Modified graphene oxide epoxy resin composite coating and preparation method thereof
A technology of ethylene epoxy resin and composite coating, which is applied in the direction of epoxy resin coating, anti-corrosion coating, coating, etc., can solve the problems of insufficient anti-corrosion coating technology and performance, and achieve the effect of compact structure and good anti-corrosion performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025] Example 1
[0026] (1) Add 10 g of sodium bicarbonate (NaHCO) to 500 ml of distilled water 3 ) And 186.6 mg of ethylenediaminetetraacetic acid disodium (EDTA.2Na), stir evenly to form a dialysate, put the dialysis bag in the dialysate and boil for 15 minutes, and then wash the dialysis bag with distilled water several times before cleaning the dialysis Place the bag in 1 mmol / L EDTA.2Na solution (PH=8.0) and boil for 10 min;
[0027] (2) Dissolve an appropriate amount of graphite oxide slurry in distilled water, sonicate it for 30 minutes, then put it into a cooled dialysis bag and stir magnetically in a beaker containing distilled water for 3 days. Finally, ultrasonic peeling was performed 3 times at 0°C by an ultrasonic cell disruptor for 30min to obtain a dispersion of graphene oxide;
[0028] (3) Weigh 10 ml of graphene oxide dispersion and place it in a beaker and add 160 ml of distilled water and place it in an oven to dry for 5 hours. The measured solid content is 9 m...
Example Embodiment
[0035] Example 2
[0036] (1) Add 10 g of sodium bicarbonate (NaHCO) to 500 ml of distilled water 3 ) And 186.6 mg of ethylenediaminetetraacetic acid disodium (EDTA.2Na), stir evenly to form a dialysate, put the dialysis bag in the dialysate and boil for 15 minutes, and then wash the dialysis bag with distilled water several times before cleaning the dialysis Place the bag in 1 mmol / L EDTA.2Na solution (PH=8.0) and boil for 10 min;
[0037] (2) Dissolve an appropriate amount of graphite oxide slurry in distilled water, sonicate it for 40 min, then put it into a cooled dialysis bag and stir it magnetically in a beaker containing distilled water for 3 days. Finally, ultrasonic peeling was carried out 4 times for 40min at 5°C by an ultrasonic cell disruptor to obtain a dispersion of graphene oxide;
[0038] (3) Weigh 10ml of graphene oxide dispersion and place it in a beaker and add 160ml of distilled water and place it in an oven to dry for 5h. The measured solid content is 9mg / ml;
...
Example Embodiment
[0045] Example 3
[0046] (1) Add 10 g of sodium bicarbonate (NaHCO) to 500 ml of distilled water 3 ) And 186.6 mg of ethylenediaminetetraacetic acid disodium (EDTA.2Na), stir evenly to form a dialysate, put the dialysis bag in the dialysate and boil for 15 minutes, and then wash the dialysis bag with distilled water several times before cleaning the dialysis Place the bag in 1 mmol / L EDTA.2Na solution (PH=8.0) and boil for 10 min;
[0047] (2) Dissolve an appropriate amount of graphite oxide slurry in distilled water, sonicate it for 30 min, then put it into a cooled dialysis bag and stir it magnetically in a beaker filled with distilled water for 4 days. Finally, ultrasonic peeling was performed 4 times for 40min at 3°C by an ultrasonic cell disruptor to obtain a dispersion of graphene oxide;
[0048] (3) Weigh 10ml of graphene oxide dispersion and place it in a beaker and add 160ml of distilled water and place it in an oven to dry for 5h. The measured solid content is 9mg / ml; ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap