Preparation method of natural coconut fiber reinforced epoxy resin composite fabric

A technology of coconut shell fiber and composite fabric, which is applied in the field of preparation of natural coconut shell fiber reinforced epoxy resin composite fabric, can solve serious, unfavorable environmental protection, difficult to degrade and other problems, achieve good elastic modulus and tensile strength, avoid The effect of coir fiber in contact with water to enhance elongation

Pending Publication Date: 2020-12-11
HAINAN UNIVERSITY
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Geosynthetics are widely used in engineering reinforcement because of their low cost, simple construction and good reinforcement effect. However, most of the traditional geosynthetics are non-renewable resources, not easy to degrade, and their production process is more polluted, which is not conducive to environmental protection.
The coconut shell fiber is natural pollution-free, green, renewable, strong toughness, high strength, and wide source. It is an ideal natural reinforcement material. It will degrade in one or two years in the state, and it is not suitable for engineering projects with a long operating time, and it needs to be treated with anti-corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of natural coconut fiber reinforced epoxy resin composite fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] In the description of the present application, it should be understood that the terms "center", "longitudinal", "transverse", "upper", "lower", "front", "rear", "left", "right", " The orientation or positional relationship indicated by "vertical", "horizontal", "top", "bottom", "inner", "outer", etc. is based on the orientation or positional relationship shown in the drawings, and is only for the convenience of describing the present application and The description is simplified, rather than indicating or implying that the device or element referred to must have a specific orientation, be constructed in a specific orientation, and operate, and thus should not be construed as limiting the application. In the description of the present application, unless otherwise specified, "plurality" means two or more.

[0034] figure 1 It is a schematic flow chart of the preparation method of the exemplary natural coconut fiber reinforced epoxy resin composite fabric of the present ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a natural coconut fiber reinforced epoxy resin composite fabric. The preparation method of the natural coconut shell fiber reinforced epoxy resin composite fabric comprises the steps of trimming prepared coconut shell fibers into fiber segments with the length of 0.5-5 cm; mixing and stirring the fiber segments and molten epoxy resin for 10-20 min in a spherical stirrer according to the mass ratio of 5%-20% to form uniformly-dispersed composite resin melt; coating a first layer of release agent on the inner surface of the mold, standing, coatinga second layer of release agent after the release agent is solidified, and slowly injecting the composite resin melt into the mold after the two layers of release agents are completely solidified; scraping and roughly machining the surface of the composite fabric through a scraper, and conducting curing forming in the room temperature state; and demolding and trimming the cured rough machining composite fabric to form the reinforced composite fabric. The preparation method of the natural coconut fiber reinforced epoxy resin composite fabric has the advantage of high durability.

Description

technical field [0001] The application relates to a preparation method, in particular to a preparation method of a natural coconut fiber reinforced epoxy resin composite fabric. Background technique [0002] Geosynthetics are widely used in engineering reinforcement due to low cost, simple construction and good reinforcement effect. However, traditional geosynthetics are mostly non-renewable resources, not easy to degrade, and their production process is more polluting, which is not conducive to environmental protection. The coconut shell fiber is natural pollution-free, green, renewable, strong toughness, high strength, and wide source. It is an ideal natural reinforcement material. It will degrade in one or two years in the state, and it is not suitable for engineering projects with a long operating time, and it needs to be treated with anti-corrosion. Contents of the invention [0003] Based on this, the purpose of this application is to provide a preparation method fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L63/00C08L97/02C08J5/06
CPCC08J5/06C08J5/045C08J2363/00C08J2497/02
Inventor 李良勇曹乾黄睿龙郑书雅
Owner HAINAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com