Modified polypropylene air guide sleeve for van
A van and polypropylene technology, applied in the field of automobile spoilers, can solve the problems of high tensile strength and impact toughness, low use effect of spoilers, and easy deformation, etc., to achieve enhanced impact strength, Not easy to deform and improve the effect of bearing capacity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] A modified polypropylene fairing for a van, the raw materials of which include: 60kg of modified polypropylene, 20kg of polyethylene, 5kg of polyvinyl chloride, 5kg of maleic anhydride grafted polypropylene, 1kg of maleic anhydride, potassium titanate Whiskers 5kg, magnesium stearate 2kg, glass fiber 10kg, allyl chloroacetate 0.1kg, 3-methyl-2-butenal 0.5kg, tetraethoxymethane 1kg, paraffin 2kg, zinc oxide 0.7kg, Pigment 0.3kg.
[0023] During the preparation of modified polypropylene, mix 10kg of nano-silica, 1kg of silane coupling agent KH570, and 100kg of 65% ethanol solution, reflux and stir at 80°C for 20min, add 50kg of polypropylene, heat up to 140°C and reflux and stir 6min, filtered, washed, dried, and pulverized to obtain modified polypropylene.
[0024] The preparation method of the above-mentioned van truck with modified polypropylene shroud comprises the following steps:
[0025] Put the raw materials in a mixer with a rotating speed of 400r / min, and mix ...
Embodiment 2
[0029] A modified polypropylene fairing for a van, the raw materials of which include: 80kg of modified polypropylene, 10kg of polyethylene, 15kg of polyvinyl chloride, 2kg of maleic anhydride grafted polypropylene, 2kg of maleic anhydride, potassium titanate Whiskers 1kg, magnesium stearate 4kg, glass fiber 4kg, allyl chloroacetate 0.5kg, 3-methyl-2-butenal 0.1kg, tetraethoxymethane 2kg, paraffin 1kg, zinc oxide 1kg, pigment 1kg.
[0030] During the preparation of modified polypropylene, mix 4kg of nano-silica, 2kg of silane coupling agent KH570, and 50kg of 80% ethanol solution, stir at 70°C for 30 minutes, add 40kg of polypropylene, heat up to 160°C and stir at reflux 2min, filtered, washed, dried, and pulverized to obtain modified polypropylene.
[0031] The preparation method of the above-mentioned van truck with modified polypropylene shroud comprises the following steps:
[0032] Put the raw materials in a mixer with a rotating speed of 600r / min, and mix them at 70°C ...
Embodiment 3
[0036] A modified polypropylene fairing for a van, the raw materials of which include: 65kg of modified polypropylene, 17kg of polyethylene, 8kg of polyvinyl chloride, 4kg of maleic anhydride grafted polypropylene, 1.3kg of maleic anhydride, titanic acid Potassium whiskers 4kg, magnesium stearate 2.5kg, glass fiber 8kg, allyl chloroacetate 0.2kg, 3-methyl-2-butenal 0.4kg, tetraethoxymethane 1.3kg, paraffin 1.8kg, oxidation Zinc 0.9kg, pigment 0.4kg.
[0037] During the preparation of modified polypropylene, mix 8kg of nano-silica, 1.3kg of silane coupling agent KH570, and 80kg of 70% ethanol solution, reflux and stir at 77°C for 22min, add 47kg of polypropylene, and heat up to 145°C to reflux Stir for 5 minutes, filter, wash, dry, and pulverize to obtain modified polypropylene.
[0038] The preparation method of the above-mentioned van truck with modified polypropylene shroud comprises the following steps:
[0039] Put the raw materials in a mixer with a rotating speed of 45...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com