Super-soft and super-fluffy spun-bonded non-woven fabric and preparation method thereof

A spun-bonded non-woven fabric, ultra-fluffy technology, applied in the direction of non-woven fabrics, textiles and papermaking, conjugated synthetic polymer artificial filaments, etc., can solve the problem of poor softness and poor mechanical properties of spun-bonded non-woven fabrics , poor waterproof performance and other problems, to achieve the effect of improving anti-ultraviolet aging performance, improving anti-oxidative aging performance, and high rebound rate

Active Publication Date: 2020-12-18
FUJIAN GUAN HONG IND
View PDF17 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. Spunbonded non-woven fabrics have poor softness, low bulkiness, low air permeability, low rebound rate and poor comfort;
[0007] 2. Poor waterproof performance;
[0008] 3. Poor comprehensive performance such as mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Super-soft and super-fluffy spun-bonded non-woven fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] A kind of supersoft super fluffy spunbonded nonwoven fabric, described supersoft superfluffy spunbonded nonwoven fabric is made of the raw materials comprising following parts by weight:

[0056] 55-65 parts of polyethylene terephthalate,

[0057] 25-32 parts of polyurethane elastomer,

[0058] 7-10 parts of polyhexamethylene adipate,

[0059] 5-7 parts of linear low-density polyethylene,

[0060] 9-12 parts of metallocene linear low-density polyethylene,

[0061] 4-6 parts of oxidized polyethylene;

[0062] The polyurethane elastomer is composed of polyadipate 1,6-hexanediol ester diol, polyethylene glycol, ethoxytrimethylolpropane, silane coupling agent KH-570 and hexamethylene diisocyanate The mass ratio of five of them is 100: (62-70): (6-9): (3.5-4.2): (3.2-4).

[0063] In this embodiment, the supersoft and super fluffy spunbonded nonwoven fabric is preferably, but not limited to, made of raw materials including the following parts by weight:

[0064] 60 part...

Embodiment 2

[0085] A kind of supersoft super fluffy spunbonded nonwoven fabric, described supersoft superfluffy spunbonded nonwoven fabric is made of the raw materials comprising following parts by weight:

[0086] 55 parts of polyethylene terephthalate,

[0087] 25 parts of polyurethane elastomer,

[0088] 7 parts of polyhexamethylene adipate,

[0089] 5 parts of linear low density polyethylene,

[0090] 9 parts of metallocene linear low density polyethylene,

[0091] 4 parts of oxidized polyethylene;

[0092] The polyurethane elastomer is composed of polyadipate 1,6-hexanediol ester diol, polyethylene glycol, ethoxytrimethylolpropane, silane coupling agent KH-570 and hexamethylene diisocyanate prepared, the mass ratio of five of them is 100:62:6:3.5:3.2.

[0093] In the present embodiment, the preparation method of the polyurethane elastomer comprises the following steps:

[0094] 1) Put 1,6-hexanediol polyadipate diol, polyethylene glycol, and 2 / 3 hexamethylene diisocyanate into ...

Embodiment 3

[0107] A kind of supersoft super fluffy spunbonded nonwoven fabric, described supersoft superfluffy spunbonded nonwoven fabric is made of the raw materials comprising following parts by weight:

[0108] 65 parts of polyethylene terephthalate,

[0109] 32 parts of polyurethane elastomer,

[0110] 10 parts of polyethylene adipate,

[0111] 7 parts of linear low density polyethylene,

[0112] 12 parts of metallocene linear low density polyethylene,

[0113] 6 parts of oxidized polyethylene;

[0114] The polyurethane elastomer is composed of polyadipate 1,6-hexanediol ester diol, polyethylene glycol, ethoxytrimethylolpropane, silane coupling agent KH-570 and hexamethylene diisocyanate prepared, the mass ratio of five of them is 100:70:9:4.2:4.

[0115] In the present embodiment, the preparation method of the polyurethane elastomer comprises the following steps:

[0116] 1) Put 1,6-hexanediol polyadipate diol, polyethylene glycol, and 2 / 3 hexamethylene diisocyanate into a react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a super-soft and super-fluffy spun-bonded non-woven fabric and a preparation method thereof. The super-soft and super-fluffy spun-bonded non-woven fabric is prepared from the following raw materials in parts by weight: 55-65 parts of polyethylene glycol terephthalate, 25-32 parts of polyurethane elastomers, 7-10 parts of polyethyleneglycol adipate, 5-7 parts of linear low-density polyethylene, 9-12 parts of metallocene linear low-density polyethylene and 4-6 parts of oxidized polyethylene. According to the super-soft and super-fluffy spun-bonded non-woven fabric, on thepremise that the mechanical property and durability are guaranteed, the softness of the super-soft and super-fluffy spun-bonded non-woven fabric is far superior to that of common PET non-woven fabric, the fluffy comfort degree of the super-soft and super-fluffy spun-bonded non-woven fabric is far superior to that of the common PET non-woven fabric, the air permeability is high and good, the disability is high, and the elasticity is good; the good waterproof performance is achieved; and the comprehensive performance index is excellent, the comprehensive use performance is good, and the marketapplication prospect is wide.

Description

technical field [0001] The invention relates to the technical field of nonwoven fabrics, in particular to a super soft and super fluffy spunbonded nonwoven fabric and a preparation method thereof. Background technique [0002] Non-woven fabrics, also known as non-woven fabrics, are composed of oriented or random fibers. It is called cloth because of its appearance and certain properties. Non-woven fabrics have no warp and weft threads, are very convenient for cutting and sewing, and are light in weight and easy to shape, so they are deeply loved by handicraft lovers. Because it is a fabric that does not need spinning and weaving, it is just oriented or random arrangement of short textile fibers or filaments to form a web structure, and then reinforced by mechanical, thermal bonding or chemical methods. [0003] Non-woven fabric is a kind of non-woven fabric. It directly uses polymer chips, short fibers or filaments to form fibers through airflow or machinery, and then unde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H3/147D01F8/14D01F8/16D01F8/06
CPCD04H3/147D01F8/14D01F8/16D01F8/06
Inventor 陈明情褚煜鑫邓燕军
Owner FUJIAN GUAN HONG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap