A kind of preparation method of corrosion-resistant nodular malleable iron material

Abstract

The invention belongs to the technical field of material preparation, in particular to a preparation method of a corrosion-resistant ductile malleable iron material. A forming device used in the method comprises a bottom plate, a rotating shaft is rotatably installed on the top of the bottom plate, and a driving motor is fixed on the top of the bottom plate A rotating wheel is fixed on the top of the drive motor, a rotating ring is fixed on the surface of the rotating shaft, a synchronous belt is movably connected between the rotating wheel and the rotating ring, a placing table is fixed on the top of the rotating shaft, and the top of the placing table is There is a placing groove, the placing groove is used for placing the casting mold, and two brackets are fixed on the side wall of the placing platform; the invention presses and produces a sheet-shaped corrosion-resistant layer, so that the corrosion-resistant layer is distributed on the surface of the ductile malleable iron material, and is compatible with the ductile malleable cast iron material. The ductile malleable iron material is integrated into one, and it can still protect the ductile malleable iron material when forging, and at the same time reduce the use of nickel and chromium, reduce the cost of use, and retain the characteristics of the ductile malleable iron material to the maximum extent.

Description

technical field [0001] The invention belongs to the technical field of material preparation, in particular to a preparation method of corrosion-resistant nodular malleable cast iron material. Background technique [0002] Malleable cast iron is a cast iron made by casting molten iron with a certain chemical composition into a white blank, and then annealed. It has high strength, plasticity and impact toughness, and can partially replace carbon steel. Malleable cast iron is a high-strength and tough cast iron obtained from white cast iron through graphitization annealing. It has high strength, plasticity and impact toughness, and can partially replace carbon steel. Compared with gray cast iron, malleable cast iron has better strength and plasticity, especially better low-temperature impact performance, and better wear resistance and vibration damping than ordinary carbon steel. Because of its certain plasticity and toughness, this kind of cast iron is commonly known as mall...

AI Technical Summary

Problems solved by technology

[0003] There have also been some technical solutions for the preparation of malleable iron materials in the prior art, such as a Chinese patent with application number 2011100074675, which discloses a corrosion-resistant nodular malleable iron material and its preparation method. Steel wire and iron wire and nodular malleable iron Combined to form a good metallurgical bond, low carbon steel wire and iron wire are distributed in the ductile iron, which has a good strengthening and toughening effect on the material, and the ductile malleable iron molten iron enters the mold cavity and contacts the nickel on the surface of the steel wire and iron wire Finally, the Ni and Cr on the surface of the wire melt into the molten iron, and the C in the molten iron reacts with Si and Ni and Cr on the surface of the steel wire and iron wire to form special compounds Ni3C, Ni3Si, Cr3Si and Cr23C6 with higher hardness than cementite. This special compound further improves the corrosion resistance of the material, but the special compound generated on the surface of the material is not uniform, which leads to the problem of uneven corrosion resistance of the material during use, which affects the overall use effect of the material. At the same time, the internal nickel and Chromium cannot be used, which wastes nickel and chromium. Accordingly, the present invention proposes a method for preparing corrosion-resistant ductile malleable iron material

Images