Acidic water glass grouting material and preparation method thereof

A grouting material and acid water technology, applied in the field of grouting materials for construction, can solve the problems of low strength of solid sand body, application limitation, easy weathering and collapsing, etc., and achieve a simple preparation method, low production cost and strong permeability. Effect

Active Publication Date: 2020-08-25
INST OF MULTIPURPOSE UTILIZATION OF MINERAL RESOURCES CHINESE ACAD OF GEOLOGICAL SCI
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the acidic water glass material still has disadvantages such as low strength of sand consolidation body and easy weathering and collapse, which limit its application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1. A kind of acid water glass grouting material, by weight, comprises water glass 70mL, sulfuric acid solution 50mL and ethylene glycol 5mL;

[0033] Wherein, the modulus of water glass is 2.6, the Baume degree is 10Be°; the mass concentration of sulfuric acid solution is 5%.

[0034] 2. a preparation method of acidic water glass grouting material, comprising the following steps:

[0035] S1. take water glass, sulfuric acid solution and ethylene glycol by weighing;

[0036] S2. Get sulfuric acid solution and ethylene glycol and mix uniformly, obtain mixed solution;

[0037] S3. Stir the water glass into the mixed solution, and mix evenly to obtain the product.

Embodiment 2

[0039] 1. An acidic water glass grouting material, by weight, comprising water glass 80mL, sulfuric acid solution 20mL and propylene glycol 20mL;

[0040] Wherein, the modulus of water glass is 2.6, the degree of Baume is 10Be°; the mass concentration of sulfuric acid solution is 15%.

[0041] 2. a preparation method of acidic water glass grouting material, comprising the following steps:

[0042] S1. take by weighing water glass, sulfuric acid solution and propylene glycol by proportioning;

[0043] S2. Get sulfuric acid solution and propylene glycol and mix uniformly, obtain mixed solution;

[0044] S3. Stir the water glass into the mixed solution, and mix evenly to obtain the product.

Embodiment 3

[0046] 1. An acidic water glass grouting material, by weight, comprising water glass 10mL, sulfuric acid solution 75mL and butanediol 10mL;

[0047] Wherein, the modulus of water glass is 2.6, the Baume degree is 20Be°; the mass concentration of sulfuric acid solution is 15%.

[0048] 2. a preparation method of acidic water glass grouting material, comprising the following steps:

[0049] S1. take by weighing water glass, sulfuric acid solution and butanediol by proportioning;

[0050] S2. get sulfuric acid solution and butanediol and mix evenly, obtain mixed solution;

[0051] S3. Stir the water glass into the mixed solution, and mix evenly to obtain the product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of grouting materials, and discloses an acidic water glass grouting material which comprises the following components, by weight: 11-67 parts of water glass, 17-79 parts of an acid solution and 4-17 parts of water-soluble polyol. The invention also discloses a preparation method of the acidic water glass grouting material. The preparation method comprises the following steps: S1, weighing water glass, an acid solution and water-soluble polyol according to a ratio; S2, uniformly mixing the acid solution with water-soluble polyol to obtain a mixed solution; and S3, adding the water glass into the mixed solution in a stirring mode, and uniformly performing mixing, thereby obtaining the product. According to the acidic water glass grouting materialdisclosed by the invention, through the synergistic effect of the water-soluble polyhydric alcohol and the acid solution, the effects of better controlling the gelation process and the gelation time of the sodium silicate, improving the compressive strength, the stability and the viscosity of the acidic sodium silicate grouting material, reducing the brittleness of the grouting material and enhancing the acid resistance and the water resistance of the sodium silicate gel are achieved.

Description

technical field [0001] The invention relates to the technical field of grouting materials for construction, in particular to an acidic water glass grouting material and a preparation method thereof. Background technique [0002] Grouting is an engineering activity, which refers to using supporting mechanical equipment and adopting a reasonable grouting process to inject grout into the gaps, cracks, roadways or cavities of rocks and soils, so that the grout can be diffused, coagulated and hardened to reduce Improve the permeability of rock and soil, enhance its strength and stability, and achieve the purposes of rock and soil reinforcement, seepage prevention and water blocking. Commonly used grouting materials include cement-based grouting materials, epoxy resin grouting materials, phenolic resin grouting materials, polyurethane grouting materials and water glass grouting materials. [0003] Water glass is an aqueous solution of alkali metal silicate, usually referred to as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/26C04B22/14C04B24/02
CPCC04B28/26C04B22/141C04B24/02C04B2201/50
Inventor 李超舒荣波程蓉徐璐邓敏
Owner INST OF MULTIPURPOSE UTILIZATION OF MINERAL RESOURCES CHINESE ACAD OF GEOLOGICAL SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products