stir evenly to obtain quantum dot ink.

Embodiment 3

[0020] A kind of using method of thermosetting quantum dot ink, by weight ratio, quantum dot ink is mixed with polyisocyanate, alicyclic amine, quantum dot ink: polyisocyanate: alicyclic amine=10:1:1, mixing After uniformity, defoaming treatment, and then printed on the glass substrate by gravure pad printing or screen printing, the thickness is 10 μm, and baked at 150 ° C for 10 minutes to obtain the quantum dot light-color conversion film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
sizeaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses thermocuring quantum dot ink and a preparation method and a use method thereof. The thermocuring quantum dot ink comprises the following components in parts by weight: 1-30 parts of quantum dots, 20-50 parts of epoxy resin, 30-75 parts of a solvent, 1-3 parts of a dispersing agent, 0.1-2 parts of an antifoaming agent, 0.5-2 parts of a leveling agent and 1-5 parts of a glassadhesion promoter. The thermocuring quantum dot photochromic conversion film ink provided by the invention can be printed on a glass substrate, is mixed with a flexible curing agent, does not blister, has a good leveling effect and uniform quantum dot dispersion, and is suitable for an intaglio pad printing process and a silk-screen printing process.

Description

technical field [0001] The invention belongs to the technical field of quantum dot inks, and in particular relates to a thermosetting quantum dot ink, a preparation method and a use method thereof. Background technique [0002] After 20 years of development, my country's major display panel manufacturers, such as BOE, Tianma, China Star, etc., have dominated the traditional LCD panel market and become leaders in the international market. In order to improve competitiveness, major international manufacturers such as Samsung Electronics have turned to the development of higher-quality quantum dot (Quantum Dot, QD) display panels, using blue OLED or μ-LED through the quantum dot light color conversion film (QD Color Change Film) ,QD-CCF), can realize wide color gamut display, and has energy-saving effect. [0003] At present, quantum dot photochromic conversion film (QD-CCF) is produced by using the same method of yellow light lithography as the production of color filters, bu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102C09D11/50C09D11/03
CPCC09D11/102C09D11/50C09D11/03
Inventor 赖耀升江建志
Owner AENEQ CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com