A kind of frost-resistant concrete and preparation method thereof
A technology of concrete and antifreeze, applied in the field of concrete, can solve the problems of concrete cracking, concrete compressive strength decrease, affecting concrete durable frost resistance, etc., to achieve the effect of promoting solidification, improving workability, and improving frost resistance performance
Active Publication Date: 2022-04-19
佛山市南海区恒锵混凝土有限公司
View PDF6 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0005] Among them, the calcium formate in the above-mentioned prior art tends to cause cracks in the concrete, so that the compressive strength of the concrete decreases rapidly with the repeated freeze-thaw tests, thereby affecting the durable frost resistance of the concrete
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1-12
[0063] The components and proportions of the antifreeze concrete in Examples 1-12 are shown in Table 2.
[0064] Component and proportioning (unit / kg) of antifreeze concrete in table 2 embodiment 1-12
[0065]
Embodiment 1
[0068] The ratio of propylene glycol, glycerol, KH550 and sodium dodecylbenzenesulfonate in the antifreeze agent in Example 1 is 2.5:1:0.2:0.3;
Embodiment 6
[0069] The ratio of propylene glycol, glycerol, KH550 and sodium dodecylbenzenesulfonate in the antifreeze agent in Example 6 is 2:1.5:0.1:0.4;
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Login to view more
Abstract
The invention relates to the field of concrete, and specifically discloses a frost-resistant concrete and a preparation method thereof. Freeze-resistant concrete includes cement, fly ash, fine aggregate, coarse aggregate, water reducer, antifreeze agent and water; the antifreeze agent includes a weight ratio of (2.0‑2.5): (1.0‑1.5): ( 0.1‑0.2): (0.3‑0.4) propylene glycol, glycerin, silane coupling agent and alkylbenzene sulfonate; the preparation method is: add water reducing agent and antifreeze agent to water for pre-mixing to obtain agent solution; uniformly mix fine aggregate and coarse aggregate to obtain an aggregate mixture; uniformly mix cement and fly ash to obtain a rubber mixture; uniformly mix the rubber mixture and aggregate mixture to obtain a premix; add to the premix admixture solution, and stir evenly to obtain frost-resistant concrete. The antifreeze concrete of the invention can be used for building concrete in low temperature regions, and has the advantage of good antifreeze performance.
Description
technical field [0001] The invention relates to the field of concrete, more specifically, it relates to a frost-resistant concrete and a preparation method thereof. Background technique [0002] Concrete refers to the artificial stone obtained by uniformly mixing, molding and hardening with cement as the main gel material, mixed with water, sand, stones, chemical additives and admixtures. With the expansion of urban areas, a large number of buildings need to be constructed, and concrete, as the most widely used building material in modern times, requires a large amount of preparation and use, and it is necessary to ensure that the concrete can be constructed normally, and it is also required that the concrete has sufficient strength after forming. strength. [0003] However, when concrete is constructed in a low-temperature environment, the free water in the concrete will cool down and transform from liquid to solid. On the one hand, solid free water cannot participate in ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B111/20
CPCC04B28/04C04B2111/20C04B14/02C04B14/06C04B2103/302C04B24/02C04B24/42C04B24/20C04B18/08C04B24/18
Inventor 蒲锦伦符卓亨张志伟
Owner 佛山市南海区恒锵混凝土有限公司
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap