Bamboo fiber powder, bamboo fiber composite board and preparation method thereof

A technology of bamboo fiber composite and bamboo fiber powder, which is used in wood heating, tool manufacturing, wood treatment, etc.

Active Publication Date: 2022-04-08
HUNAN HENGXIN NEW BUILDING MATERIALS CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The main purpose of the present invention is to provide a kind of bamboo fiber powder, bamboo fiber composite board and preparation method thereof, to solve the problem that existing bamboo fiber powder is modified by chemical reagents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A preparation method of bamboo fiber powder, comprising the following steps:

[0026] After steaming the bamboo slices, crush them along the bamboo fiber growth direction without breaking the bamboo slice fibers to obtain bamboo filaments;

[0027] Drying the bamboo filaments, and irradiating them with a microwave with a power of 180-220W for 40-45 minutes to obtain semi-carbonized bamboo filaments;

[0028] After the semi-carbonized bamboo silk is ground into bamboo powder, it is irradiated with a microwave with a power of 12-14KW for 80-90s, and heated to obtain the bamboo fiber powder.

[0029] Remove bamboo green and bamboo yellow from bamboo, and cut into bamboo slices. Bamboo chip steaming can remove soluble organic matter in bamboo, and at the same time make the bamboo chip absorb enough water, which is convenient for subsequent crushing. The crushing direction is the growth direction of the bamboo fiber, so as to avoid the breakage of the bamboo fiber.

[003...

Embodiment 1

[0056] One, preparing bamboo fiber powder comprises the following steps:

[0057] Bamboo slices were steamed at 105°C for 6 hours, cooled in ice water, taken out and crushed along the bamboo fiber growth direction without breaking the bamboo fibers to obtain bamboo filaments.

[0058] The bamboo filaments were dried and irradiated under a microwave with a power of 180W for 45 minutes to obtain semi-carbonized bamboo filaments.

[0059] The semi-carbonized bamboo shreds were ground into bamboo powder, irradiated with a microwave with a power of 12KW for 90s, and heated at 240°C for 60 minutes to obtain the bamboo fiber powder.

[0060] Two, the preparation method of bamboo fiber composite plate, comprises the following steps:

[0061] Prepare 55 parts of bamboo fiber powder, 95 parts of calcium carbonate powder, 50 parts of polyvinyl chloride resin powder, 10 parts of blowing agent, 2 parts of coupling agent, 12 parts of stabilizing agent, 1 part of plasticizer; Described calc...

Embodiment 2

[0067] One, preparing bamboo fiber powder comprises the following steps:

[0068] Bamboo slices were steamed at 115°C for 5 hours, cooled in ice water, taken out and crushed along the growth direction of bamboo fibers without breaking the bamboo fibers to obtain bamboo filaments.

[0069] The bamboo filaments were dried and irradiated under a microwave with a power of 220W for 40 minutes to obtain semi-carbonized bamboo filaments.

[0070] The semi-carbonized bamboo shreds were ground into bamboo powder, irradiated with a microwave with a power of 14KW for 80s, and heated at 240°C for 50 minutes to obtain the bamboo fiber powder.

[0071] Two, the preparation method of bamboo fiber composite plate, comprises the following steps:

[0072] Prepare 60 parts of bamboo fiber powder, 80 parts of calcium carbonate powder, 60 parts of polyvinyl chloride resin powder, 5 parts of foaming agent, 2 parts of coupling agent, 8 parts of stabilizing agent, 1 part of plasticizer; Described ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a bamboo fiber powder, a bamboo fiber composite board and a preparation method thereof, comprising the following steps: after cooking the bamboo chips, crushing them along the growth direction of the bamboo fibers without breaking the bamboo fibers to obtain bamboo filaments; The bamboo silk is dried, and irradiated under a microwave with a power of 180-220W for 40-45 minutes to obtain semi-carbonized bamboo silk; after the semi-carbonized bamboo silk is ground into bamboo powder, it is irradiated with a microwave with a power of 12-14KW for 80- 90s, heating to obtain the bamboo fiber powder. The above-mentioned bamboo fiber powder is combined with microwave and heating technology to form a large number of pores on the surface and inside of the bamboo powder, thereby increasing the surface area of ​​the bamboo fiber powder, which is better combined with other components in the bamboo fiber composite board such as resin and calcium powder .

Description

technical field [0001] The invention belongs to the technical field of plate processing, and in particular relates to bamboo fiber powder, bamboo fiber composite plate and a preparation method thereof. Background technique [0002] Bamboo has a short growth cycle and abundant resources, and bamboo products are widely used in daily life. Bamboo fiber composite board is a product that uses bamboo as raw material for deep processing. Among them, bamboo fiber extracted from bamboo is one of the important raw materials. Bamboo fiber has the characteristics of good air permeability, instant water absorption, strong wear resistance and good dyeability. The interface performance of bamboo fiber is poor, and it needs to be modified to better combine with resin and improve the strength of bamboo fiber and bamboo fiber composite board. Usual modification method all is to adopt chemical reagent to modify bamboo fiber, but this kind of mode does not match with the concept of green env...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B27K5/00B27L11/06B28B3/00
CPCB27K5/001B27K5/0055B27L11/06B28B3/00
Inventor 向湘军王杰超袁仕云王水平刘晶谭海斌
Owner HUNAN HENGXIN NEW BUILDING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap