Treatment method of pre-lithiated SiOx negative electrode material

A technology of negative electrode material and processing method, which is applied in the processing field of pre-lithiated SiOx negative electrode material and can solve the problems of poor stability of pre-lithiated SiOx negative electrode material and the like

Pending Publication Date: 2020-12-18
SUNWODA ELECTRIC VEHICLE BATTERY CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the stability of the pre-lithiated SiOx anode materia

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Treatment method of pre-lithiated SiOx negative electrode material
  • Treatment method of pre-lithiated SiOx negative electrode material

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0057]Example 1

[0058]The processing method of the pre-lithiated SiOx negative electrode material of this embodiment is as follows:

[0059]1) Combine 100g 6μm SiO and 10g Li2O was mixed by mechanical ball milling for 3 hours, and then calcined at 500°C for 2 hours under the protection of an inert atmosphere of nitrogen to obtain a pre-lithiated SiOx negative electrode material, which was recorded as sample S1;

[0060]Take 100g of S1 with a particle size of 6μm and a carbon coating content of 3wt%, and take NH4F 5g, stir at room temperature for 1 hour, mix uniformly, then put the mixed sample in a tube furnace, and pass in nitrogen at a rate of 50mL / min. After nitrogen has been passed in for half an hour, start to heat up to 190°C. The temperature was controlled at 30°C / min, the temperature was raised to 190°C, and the temperature was kept for 0.5h. The obtained powder was ground and sieved to finally obtain a pre-lithiated SiOx negative electrode material coated with a layer of LiF, whic...

Example Embodiment

[0061]Example 2

[0062]The processing method of the pre-lithiated SiOx negative electrode material of this embodiment is as follows:

[0063]Mix 10g of biphenyl with 100g of tetrahydrofuran, then add 0.5g of lithium metal powder to obtain an organic solution containing lithium metal, then add 10g of 6μm SiO, stir for 12h, filter, and wash with tetrahydrofuran to obtain pre-lithiated SiOx anode material, denoted as Sample S2;

[0064]Take 100g of S2 with a particle size of 6μm and a carbon coating content of 3wt%, and take NH4F 5g, stir at room temperature for 1 hour, mix uniformly, then put the mixed sample in a tube furnace, and pass in nitrogen at a rate of 50mL / min. After nitrogen has been passed in for half an hour, start to heat up to 190°C. The temperature was controlled at 30°C / min, the temperature was raised to 190°C, and the temperature was kept for 0.5h. The obtained powder was ground and sieved to finally obtain a pre-lithiated SiOx negative electrode material coated with a layer...

Example Embodiment

[0065]Example 3

[0066]The processing method of the pre-lithiated SiOx negative electrode material of this embodiment is as follows:

[0067]Mix 100g of 6μm SiO anode with 5g of lithium metal powder, then add 100g of electrolyte to it, and let stand for 12h at room temperature to obtain pre-lithiated SiOx anode material, denoted as sample S3, where the solute of the electrolyte is 1.2mol / L Lithium hexafluorophosphate, the solvent is ethylene carbonate EC;

[0068]Take 100g of S3 with a particle size of 6μm and a carbon coating content of 3wt%, and take NH4F 5g, stir at room temperature for 1 hour, mix uniformly, then put the mixed sample in a tube furnace, and pass in nitrogen at a rate of 50mL / min. After nitrogen has been passed in for half an hour, start to heat up to 190°C. The temperature was controlled at 30°C / min, the temperature was raised to 190°C, and the temperature was kept for 0.5h. The obtained powder was ground and sieved to finally obtain a pre-lithiated SiOx negative electro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a treatment method of a pre-lithiated SiOx negative electrode material. The treatment method of the pre-lithiated SiOx negative electrode material comprises the following steps: mixing the pre-lithiated SiOx negative electrode material with a first solid compound to obtain a first mixture, X being greater than 0 and less than 2, and the first solid compound being selectedfrom at least one of ammonium fluoride and ammonium phosphate; under the atmosphere of protective gas, carrying out heat preservation sintering on the first mixture the temperature of 50 to 300 DEG Cto obtain the first pre-lithium-silicon negative electrode material. According to the treatment method of the pre-lithiated SiOx negative electrode material, the stability of the pre-lithiated SiOx negative electrode material can be improved.

Description

technical field [0001] The invention relates to the technical field of batteries, in particular to a treatment method for pre-lithiated SiOx negative electrode materials. Background technique [0002] As people's requirements for the cruising range of electric vehicles are getting higher and higher, the energy density of passenger car battery systems needs to be continuously improved. Traditional graphite anodes can no longer meet the current energy density requirements of power batteries. Due to the high gram capacity of silicon-based anodes, silicon-based anodes have become key research materials. [0003] Compared with pure Si anode, silicon oxide compound SiO x With higher gram capacity, lower expansion and better cycle life, it is regarded as the next generation of anode materials. However, the traditional silicon oxide compound SiO x There is a problem of low first effect, which seriously restricts its commercial application. At present, there are two main ways to i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/36H01M4/48H01M10/42
CPCH01M4/366H01M4/483H01M10/4235H01M2004/027Y02E60/10
Inventor 陈鹏褚春波张耀
Owner SUNWODA ELECTRIC VEHICLE BATTERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap