Thermoplastic elastomer anti-sticking agent, and preparation method and application thereof
A technology of thermoplastic elastomer and thermoplastic elasticity, applied in the direction of coating, etc., can solve the problems of easy pollution, damage to molding catalyst, failure of molding catalyst, etc., and achieve the effect of not affecting the environment
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025] Example one
[0026] Thermoplastic elastomer release agent, composed of soybean oil fatty acid ethanolamide, isopropanol and water, in which the mass percentage of each component is:
[0027] Soybean oil fatty acid ethanolamide 20%
[0028] Isopropanol 20%
[0029] Water 60%.
[0030] The preparation method of the thermoplastic elastomer release agent, at 50℃, firstly, the soybean oil fatty acid ethanolamide and isopropanol are mixed to obtain a mixed solvent, and then the above mixed solvent is placed in water at 50℃ and stirred to make it uniformly dissolved , And finally get a thermoplastic elastomer release agent, wherein the mass percentage of soybean oil fatty acid ethanolamide in the thermoplastic elastomer release agent is 20%, and the mass percentage of isopropanol in the thermoplastic elastomer release agent is 20%, The mass percentage of water in the thermoplastic elastomer release agent is 60%.
Example Embodiment
[0031] Example two
[0032] Thermoplastic elastomer anti-sticking agent, composed of palm kernel oleic acid glycolamide, ethanol and water. The mass percentage of each component is:
[0033] Palm kernel oleic acid glycolamide 30%
[0034] Ethanol 30%
[0035] Water 40%.
[0036] The preparation method of thermoplastic elastomer release agent, at 40°C, firstly, palm kernel oleic acid glycolamide and ethanol are mixed to obtain a mixed solvent, and then the mixed solvent is placed in water at 40°C and stirred to make it uniformly dissolved. Finally, a thermoplastic elastomer release agent is obtained, wherein the mass percentage of palm kernel oleic acid glycolamide in the thermoplastic elastomer release agent is 30%, the mass percentage of ethanol in the thermoplastic elastomer release agent is 30%, and the water is The mass percentage in the thermoplastic elastomer release agent is 40%.
Example Embodiment
[0037] Example three
[0038] Thermoplastic elastomer anti-sticking agent, composed of coconut oleic acid glycolamide, methanol and water, in which the mass percentage of each component is:
[0039] Coconut oleic acid glycolamide 15%
[0040] Methanol 15%
[0041] Water 70%.
[0042] The preparation method of the thermoplastic elastomer release agent, at 60℃, firstly, the coconut oleic acid glycolamide and methanol are mixed to obtain a mixed solvent, and then the above mixed solvent is placed in water at 60℃ and stirred to make it uniformly dissolved. A thermoplastic elastomer release agent is obtained, wherein the mass percentage of coconut oleic acid glycolamide in the thermoplastic elastomer release agent is 15%, the mass percentage of methanol in the thermoplastic elastomer release agent is 15%, and water is in the thermoplastic elastomer The mass percentage in the body release agent is 70%.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap