Method for improving surface coating performance by treating rubber wood based on steam explosion method

A surface coating and rubber wood technology, applied in wood treatment, wood heat treatment, pressurized wood treatment, etc., can solve problems such as mildew, corrosion, poor adhesion, and reduced service life of coatings, and achieve hemicellulose The effect of content reduction, enhanced adhesion, and good brushing performance

Inactive Publication Date: 2020-10-27
安徽三和工艺品有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, wood products made of oak are prone to mildew and corrosion during use. Therefore, the surface needs to be treated for protection and to improve its service life. Usual

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] A method for improving the surface finish of rubber wood based on steam explosion method, comprising: lye treatment of oak, steam explosion treatment after lye treatment; said lye treatment is carried out under microwave assisted conditions; The alkali solution is obtained by mixing a strong alkali solution and a weak alkali solution; the mixing mass ratio of the strong alkali solution and the weak alkali solution is 3:1. The alkali solution is obtained by mixing a strong alkali solution and a weak alkali solution; the strong alkali solution is a sodium hydroxide solution; and the weak alkali solution is an aqueous ammonia solution. The mass fraction of the sodium hydroxide solution is 6%; the aqueous ammonia solution is a saturated aqueous ammonia solution. The lye treatment method is: adding oak to the lye for soaking treatment. The lye treatment adopts microwave-assisted treatment: when oak is immersed in lye, microwave heating treatment is performed, and the microwa...

Embodiment 2

[0064] A method for improving the surface finish of rubber wood based on steam explosion method, comprising: lye treatment of oak, steam explosion treatment after lye treatment; said lye treatment is carried out under microwave assisted conditions; The alkali solution is obtained by mixing a strong alkali solution and a weak alkali solution; the mixing mass ratio of the strong alkali solution and the weak alkali solution is 3:1.5. The alkali solution is obtained by mixing a strong alkali solution and a weak alkali solution; the strong alkali solution is a sodium hydroxide solution; and the weak alkali solution is an aqueous ammonia solution. The mass fraction of the sodium hydroxide solution is 8%; the aqueous ammonia solution is a saturated aqueous ammonia solution. The lye treatment method is: adding oak to the lye for immersion treatment. The lye treatment adopts microwave-assisted treatment: when oak is immersed in lye, microwave heating treatment is performed, and the mic...

Embodiment 3

[0066] A method for improving the surface finish of rubber wood based on steam explosion method, comprising: lye treatment of oak, steam explosion treatment after lye treatment; said lye treatment is carried out under microwave assisted conditions; The alkali solution is obtained by mixing a strong alkali solution and a weak alkali solution; the mixing mass ratio of the strong alkali solution and the weak alkali solution is 3:1.2. The alkali solution is obtained by mixing a strong alkali solution and a weak alkali solution; the strong alkali solution is a sodium hydroxide solution; and the weak alkali solution is an aqueous ammonia solution. The mass fraction of the sodium hydroxide solution is 7%; the aqueous ammonia solution is a saturated aqueous ammonia solution. The lye treatment method is: adding oak to the lye for immersion treatment. The lye treatment adopts microwave-assisted treatment: when oak is immersed in lye, microwave heating treatment is performed, and the mic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for improving surface coating performance by treating rubber wood based on a steam explosion method, and relates to the technical field of wood product treatment. Themethod comprises the steps that oak is subjected to alkali liquor treatment, and steam explosion treatment is conducted after alkali liquor treatment, wherein the alkali liquor treatment is carried out under a microwave-assisted condition, the alkali liquor is obtained by mixing a strong alkali solution and a weak alkali solution, and the mixing mass ratio of the strong alkali solution to the weakalkali solution is 3: (1-1.5); the oak surface treated through the method has better brushing performance, the binding force between the oak surface and a coating can be greatly improved, and therefore the oak surface can be used for a longer time, and the situation that the coating on the surface falls off too early is avoided.

Description

Technical field [0001] The invention belongs to the technical field of wood products, in particular to a method for improving the surface coating performance of rubber wood based on a steam explosion method. Background technique [0002] White oak and red oak are collectively referred to as oak, which is hard and heavy and has beautiful patterns. They are high-quality materials for making furniture, floors, and interior wood lines. The oak imported from abroad is divided into two types of commercial materials: white oak and red oak, namely white oak and red oak. Red oak is mainly produced in North America and Europe; white oak is mainly produced in Asia, Europe and North America. The wood structure of red oak and white oak is similar to that of Sawtooth oak and Quercus oak produced in China. [0003] The sapwood and heartwood of oak are slightly distinguished. The sapwood is grayish-yellow-white, and the color of the heartwood is variable, ranging from yellowish brown to reddish ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B27K3/32B27K3/20B27K5/00
CPCB27K3/20B27K3/32B27K5/0055B27K5/007B27K5/009
Inventor 徐治合徐蓝天徐艳云
Owner 安徽三和工艺品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap